This article presents the results of examination of processing conditions such as mold Tf and injection Tw temperature influence on mechanical properties of the moldings made of copolymer ABS (acrylonitrilebutadiene-styrene) without and with a coloring agent in the form of a pigment and its masterbatches. The pigment was added in the amount of 1 wt ‰ and 2 wt ‰, while the masterbatches were added in the amount of 1 wt % and 2 wt %. The mechanical properties of the molded parts were determined in hardness, impact strength and tensile strength tests. The analysis of the obtained results allowed to state that the addition of the coloring agent in a form of pigment does not significantly affect the values of hardness and impact strength. However, the change of the processing conditions, e.g., increasing the mold temperature, contributed to the decrease of hardness and, at the same time, to the increase of impact strength. The tensile strength of the moldings made of ABS without and with the addition of the masterbatch is similar, regardless of the injection molding parameters, whereas their strain at break and Young’s modulus change, depending on the injection molding parameters. When using the low values of the mold temperature (30 °C) and injection temperature (230 °C), lower values of Young’s modulus were found, however, the aforementioned temperatures allow for obtaining a higher strain at break (noticed for colored samples).
PL
Oceniano wpływ warunków przetwórstwa: temperatury wtryskiwania Tw oraz temperatury formy Tf na właściwości mechaniczne wyprasek wytworzonych z kopolimeru akrylonitryl-butadien-styren (ABS) bez dodatku i z dodatkiem środka barwiącego w postaci koncentratu lub pigmentu. Koncentrat dozowano w ilości 1 % mas. i 2 % mas., a pigment w ilości 1 ‰ mas. i 2 ‰ mas. Badania właściwości mechanicznych wyprasek obejmowały twardość, udarność i statyczną próbę rozciągania. Na podstawie analizy otrzymanych wyników stwierdzono, że dodatek środka barwiącego nie wpływa w istotnym stopniu na twardość i udarność wyprasek. Natomiast zmiana parametrów przetwórstwa, np. podwyższona temperatura formy, przyczynia się do zmniejszenia twardości, a jednocześnie zwiększenia udarności. Bez względu na warunki przetwórstwa wytrzymałość na rozciąganie próbek z tworzywa ABS bez dodatku oraz z dodatkiem koncentratu barwiącego była zbliżona, natomiast w zależności od warunków wtryskiwania następowała zmiana ich odkształcenia przy zerwaniu oraz modułu sprężystości przy rozciąganiu. W wypadku wyprasek barwionych zastosowanie niskiej temperatury formy wtryskowej (30°C) oraz niskiej temperatury wtryskiwania (230°C) powodowało zmniejszenie wartości modułu sprężystości oraz, na ogół, zwiększenie wartości odkształcenia przy zerwaniu.
W artykule omówiono wpływ parametrów wtryskiwania, takich jak temperatura formy Tf i temperatura wtryskiwania Tw na właściwości mechaniczne wyprasek wytworzonych z tworzywa ABS (akrylonitryl - butadien - styren) bez oraz z dodatkiem środka barwiącego w postaci koncentratu oraz pigmentu. Koncentrat dozowano w ilości 1% i 2%, a pigment w ilości 1‰ i 2‰. Właściwości mechaniczne wyprasek wyznaczano w badaniach twardości, udarności i statycznej próbie rozciągania. Analiza uzyskanych wyników badań pozwoliła stwierdzić, że dodatek środka barwiącego nie wpływa znacząco na uzyskane wartości twardości i udarności. Natomiast zmiana warunków przetwórstwa np. podwyższenie temperatury formy, przyczyniła się do zmniejszenia twardości i jednocześnie do zwiększenia udarności. Z kolei wytrzymałość na rozciąganie próbek z tworzywa ABS niebarwionego oraz zawierającego koncentrat barwiący jest zbliżona, bez względu na warunki przetwórstwa. Natomiast, w zależności od warunków wtryskiwania, zmienia się ich odkształcenie przy zerwaniu oraz moduł sprężystości przy rozciąganiu. Zastosowanie niskiej temperatury formy wtryskowej 30°C oraz niskiej temperatury wtryskiwania 230°C przyczynia się do zmniejszenia wartości modułu sprężystości, jednak umożliwia uzyskanie większej wartości odkształcenia wyprasek przy zerwaniu.
EN
The results of examination of the influence of mould and injection temperature on mechanical properties of samples made of terpolymer ABS (acrylonitrile - butadiene - styrene) without and with colouring agent in the form of pigment and its masterbatches are presented in the article. Pigment was added in amount of 1‰ and 2‰, while masterbatches were added in an amount of 1% and 2%. Mechanical properties of moulded parts were determined in static tensile tests and measurements of hardness and impact resistance. The analysis of the obtained results allowed to state that addition of colouring agent does not significantly affect values of hardness and impact strength. However the change in processing conditions, eg. increasing mould temperature contributed to decrease in hardness and, at the same time, increase in impact strength. The tensile strength of mouldings made of ABS without and with addition of masterbatch is similar, regardless of the injection moulding parameters. Whereas, their strain at break and Young’s modulus change, depending on the injection moulding parameters. When using the low values of mould temperature 30°C and injection temperature 230°C the lower values of Young’s modulus were found, but it allows to obtain higher strain at break.
W artykule omówiono wpływ starzenia promieniami UV na morfologię wyprasek wtryskowych wytworzonych z tworzywa ABS z dodatkiem środka barwiącego w postaci proszku oraz koncentratu barwiącego (granulatu) na nośniku ABS i PS. Starzenie promieniami UV w warunkach przyspieszonych prowadzono przez 745 godzin, przy pomocy komory Solarbox 1500e. Zmiany w morfologii obserwowano za pomocą elektronowego mikroskopu skaningowego (SEM). Wykazano, że promieniowanie UV przyczynia się do zmian strukturalnych tworzywa, zależnych od rodzaju środka barwiącego.
EN
The results of examination of the influence of ageing by UV rays on the morphology of injection moulded parts made of terpolimer ABS with addition of colouring agent in the form of powder and its masterbatch (granulate) based on ABS and PS have been presented. Ageing by UV rays, under accelerated conditions, was carried out for 745 hours using the Solarbox 1500ecell. Changes in the morphology were observed by scanning electron microscope (SEM). It has been shown that the UV radiation contributes to structural changes in polymer, which are dependent on the type of colouring agent.
The results of examination of the influence of polymer processing parameters and addition of coloring agents in the form of yellow organic pigment PY 191 and its masterbatches based on acrylonitrile-butadiene-styrene copolymer (ABS) or polystyrene (PS) on the color and gloss of injection molded parts have been presented. Gloss investigations, at the light incidence on the molding surface in the direction of polymer flow in the cavity and in the opposite direction at an angle of 60° and 20° were made (Figs. 3–6). Color tests were also carried out (Table 4). The obtained results showed that high mold temperature (Tf = 80 °C) and lower injection temperature (Tω = 230 °C) allow to obtain parts of higher gloss and smaller variation in their color.
PL
Omówiono wpływ warunków przetwórstwa oraz dodatku środków barwiących w postaci żółtego pigmentu organicznego PY 191 oraz jego koncentratów na bazie kopolimeru akrylonitryl--butadien-styren (ABS) lub polistyrenu (PS) na barwę oraz połysk wyprasek. Wykonano badania połysku powierzchni wyprasek przy świetle padającym zgodnie z kierunkiem przepływu tworzywa w gnieździe formującym oraz w kierunku przeciwnym pod kątem 60° i 20° (rys. 3–6). Przeprowadzono również badania barwy porównując barwę wytworzonych wyprasek do wzorców wybranych ze wzornika NCS (z ang. Natural Color System) (tabela 4). Na podstawie otrzymanych wyników określono, że najwyższa z badanych temperatura formy (Tf = 80 °C) oraz niższa temperatura wtryskiwania (Tω = 230°C) umożliwiają uzyskanie wyprasek charakteryzujących się większym połyskiem oraz mniejszym zróżnicowaniem barwy.
W artykule omówiono wpływ wybranych parametrów przetwórstwa, takich jak temperatura formy Tf, temperatura wtryskiwania Tw i prędkość wtryskiwania Vw na barwę i połysk wyprasek wtryskowych wytworzonych z kopolimeru ABS (akrylonitryl - butadien - styren) z dodatkiem środka barwiącego w postaci koncentratu na bazie tego samego tworzywa. Pomiary barwy przeprowadzono z wykorzystaniem spektrofotometru sferycznego SP 60 firmy X-Rite. Następnie porównano je ze wzorcem z katalogu NCS (ang. Natural Color System). Określono wpływ warunków przetwórstwa na wartość ΔE (różnicę w barwie między wzorcem, a wytworzoną próbką). Badania połysku wykonano przy użyciu połyskomierza Elcometer 406 z zastosowaniem geometrii 60°. Analiza uzyskanych wyników badań pozwoliła stwierdzić, że zastosowanie niższej temperatury wtryskiwania oraz formy (230÷240°C), a także większej prędkości wtryskiwania (113 mm/s) pozwala uzyskać wypraski cechujące się największą wartością połysku, a także najmniejszą wartością ΔE.
EN
In the article the results of experiment in which the influence of chosen injection moulding parameters, such as: mould temperature, injection temperature and injection velocity on colour and gloss of mouldings made of copolymer ABS (acrylonitrile - butadiene - styrene) with the addition of masterbatch based on the same polymer are presented. Colour measurements were carried out using a spherical spectrophotometer SP 60 from X-Rite. Then results were compared with colour model from NCS (Natural Color System) catalog. On the basis of the obtained results, the effect of processing conditions on the value of ΔE (the difference in color between the model and the sample) was determined. Gloss tests were performed using a glossmeter Elcometer 406 with geometry 60°. The analysis of the obtained results has shown that the use of lower injection and mould temperature, as well as higher injection velocity allow to produce mouldings with the highest value of gloss, and the lowest value of ΔE.
The aim of this work was to evaluate the effect of shear plastic into the mold cavity with a variable height on the structure and selected properties of molded parts. It was used as a special designed mold for producing test samples with varying thickness. It was shown, that the wall thickness of the molded part can significantly affect its properties, not only because of the greater volume of the amount of material, but also because of the process taking place within the molded part during the solidification of the material. The degree of crystallinity can be different depending on the cooling time, which may contributes to the change in strength.
7
Dostęp do pełnego tekstu na zewnętrznej witrynie WWW
Przedstawiono wyniki badań doświadczalnych otrzymywania mikrokanałów mających zastosowanie do osłony mikrokabli optotelekomunikacyjnych. Mikrokanały wytworzono w linii technologicznej wytłaczania porującego polietylenu małej gęstości (PE-LD) z zastosowaniem środka porującego chemicznie o endotermicznym charakterze rozkładu. W badaniach eksperymentalnych określono gęstość oraz stopień sporowacenia otrzymanych mikrokanałów. Przeprowadzono analizę mikroskopową wytworzonych mikrokanałów. Wykonano ocenę właściwości tribologicznych mikrokanałów przy kontakcie z mikrokablem zawierającym pojedyncze włókno światłowodowe. Stwierdzono, że otrzymana wytłoczyna ma wewnątrz ścianki strukturę porowatą, a warstwę wierzchnią litą, co przy odpowiedniej zawartości środka porującego (0,2-0,4%) zapewnia jej dobre właściwości fizykalne i tribologiczne.
EN
A blowing agent (mixt. of NaHCO3 and C(CH2COOH)2(OH) COOH) was added (0.2-0.8% by mass.) to low-d. Polyethylene extruded then to microducts (diam. 9 mm, wall thickness 1.4-1.8 mm). The extrudates had porous cores and solid surface layers at the proper amt. of the blowing agent (0.2-0.4%). The microducts were studied for d., porosity and tribol. properties in contact with an optical micro-cable. They met the quality requirements.
8
Dostęp do pełnego tekstu na zewnętrznej witrynie WWW
W niniejszej pracy szerzej przedstawiono jedną z metod wtryskiwania niekonwencjonalnego, pozwalającą na uzyskanie wyprasek porowatych, a mianowicie wtryskiwanie mikroporujące z zastosowaniem poroforów fizycznych. Może ono być przeprowadzane przy użyciu konwencjonalnych wtryskarek wyposażonych w układ uplastyczniający z system wtryskiwania gazu w stanie nadkrytycznym.
EN
This work broadly shows one method of an unconventional injection moulding process, which allows to obtain porous moulded parts, namely microcellular injection moulding, using physical blowing agents. It may be carried out using a conventional injection moulding plasticizing system equipped with a supercritical gas injection system.
9
Dostęp do pełnego tekstu na zewnętrznej witrynie WWW
Obszary łączenia strumieni tworzywa, powstające w wyniku zderzania się frontów przepływającego tworzywa, negatywnie wpływają na właściwości mechaniczne oraz wygląd wyprasek wtryskowych. Problem ten szczególnie dotyczy wyprasek wykonanych z kompozytów z napełniaczami włóknistymi, ze względu na prostopadłe do kierunku przepływu zorientowanie włókien napełniacza w czole frontu strumienia tworzywa wypełniającego gniazdo formujące. W pracy przedstawiono wyniki badań wpływu wybranych warunków procesu wtryskiwania na wytrzymałość na rozciąganie, udarność oraz wygląd wyprasek z obszarami łączenia strumieni tworzywa. Walor estetyczny wyprasek oceniano na podstawie kształtu i wymiarów szczeliny, powstałej na powierzchni wypraski w obszarze łączenia. Badane próbki wykonane zostały z kompozytu polipropylenu z 20% zawartością talku. Wykazano wpływ warunków procesu wtryskiwania na głębokość i szerokość szczeliny, decydującej o widoczności linii łączenia strumieni tworzywa na powierzchni wypraski. Nie stwierdzono natomiast wpływu badanych parametrów wtryskiwania na wartość wytrzymałości na rozciąganie wyprasek. Wyniki badań wyprasek z obszarami łączenia strumieni tworzywa porównano z wynikami uzyskanymi dla wyprasek bez tych obszarów.
EN
Weld lines are formed as a result of collision of several fronts of the polymer flow that negatively affect the mechanical properties and the visual aspect of the moulded parts. This problem concerns in particular the moulded parts made of composites with fibrous fillers due to the perpendicular (with direction of the flow) orientation of the filler’s fibres in the frontal face of the stream of plastic that fills the cavity. This work presents the results of the investigations of the effect of selected injection moulding conditions on the tensile strength, impact strength and the visual aspects of the moulded parts with the weld lines. Aesthetical value of the moulded parts was evaluated based on shape, dimensions of the gaps that were formed on the moulded parts surface in the area of flow fusion. The specimens were trade of a composite of polypropylene with 20% of talc. The effect of the injection moulding conditions on the depth and width of a gap that determines the visibility of the line of connection of the plastic streams on the surface of the moulded parts was demonstrated. However, no effect of the injection moulding parameters on the moulded parts tensile strength was found. The results of the examinations obtained for the moulded parts with the weld lines were compared with the results obtained for the moulded parts without these lines.
10
Dostęp do pełnego tekstu na zewnętrznej witrynie WWW
The examinations of changes in mechanical properties, colour and gloss of injection molded parts from polyamide PA 6.10 after cyclic loading with varying frequency, at a constant level of deformation, are presented in the article. The relationships between the stress and the elongation of samples after 1 and 3000 cycles of tensile - compression tests were registered and the hysteresis loops were obtained. It was found that cyclic loading causes changes in mechanical properties of samples. In investigations of the effect of loading frequency on hysteresis loop shape it was stated that the value of the maximum stress increased with the increasing load frequency. In the DSC examinations, the effect of loading frequency on the degree of crystallinity of samples, and changes in the range of the melting point of the crystalline phase of polyamide were shown. Small changes in the degree of crystallinity in the surface layer and the core of samples during cyclic loading with different frequencies were observed, but generally the degree of crystallinity in the surface layer is higher than in the core. Cyclic loading affects also the colour and gloss of samples. Smaller changes in colour of loaded samples occurred at the lower value of cyclic loading frequency. The gloss of samples after cyclic loading is lower than not loaded ones and with the increase in loading frequency the gloss decreases.
11
Dostęp do pełnego tekstu na zewnętrznej witrynie WWW
Przedstawiono wyniki badań charakterystyki odkształceniowo-naprężeniowej uzyskane w próbie cyklicznego rozciągania - ściskania, przy założeniu stałego poziomu amplitudy odkształcenia. Badaniom poddano poliacetal oraz jego kompozyty o zawartości 10 i 26% włókna szklanego. Rejestrowano zależność pomiędzy naprężeniem i wydłużeniem próbki, uzyskując pętle histerezy. Wykazano zmiany właściwości mechanicznych badanych próbek spowodowane cyklicznym obciążeniem. Badano strukturę oraz wyznaczono metodą DSC stopień krystaliczności próbek nieobciążonych i po obciążeniu.
EN
The results of investigations of strain-stress characteristics obtained during the cyclic tensile - compression test, at constant level of strain amplitude were presented in this work. Polyacetal and its composites filled with 10 and 26% of glass fibre have been tested. The relationship between tensile stress and elongation of the sample was recorded. As a result hysteresis loops were obtained. The change in mechanical properties and structure of test specimens caused by cyclic loading has been shown. The degree of crystallinity was determined using DSC method.
12
Dostęp do pełnego tekstu na zewnętrznej witrynie WWW
W pracy przedstawiono wyniki badań wpływu wybranych warunków wtryskiwania na grubość, długość, masę oraz gęstość wyprasek wytwarzanych metodą wtryskiwania kaskadowego. Uzyskano wypraski charakteryzujące się równomierną gęstością na całej długości. Wykazano wpływ warunków wtryskiwania na masę i wymiary wyprasek oraz brak ich wpływu na gęstość tworzywa w poszczególnych obszarach wypraski.
EN
The paper presents the results of investigations on the influence of selected injection molding conditions on the thickness, length, weight and density of parts made by cascade injection molding. The obtained parts are characterized by uniform density throughout. The influence of injection molding conditions on the weight and dimensions of the molded parts and the lack of their impact on the density of the material in the various areas of the parts are shown.
13
Dostęp do pełnego tekstu na zewnętrznej witrynie WWW
Celem badań była ocena wpływu wielokrotnego przetwórstwa tworzywa PE-HD z dodatkiem poroforu na grubość powierzchni, wybrane właściwości mechaniczne i strukturę wyprasek wtryskowych. W badaniach użyto tworzywo PE-HD Hostalen GC 7260 oraz porofor o endotermicznym przebiegu rozkładu (Hostatron P 1941), który dodawano w ilościach 3% oraz 6%. Ciśnienie i czas docisku redukowano ze zwiększeniem procentowej zawartości poroforu w tworzywie. Próbki uzyskane z tworzywa pierwotnego poddano wielokrotnemu przetwarzaniu. Wykazano, że zastosowanie poroforu polepsza dokładność wymiarową wyprasek, ale pogarsza ich wytrzymałość i wpływa na zmianę koloru. Wielokrotne przetwórstwo tworzywa z poroforem nie spowodowało znacznego pogorszenia właściwości mechanicznych. W badaniach DMTA wykazano jedynie pewien spadek wartości modułu zachowawczego. W badaniach strukturalnych wyprasek z tworzywa wtórnego stwierdzono występowanie coraz mniejszej liczby porów po kolejnych cyklach przetwarzania. Wypraski z tworzywa poddanego 5-krotnemu recyklingowi miały strukturę litą, co oznacza, że nie występował już dalszy rozkład poroforu.
EN
Examinations were carried out to determine the influence of multiple reprocessing of HDPE with chemical blowing agent on thickness surface state, selected mechanical properties and structure of moulded parts. Samples were made of HDPE Hostalen GC 7260 without and with 3% and 6% addition of Hostatron P 1941 endothermic chemical blowing agent. Properties of samples made of 1 to 6-time processed polymer were examined. During the injection moulding process the holding pressure and holding time was changed according to the blowing agent content. It was found that the application of the blowing agent improved parts dimensional accuracy, but lowered tension strength and caused the change in their colour. Multiple foamed polymer recycling did not caused significant lowering of parts mechanical properties. The DMTA investigations showed some decrease in values of storage modulus caused by multiple reprocessing of foamed polyethylene. Microscopic observations showed that there is no porous structure in samples made of 5-time recycled HDPE with 6% blowing agent, so it means that the foaming process stopped.
14
Dostęp do pełnego tekstu na zewnętrznej witrynie WWW
W pracy przedstawiono wyniki badań wpływu wybranych warunków wtryskiwania na połysk wyprasek z polipropylenu z 20% zawartością talku. Zbadano również entalpię topnienia próbek polimeru pobranego z rdzenia oraz z naskórka wypraski. Wykazano wpływ warunków wtryskiwania na rozmieszczenie cząsteczek talku w przekroju wypraski oraz ich wpływ na krystalizację i połysk wyprasek.
EN
The results of the influence of selected injection molding parameters on gloss of polypropylene filled with 20% talc injection molded parts are presented in this article. The melting enthalpy of the polymer in the core and in the skin of the molded part was also examined. The impact of injection molding conditions on the distribution of talc particles in the molding parts cross-section and their influence on crystallization and gloss of molded parts has been shown.
15
Dostęp do pełnego tekstu na zewnętrznej witrynie WWW
Przedstawiono charakterystyki odkształceniowo-naprężeniowe uzyskane w próbie cyklicznego rozciągania, przy założeniu stałego poziomu amplitudy odkształcenia, wyprasek wtryskowych z poliwęglanu, badanych w temperaturze pokojowej oraz podwyższonej temperaturze (50 °C, 70 °C, 90 °C). Rejestrowano zależność pomiędzy naprężeniem rozciągającym i wydłużeniem próbki, uzyskując pętle histerezy. Wykazano zmiany właściwości mechanicznych oraz stanu naprężeń próbek spowodowane cyklicznym obciążeniem.
EN
Strain-stress characteristics obtained in the cyclic tensile test, at a constant level of deformation amplitude of injection molded parts made of polycarbonate, studied at room and elevated temperature (50 °C, 70 °C, 90 °C) are presented. The relationship between the tensile stress and elongation of the samples, were recorded and hysteresis loops were obtained. Changes in mechanical properties and internal stress of samples caused by cyclic loading were stated.
16
Dostęp do pełnego tekstu na zewnętrznej witrynie WWW
W pracy przedstawiono wyniki badania twardości metodą Shore'a typ D, udarności oraz właściwości lepkosprężystych niebarwionego tworzywa ABS Terluran GP - 35 firmy BASF oraz z dodatkiem środków barwiących w postaci pigmentu oraz koncentratu (masterbatch'a). Dokonano oceny wpływu wskazanych środków barwiących na właściwości mechaniczne wyprasek. Poza różnymi zawartościami środków barwiących w badaniach brano pod uwagę zmienne warunki przetwórstwa takie jak temperatura wtryskiwania Tw i temperatura formy Tf przy stałym ciśnieniu docisku pd oraz prędkości wtryskiwania vw.
EN
The paper shows the results of hardness research determined by Shore type D method, impact resistance and viscoelastic properties of polymer ABS Terluran GP - 35 from BASF, without and with colouring agent in the form of pigment and masterbatch. An impact assessment of advisable colouring agent on mechanical properties was executed. In addition to various contents of the colouring agents in researches were taken into account the processing conditions such as: injection temperature Tw, mould temperature Tf at constant pressure pd and injection velocity vw.
17
Dostęp do pełnego tekstu na zewnętrznej witrynie WWW
Dokonano oceny wpływu zawartości poroforu i warunków wtryskiwania na wybrane właściwości wyprasek wtryskowych z polipropylenu z udziałem 0,125—0,5 % poroforu endotermicznego. W badaniach stosowano cztery zmienne parametry wtryskiwania: procentową zawartość poroforu (c), temperaturę formy (Tf), temperaturę wtryskiwania (Tw) i prędkość wtryskiwania (vw). Wykazano, że na masę i gęstość wyprasek wpływa głównie temperatura formy, przy czym z jej wzrostem masa i gęstość wyprasek maleje. Właściwości wytrzymałościowe wyprasek zależą zaś w znacznym stopniu od temperatury formy i temperatury wtryskiwania. Zastosowanie wyższych wartości pogarsza wydłużenie względne wyprasek przy maksymalnym naprężeniu rozciągającym (eM). Wyższa temperatura formy, sprzyjająca niekorzystnemu rozrostowi porów, jest jednak wskazana ze względu na wydłużenie czasu krystalizacji tworzywa, co w efekcie powoduje wzrost wytrzymałości na rozciąganie wytworzonych wyprasek. Wypraski uzyskane z tworzywa z udziałem poroforu charakteryzują się mniejszą udarnością niż wypraski z tworzywa litego. Na stan powierzchni wyprasek, określany na podstawie wielkości zapadnięć, połysku i koloru, w sposób istotny wpływa zawartość poroforu i temperatura formy. Dodatek poroforu do tworzywa skutkuje zmniejszeniem zapadnięć, zwłaszcza w warunkach niższej temperatury formy, jednocześnie następuje pogorszenie połysku i zmiana koloru.
EN
The effects of blowing agent content and injection moulding conditions on the selected properties of polypropylene moulded parts containing 0,125—0.5 % endothermic blowing agent, were investigated. Four variable injection process parameters: the percentage of blowing agent (c), mould temperature (Tf), injection temperature (Tw) and injection velocity (vw) were used in the experiments. It was found that the mass and density of moulded parts depend mainly on the mould temperature — with an increase in temperature, the decrease in mass and density of the parts was observed (Figs. 4—7). The mechanical properties of the parts were mostly influenced by the mould temperature and injection temperature (Figs. 8 and 9). The parts moulded at higher temperatures showed lower elongation at maximum force (eM). High mould temperature, which is conducive to the growth of pores, is advantageous because of the longer time of polymer crystallization and, as a result, the increase in tensile strength of the obtained parts. The moulded specimens made of polypropylene with the addition of blowing agent have lower impact strength than the parts obtained from solid polymer (Figs. 10 and 11). The surface state of the moulded parts (sink marks, colour and gloss) was mainly influenced by the blowing agent content and mould temperature (Figs. 12—19). The addition of blowing agent results in the reduction of sink marks, particularly at low mould temperature, but can lead to a loss of gloss and change of colour of the moulded products.
18
Dostęp do pełnego tekstu na zewnętrznej witrynie WWW
W artykule omówiono różne modele przestrzeni barw oraz ich postrzeganie przez ludzkie oko. W części badawczej dokonano pomiarów barwy wyprasek wtryskowych z tworzywa ABS kolorymetrem SP60 firmy X-rite. Badania miały na celu porównanie barwy wyprasek wtryskowych z tworzywa o różnych zawartościach procentowych środków barwiących. Wyniki badań zostały przekonwertowane ze skali CIELab do skali RGB. Przestawiono schemat przeliczania modeli barw pomiędzy skalą niezależną CIELab do modelu przestrzeni RGB. Pozwoliło to na przedstawienie różnic barwy określonej przy wykorzystaniu tych modeli. Stwierdzono, że model przestrzeni barwy RGB nie może być stosowany, jako model referencyjny, ponieważ jest on ściśle związany z urządzeniem wyświetlającym lub odczytującym. W badaniach przemysłowych lub naukowych, porównywanie barw powinno odbywać się przy użyciu modeli niezależnych.
EN
Models of colour space and also colour preception by the human eye in the colour studies of ABS without and with addicton of colorant agents were decribed. In experiments colour measurement of injection moulded parts using colorimeter SP60 from X-rite was made. The aim of the study was to compare the colour of moulded parts made of ABS with different percentage of colorant agents. The results in CIELab scale were converted into RGB scale. The scheme of colour models conversion from independent CIELab to RGB colour space model was presented. This allowed for presentation of colour differences determined by these models. RGB colour space model cannot be used as a reference model because of its close dependence with the display and reading devices. It means that, in industrial or scientific investigations, colour comparison should be done using independent models.
19
Dostęp do pełnego tekstu na zewnętrznej witrynie WWW
W pracy przedstawiono wyniki symulacji komputerowej procesu wtryskiwania kaskadowego na przykładzie wypraski cienkościennej wytwarzanej dla przemysłu motoryzacyjnego. Symulację przeprowadzono przy pomocy programu Moldflow Plastic Insight w wersji 5.0. W badaniach symulacyjnych określono wpływ warunków wtryskiwania (temperatura formy Tf, temperatura wtryskiwania Tw, objętościowe natężenie przepływu tworzywa V) na równomierność rozkładu temperatury w wyprasce, czas zestalenia tworzywa w gnieździe formy wtryskowej, wartość siły zamykania formy oraz wskaźnik zapadnięć.
EN
The results of computer simulation of cascade injection molding process on the example of thin-wall parts manufactured for the automotive industry were presented in this article. The simulation was made using Moldflow Plastic Insight 5.0 software. The simulations allow to determine the influence of injection moulding conditions (mold temperature Tf, melt temperature Tw, flow rate V) on the uniformity of molding parts temperature, time to freeze, clamp force and sink index.
20
Dostęp do pełnego tekstu na zewnętrznej witrynie WWW
Przedstawiono wyniki badań charakterystyki odkształceniowo-naprężeniowej uzyskane w próbie cyklicznego rozciągania, przy założeniu stałego poziomu amplitudy naprężenia, wyprasek wtryskowych z PP, ABS oraz PA. Rejestrowano zależność pomiędzy naprężeniem rozciągającym i wydłużeniem próbki, uzyskując pętle histerezy. Wykazano zmiany właściwości mechanicznych badanych próbek spowodowane cyklicznym obciążeniem. W badaniach DSC zaobserwowano nieznaczne zmiany stopnia krystaliczności cyklicznie obciążanych próbek.
EN
The results of investigations of strain-stress characteristics obtained during the cyclic tensile test, constant level of stress amplitude were presented in this work. The injection molded parts form PP, ABS and PA were tested. The relationship between tensile stress and elongation of the sample was recorded. As a result hysteresis loops were obtained. The change in mechanical properties of test specimens caused by cyclic loading has been shown. In DSC studies small changes in polymer crystallinity degree during cyclic loading were observed.