The influence of NCO/OH ratio and acrylic polymer structure on curing and properties of 2K polyurethane coatings

Grianko I., Soloveva V., Kalinina I., Vasilev D., Ilin A.

Farby i Lakiery

2017

nr 5

37--46

At the moment the variety of acrylic styrene copolymers for coatings is very high. Although there are a lot of studies devoted to the influence of NCO/OH ratio on the curing behavior and properties of 2K solventborne polyurethane coatings, the trend to decrease the coating costs while maintaining their performance makes the investigations in this area relevant again. One of the ways to tackle this challenge is to vary the NCO/OH ratio in the coating composition using different types of hydroxyl-functional acrylic styrene copolymer (containing primary, secondary hydroxyl groups or mixtures thereof). A correlation between curing kinetics and the properties of 2K-PU coating at different NCO/OH ratios in uncatalysed reaction conditions at different curing temperatures was established.

Obecnie różnorodność kopolimerów styrenowo-akrylowych stosowanych w wyrobach lakierowych jest bardzo duża. Pomimo, że wiele badań poświęconych było wpływowi stosunku grup NCO/OH na proces utwardzania i właściwości powłok otrzymanych z dwuskładnikowych, rozpuszczalnikowych, poliuretanowych wyrobów lakierowych, jednak tendencja do obniżania kosztów przy jednoczesnym zachowaniu ich właściwości sprawia, że badania w tym obszarze są znowu znaczące. Jednym ze sposobów radzenia sobie z tym wyzwaniem jest zmiana stosunku NCO/OH w kompozycji powłokowej przy użyciu różnych typów kopolimeru styrenowo-akrylowego zawierającego grupy hydroksylowe (pierwszorzędowe, drugorzędowe grupy hydroksylowe lub ich mieszaniny). Ustalono korelację pomiędzy kinetyką utwardzania a właściwościami dwuskładnikowych, poliuretanowych powłok przy różnych stosunkach NCO/OH w warunkach bez katalizatora i w różnych temperaturach utwardzania.

The influence of hydroxy-functional acrylic styrene copolymers structure on curing and properties of solventborne polyurethane coatings

Soloveva V., Grianko I., Prosorova I., Vasilev D., Ilin A.

Farby i Lakiery

2017

nr 4

38--46

In this study the influence of the steric factor of styrene acrylic copolymer composition on coating formation and properties was estimated. The influence of primary and secondary hydroxyl groups in (meth)acrylic-styrene copolymers on curing behavior and properties of 2К polyurethane solventborne coatings with stoichiometric ratio of hydroxyl and isocyanate groups in uncatalysed reaction conditions at different temperatures was investigated. The samples having the same glass transition temperature, OH-content, acid value, solids content and dynamic viscosity, and different types of hydroxyl functional monomers (primary/secondary groups) and mixture thereof were used. During the curing process of 2K polyurethane compositions the following parameters were studied: – curing kinetics; – rheological behavior; – change in the glass transition temperature; – physical and mechanical properties.

W artykule przedstawiono wyniki badań wpływu czynnika sterycznego kopolimeru akrylowo-styrenowo na tworzenie powłok i ich właściwości. Badano wpływ pierwszorzędowych i drugorzędowych grup hydroksylowych w kopolimerach metakrylowo-styrenowych na proces utwardzania oraz właściwości dwuskładnikowych, poliuretanowych, rozpuszczalnikowych wyrobów lakierowych przy stechiometrycznym stosunku grup hydroksylowych do izocyjanianowych bez katalizatora, w różnych temperaturach. Stosowano próbki o jednakowej temperaturze zeszklenia, zawartości grup hydroksylowych, liczbie kwasowej, zawartości części nielotnych i lepkości, a o monomerach zawierających różne typy grup hydroksylowych (grupy pierwszorzędowe /drugorzędowe). W czasie utwardzania dwuskładnikowych kompozycji poliuretanowych oznaczano następujące parametry: - kinetykę utwardzania; - właściwości reologiczne; - zmianę temperatury zeszklenia; - fizyczne i mechaniczne właściwości.