The effect of heavy deformation on the structure of Mg-AZ31 alloy at ambient and elevated temperatures

Bonarski J., Pospiech J.

Inżynieria Materiałowa

|

2010

|

Vol. 31, nr 3

565-568

EN

The behavior of the Mg-AZ31 (Mg based) alloy containing 3.1 wt. % Al and 1.3 wt. % Zn based on structure observations during heavy deformation by the Equal Channel Angular Pressing (ECAP) at room and elevated temperatures has been investigated. Heavy deformation of metals opens new possibilities to control the structure and texture in order to obtain new mechanical properties. The refinement of microstructure together with the increase of strength and ductility of material are the most desired effects of such a technique. Such requirements can be realized by the use of the ECAP technique often applied to deform metals of cubic and hexagonal lattices. In contrast to materials of low deformability at room temperature such as the Mg-AZ31 alloy, extrusion with the ECAP technique is not effective because usually leads to its failure. In the presented work, the results of the attempt to moderate the Mg-AZ31 alloy destruction in the ECAP processing through the use of Al-shield protection have been presented. The behavior of the Mg-based alloy in the ECAP process at room and elevated temperatures was examined with texture measurements and structure observations.

PL

Na podstawie obserwacji struktury badano zachowanie się stopu magnezu Mg AZ31 (3,1% mas. Al i 1,3% mas. Zn) podczas intensywnego odkształcenia w procesie Equal Channel Angular Pressing (ECAP) w temperaturze pokojowej i podwyższonej. Intensywne odkształcenie metali stwarza nowe możliwości sterowania strukturą i teksturą krystalograficzną w aspekcie poprawy właściwości materiału, przede wszystkim mechanicznych. Najważniejsze pożądane efekty intensywnego odkształcenia to silne rozdrobnienie mikrostruktury z równoczesnym wzrostem wytrzymałości i ciągliwości materiału. Wymagania takie spełnia metoda przeciskania przez kanał kątowy ECAP, co wykazano w wielu jej zastosowaniach dla metali o sieci regularnej i heksagonalnej. Technologia ECAP nie jest jednakże efektywna w przypadku materiałów o słabej odkształcalności w temperaturze otoczenia, takich jak stop Mg AZ31, który jest przedmiotem badań opisanych w niniejszej pracy. Przeciskanie metodą ECAP w temperaturze pokojowej prowadzi do destrukcji tego stopu. W niniejszej pracy przedstawiono wyniki podjętej próby złagodzenia destrukcji stopu Mg AZ31 w procesie ECAP przez zastosowanie osłony aluminiowej. Badano zachowanie się stopu magnezu AZ31 w procesie ECAP w temperaturze pokojowej oraz podwyższonej na podstawie pomiarów tekstury i obserwacji mikrostruktury.

2

Effects in the texture and mictostructure in some metals of cubic and heksagonal symmetry caused by the change of the rolling direction

Pospiech J.

Archives of Metallurgy and Materials

|

2008

|

Vol. 53, iss. 1

83-87

EN

In the present paper texture and microstructure effects which are released after the change of the deformation path in metals are displayed. The effects are characterized by experimental results selected from earlier studies for some metals of cubic and hexagonal symmetry. The observed effects result directly from the instability of the texture and microstructure with respect to the modified geometry of deformation. A consequence of the change of the geometry of deformation is at the same time a reduction of the global strain hardening which causes that the observed changes are rapid and dynamic. The presented results which were obtained in the rolling process of copper, copper alloy and magnesium alloy show strong effects of destabilization after the change of the rolling direction and after a relatively small amount additional deformation. The performed investigations, were inspired by works published in the 1990s mainly by A.Korbel.

PL

Prezentowane są efekty w teksturze i mikrostrukturze metali wywołane zmiany drogi plastycznego odksztalcenia. Są one charakteryzowane wynikami eksperymentalnymi, które wybrano z wcześniejszych prac dla niektórych metali sieci regularnej i heksagonalnej. Obserwowane efekty wynikają bezpośrednio z niestabilności tekstury i mikrostruktury względem zmienionej geometrii odksztalłenia. Skutkiem zmiany geometrii odkształcenia jest równocześnie redukcja globalnego umocnienia, co powoduje, że zachodzace zmiany są szybkie i dynamiczne. Przedstawione wyniki, które uzyskano w procesie walcowania miedzi, stopu miedzi i stopu magnezu, pokazują efekty destabilizacji po zmianie kierunku walcowania, po względnie małych dodatkowych odkształceniach. Wykonanie eksperymentów inspirowane było pracami A.Korbla w latach 90-tych.

3

The effect of the rolling geometry on the texture and microstructure in AZ31 and copper

Pospiech J., Ostafin M., Schwarzer R.

Archives of Metallurgy and Materials

|

2006

|

Vol. 51, iss. 1

37-42

EN

The destabilization phenomena in texture and microstructure caused by the change of the deformation path are considered in an AZ31 magnesium alloy. The study, based on individual grain orientation measurements in the SEM by COM/EBSD, is a continuation of earlier investigation on copper. The phenomena in materials caused by the destabilization provide new information about the mechanism of plastic deformation and its structure-texture effects which are valuable for the solving basic problems of controlling mechanical properties.

PL

Przedmiotem pracy jest zjawisko destabilizacji w teksturze i mikrostrukturze wywołane zmianą drogi odkształcenia w stopie magnezu AZ31 i w miedzi. Badania oparte na pomiarach pojedynczych orientacjach techniką COM/EBSD w SEM, stanowią kontynuację wcześniejszych prac nad miedzią. Zjawiska w materiałach wywołane destabilizacją dostarczają nowych informacji cennych dla rozwiązania podstawowych problemów sterowania właściwościami mechanicznymi.

4

The evolution of deformation texture in copper by unidirectial and by cross roling

Ostafin M., Pospiech J., Schwarzer R.

Archives of Metallurgy and Materials

|

2005

|

Vol. 50, iss. 2

409-415

EN

The change of the deformation path has a strong effect on the formation of cold-rolling texture. In particular, the texture stabilized during rolling becomes unstable and disintegrates when the rolling direction is changed in the last stitches from unidirectional or reverse rolling to pseudo-cross rolling by rotating the sample through an angle of 90° or 45° about the normal direction. In addition to global texture, the microstructure is also specifically changed on a grain-size level. The change of the path of plastic deformation leads to a destabilization of the substructure which was formed during the primary step of rolling in one direction. In investigations on electrolytic copper distinct changes of texture and microstructure have been found depending on the deformation process. The orientation density function (ODF) shows that the reverse rolled starting sample of copper in this investigation contains only one component in the C={112}<111> position. By rotation about ND through 90° or 45°, the C component changes into the unstable C90={112}<110> or C45={112}<914> position, espectively, which almost disappears with progressive deformation. The effect of the mode of rolling on texture evolution has been studied in detail on a macroscopic scale by X-ray pole-figure measurement as well as on a grain-specific scale by individual grain orientation mapping (ACOM, “Automated EBSD”) in the SEM. The statistical distributions of grain orientations (pole figures, ODF), misorientations across grain boundaries (MODF) and &Sigma grain boundaries are considered.

PL

Zmiana drogi odkształcenia silnie oddziaływuje na teksturę walcowania. W szczególności tekstura ustabilizowana podczas walcowania staje się niestabilna i ulega rozpadowi, gdy w ostatnim etapie walcowanie jednokierunkowe lub rewersyjne zamieniamy na walcowanie poprzeczne obrotem próbki dookoła KN o 90° lub 45°. Równocześnie z teksturą globalną obserwowane są specyficzne zmiany w mikrostrukturze w skali wielkości porównywalnej z wielkością ziarna. Zmiana drogi plastycznego odkształcenia doprowadzą do destabilizacji substruktury, która została uformowana w początkowym etapie jednokierunkowego względnie rewersyjnego walcowania. W badaniach nad elektrolityczną miedzią wytworzone zostały znaczne zmiany w teksturze i mikrostrukturze w zależności od procesu odkształcenia. Funkcja gęstości orientacji (ODF) pokazała, że próbka do badań w stanie początkowym przed walcowaniem rewersyjnym zawiera tylko jedną składową w położeniu C={112}<111>. Po obrocie dookoła KN o 90° względnie 45°, składowa C przechodzi w niestabilne położenie odpowiednio C90={112}<110> względnie C45={112}<914>, które zanikają ze wzrostem odkształcenia. Wpływ sposobu walcowania na ewolucje tekstury badano szczegółowo zarówno w skali makro przez pomiar rentgenowskich figur biegunowych jak i w skali rozmiaru ziarna przez odwzorowanie indywidualnych orientacji ziarn techniką ACOM (automatyzowane EBSD) w SEM. Rozpatrywano rozkłady statystyczne orientacji ziarn (figura biegunowa, ODF), dezorientacje w poprzek granic ziarn (MODF) i granice specjalne &Sigma.

5

Inhomogeneity of deformation induced by the change of deformation path in channel-die compressed (112)[111] copper single crystals

Jasieński Z., Pospiech J., Schwarzer R., Piątkowski A., Litwora A.

Inżynieria Materiałowa

|

2004

|

R. XXV, nr 3

359-363

EN

The microtextural and microstructural effects caused by the change of the deformation path in the cold rolling process of fcc metals of medium SFE have been studied by SEM/EBSD and X-ray diffraction methods. The selected (112)[111) and (112)[110] orientations and the channel-die compression method in the investigation of copper single crystals enabled a more detailed characteristics of these effects. The aim of the investigations to elucidate the crystallographic conditions of the strong texture and structure alterations which were observed in deformed cold rolled polycrystalline copper after the change of the rolling direction by 90° rotation around ND. It has been found that the main textural effect is the destabilization of the {112}<110> orientation which leads to the appearance of the {110}<112> components of texture in pre-deformed single crystals. The fragmentation of the pre-deformed single crystal structure in the form of compact clusters of layers and/or non-regular blocks is the origin of the development of two {110}<112> complementary components of texture. It has been shown that the formation of two sets of layers with complementary components {110}<112> of texture in these banded structures of pre-deformed samples is similar to the deformation banding, which differs from the typical copper-type shear bands.

PL

Mikroteksturowe i mikrostrukturalne efekty zmiany drogi odkształcenia w procesie walcowania metali o sieci A1 i średniej energii błędu ułożenia badano przez pomiar pojedynczych orientacji z zastosowaniem SEM/EBSD oraz rentgenowski pomiar figur biegunowych. Wybór monokryształów miedzi orientacji (112)[111] i (112)[110] oraz metody nieswobodnego ściskania umożliwił bardziej szczegółową charakterystykę tych efektów. Wyjaśniono krystalograficzne uwarunkowania silnych zmian tekstury i struktury, obserwowanych w przypadku wstępnie walcowanej polikrystalicznej miedzi po zmianie drogi odkształcenia przez obrót 90° wokół ND. Stwierdzono, że głównym efektem teksturowym jest destabilizacja orientacji {112}<110>, powodująca wystąpienie składowych tekstury {110}<112> we wstępnie walcowanych próbkach monokrystalicznych jak również w monokryształach idealnej orientacji (112)[110] nie poddanych wstępnemu odkształceniu. Fragmentacja struktury odkształconych monokryształów w formie nieregularnych bloków lub zwartych pakietów pasm, jest przyczyną rozwoju dwóch komplementarnych składowych tekstury {110}. Wystąpienie warstw charakteryzujących się alternatywnie jedną z dwóch komplementarnych składowych tekstury {110}<112> we wstępnie walcowanych próbkach jest podobne do procesu tworzenia pasm odkształcenia znacznie różniących się mikrostrukturą od typowych pasm ścinania w miedzi.

6

Textural and structural effects of the change of deformation path in copper single crystals in a channel-die test

Jasieński Z., Pospiech J., Piątkowski A., Schwarzer R., Litwora A., Ostafin M.

Archives of Metallurgy and Materials

|

2004

|

Vol. 49, iss. 1

11-28

EN

The microtextural and microstructural effects caused by the change of the deformation path in the cold rolling process of fee metals of medium SFE have been studied by individual grain orientation measurement in the SEM (ACOM, "Automated EBSD") and by X-ray pole figure measurement. The choice of the (112)[111] and the (112)[110] orientations and channel-die compression for the investigation of copper single crystals enabled a more detailed characteristic of these effects. These investigations aim to elucidate the crystallographic conditions of the strong texture and structure changes which were observed in cold rolled polycrystalline copper after the change of the rolling direction. It has been found that the main textural effects is the destabilization of the {112}<110> orientation which leads to the appearance of the {110}<112> components of texture in pre-deformed crystals as well as in not pre-deformed (112)[110] single crystals. However, in the former case in which the deformation path was changed, the transformation proceeds much faster and more dynamic in comparison with the latter. The fragmentation of the pre-deformed single crystal structure in the form of non-regular blocks and/or compact clusters of layers is the origin of the development of two {110}<112> complementary components of texture. It has been shown that the formation of two sets of layer with complementary {110}<112> components of texture in these banded structures of pre-deformed samples is rather similar to deformation band, which differ from the typical copper-type shear bands.

PL

Mikroteksturowa i mikrostrukturalne efekty zmiany drogi odkształcenia w procesie walcowania metali o sieci Al i średniej energii błędu ułożenia badano przez pomiar pojedynczych orientacji przy użyciu SEM (ACOM, "Automated EBSD) oraz rentgenowski pomiar figur biegunowych. Wybór monokryształów miedzi orientacji (112)[111] i (112)[110] oraz metodyniesfobodnego ściskania umozliwił bardziej szczegółową charakterystykę tych efektów. Badania miały na celu wyjaśnienie krystalograficznych uwarunkowań silnych zmian tekstury i struktury, które obserwuje się w przypadku wstepnie walcowanej polikrystalicznej miedzi po zmianie drogi odkształcenia przez obrót 90 stopni wokół ND. Stwierdzono, że głównym efektem teksturowym jest destabilizacja orientacji {112}<110>, która powoduje wystapienie składowych tekstury {110}<112> we wstepnie walcowanych próbkach monokrystalicznych jak również w monokryształach idealnej orientacji (112)[110] nie poddanych wstepnemu odkształceniu. Jednakże w pierwszym przypadku transformacja tekstury jest bardziej dynamiczna. ragmentacja struktury odkształconych monokryształów w formie nieregularnych bl;oków a zwłaszcza w formie zwartych pakietów warstw, występujących głównie we wstepnie odkształconych próbkach jest przyczyną rozwoju dwóch komplementarnych składowych tekstury {110}<112>. Wykazano, że powstanie dwóch zbiorów warstw charakteryzujących sie alternatywnie jedną z dwóch komplementarnych składowych tekstury {110}<112> we wstepnie walcowanych próbkach jest podobne raczej do procesutworzenia pasm odkształcenia znacznie różniących się od struktury typowych pasm ścinania w miedzi.

7

Microstructural aspects of crossrolling of copper

Pospiech J., Ostafin M., Schwarzer R.A.

Inżynieria Materiałowa

|

2003

|

R. XXIV, nr 6

802-805

EN

The objectives of this investigation are structural effects in fcc metals (here represented by pure copper) that are caused by the change of the direction of rolling. The studies are mainly based on results of individual grain orientation measurements performed by EBSD in the SEM on relatively large sample areas. The change of the path of plastic deformation leads to destabilization of the substructure formed during primary unidirectional rolling. The results of measurement enable a detailed analysis of the micro- macrostructure of deformed material with the aid of orientation distributions and characteristics determined from sets of orientation differences across grain boundaries.

PL

Przedmiotem badań są skutki, które w mikrostrukturze i teksturze wywołuje odkształcenie po zmianie kierunku walcowania w metalach sieci A1 na przykładzie czystej miedzi. Badania oparte są głównie na wynikach automatycznych pomiarów lokalnych orientacji krystalograficznych wykonanych techniką EBSD/SEM na względnie dużych powierzchniach próbki. Zmiana drogi plastycznego odkształcenia doprowadza do destabilizacji substruktury uformowanej podczas pierowtnego jednokierunkowego walcowania. Wyniki z pomiarów lokalnych orientacji pozwalają na szczegółową analizę mikro i makrotekstury odkształconego materiału za pomocą funkcji rozkładu orientacji i charakterystyk określonych przez różne zestawy zbiorów różnic orientacji.

8

Zjawisko żebrowania w stalach odpornych na korozję o strukturze ferrytycznej

Rostek T., Sztwiertnia K., Pospiech J., Bołd T.

Archiwum Nauki o Materiałach

|

2002

|

T. 23, nr 4

283-299

PL

Na podstawie prac własnych oraz danych z literatury dokonano syntetycznego opisu zjawiska żebrowania w ferrytycznych stalach chromowych odpornych na korozję. Badania wykazały pewne prawidłowości w strukturze i teksturze materiału mogące mieć wpływ na zjawisko żebrowania. W mikroteksturze materiału wyodrębniono dwa elementy o odmiennej anizotropii plastycznej; pasma orientacji {001}<110> oraz osnowę, w której przeważają obszary o orientacjach {112}<110>, {111}<112> i {111}<134>. Zwrócono również uwagę na segregację pierwiastków stopowych i jej związek z występowaniem niejednorodności oraz podatnością na korozję blach ze stali ferrytycznej. Zaproponowano zmiany w tradycyjnej technologii produkcji blach w celu minimalizacji niekorzystnego zjawiska żebrowania.

EN

Based on the authors' own investigations, as well as on observations of other authors, synthetic description of ridging phenomenon occuring in ferritic stainless steel was made. Investigations show some regularities in structure and texture having influence on the ridging phenomenon. The material is composed of two macro-elements of different plastic anisotropy: the bands described by the texture component {001}<110> and the matrix described by the components {112}<110>, {111}<112> and {111}<134>. The segregation of the alloy elements may play an important role in the formation of these inhomogeneities and in the corrosion of sheets. The proposed changes in the traditional technological processing of sheets obtained from this steel type are to limit the occurrence of the ridging effect.

9

The comparison of unidirectional and reverse rolling textures in polycrystalline FCC metals with different stacking fault energy

Wróbel M., Pospiech J., Bonarski J., Blicharski M., Dymek S.

Archives of Metallurgy

|

2002

|

Vol. 47, iss. 2

185-195

EN

The formation of texture and microstructure in polycrystalline Cu and Cu-5 wt.%Al alloy during two modes of homogenous rolling have been compared. two samples of each metal were rolled. one sample was rolled unidirectionally, while the other by reverse rolling. Some differences in the textures depending on the rolling mode have been observed in the range of deformation of the Cu-5 wt.%Al alloy where intensive twinning took place. It was also found that the texture of reverse rolling was more homogeneous across the thickness of the rolled alloy sheet than the texture of unidirectionally rolled material. no clear effect of the rolling mode on microstructure has been observed.

PL

W pracy porównano tekstury dwóch sposobów walcowania polikrystalicznych metali: miedzi i stopu Cu-5%Al. Dla kazdego z metali jednorodnie przewalcowano po dwie próbki.Dla jednej z nich, kierunek walcowania był taki sam w każdym przepuście (walcowanie jednokierunkowe). Dla drugiej próbki po każdym przepuście kierunek walcowania zmieniano na kierunek przeciwny (walcowanie rewersyjne). Sposób walcowania wplywał na teksturę jedynie w przypadku stopu Cu-5%Al, w tym zakresie odkształceń, w którym zachodziło intensywne bliźniakowanie. Dla stopu, stwierdzono większą jednorodność rozkładu tekstury na grubość płaskowników przewalcowanych rewersyjnie niż w przypadku płaskowników przewalcowanych jednokierunkowo. Nie obserwowano wyraźnego wpływu sposobu walcowania na mikrostrukturę.

10

Microstructure development in ridging affected ferritic

Sztwiertnia K., Pospiech J., Rostek T., Faryna M.

Archives of Metallurgy

|

2002

|

Vol. 47, iss. 2

197-204

EN

The subject of investigation is the ridging phenomenon occuring in ferritic stainless chromium steels. the origin of this undersirable surface phenomenon is connected with the observed strips of texture inhomogenities showing plastic anisotropy. Basing on measurements of crystallographic orientation topography the texture inhomogeneities together with the ridging effects have been investigated in sheets from earlier stages of the production process. The proposed changes in the traditional technological processing of sheets obtained from this steel type are intended to limit the occurrence of ridging effect.

PL

Przedmiotem badań jest zjawisko żebrowania występujące w blachach ferrytycznej stali chromowej odpornej na korozję. Przyczyny tego zjawiska powierzchniowego związane są z występującymi pasmami niejednorodności tekstury wykazującymi anizotropię plastyczną. W oparciu o pomiary topografii orientacji krystalograficznych badano niejednorodność tekstury w powiązaniu z efektami żebrowania we wczesnych stadiach procesu produkcjiblach. Zaproponowano zmiany w tradycyjnej technologii produkcji blach w celu ograniczenia wystepowania efektu żebrowania.

11

Origin of the ridging phenomenon in ferritic stainless steels.

Sztwiertnia K., Pospiech J., Rostek T., Bołd T.

Inżynieria Materiałowa

|

2001

|

R. XXII, nr 5

904-907

EN

The subject of investigation is the ridging phenomenon, occuring in ferritic stainless chromium steels. The origin of this undesirable surface phenomenon is connected with the observed strips of texture inhomogeneities showing plastic anisotropy. Basing on measurements of crystallographic orientation topography in the sample area the development of texture inhomogeneities together with the ridging effects in the earlier stages of the process of sheet production were investigated. The proposed changes in the traditional technological processing of sheets from this steel type are intended to limit the occurrence of the ridging effect.

PL

Przedmiotem badań jest zjawisko żebrowania występujące w blachach ferrytycznej stali chromowej odpornej na korozję. Przyczyny tego niekorzystnego zjawiska powierzchniowego związane są z pasmowymi niejednorodnościami tekstury wykazującymi anizotropię plastyczną. W oparciu o pomiar topografii orientacji krystalograficznych w obszarach próbki badano rozwój niejednorodności tekstury wraz z efektami żebrowania we wczesnych stadiach procesu produkcji blach. Zaproponowano zmiany w tradycyjnej technologii produkcji blach w celu ograniczenia występowania efektu żebrowania.

12

Influence of rolling mode on texture development in polycrystalline Cu and Cu-5 wt.% Al alloy.

Wróbel M., Pospiech J., Bonarski J., Blicharski M., Moskalewicz T.

Inżynieria Materiałowa

|

2001

|

R. XXII, nr 5

970-973

EN

Texture and microstructure development during homogeneous rolling of polycrystalline Cu and Cu-5 wt. % Al alloy were investigated. Two samples of each metal were rolled. One sample was rolled only in one direction in all passes. The second one was rolled in both directions by reversing the ends between passes. Some differences in the textures depending on the rolling mode have been observed in the deformation range of intensive twinning of the Cu-5 wt. % Al alloy and explained by polarization of twinning. No clear effect of the rolling mode on microstructure was observed.

PL

W pracy przedstawiono wyniki badań rozwoju tekstury i mikrostruktury podczas jednorodnego walcowania materiałów polikrystalicznych Cu i Cu-5%Al. Walcowano po dwie próbki każdego materiału. Jedna z nich była walcowana w tym samym kierunku w każdym przepuście a w przypadku drugiej próbki, w kolejnych przepustach kierunek walcowania zmieniano na przeciwny. Na teksturę stopu Cu-5%Al wpływał sposób walcowania w zakresie odkształceń intensywnego bliźniakowania. W przypadku miedzi nie zaobserwowano wpływu sposobu walcowania na teksturę. Nie zaobserwowano również wpływu sposobu walcowania na mikrostrukturę obydwu metali.

13

Orientation topography and ridging phenomenon in ferritic stainless steel sheets

Sztwiertnia K., Pospiech J.

Archives of Metallurgy

|

1999

|

Vol. 44, iss. 2

157-165

14

Ridging phenomenon in ferritic stainless steels.

Sztwiertnia K., Pospiech J., Bethke K.

Inżynieria Materiałowa

|

1998

|

R. XIX, nr 3

264-267

EN

FeCr17 ferritic stainless steel sheets, after cold rolling and annealing, exhibits ridging in the case of rolling direction elongation. The resulting deterioration in surface quality is a serve and long known problem in industrial processing. This problem is here investigated by the SEM-EBSD technique (Electron Backscattering Diffraction in the Scanning Electron Microscope). The results of the single orientation analysis suggest that to clarify the origin of the ridging morphology ealier models such as that elaborated by Wright (4) can be adopted.

15

Microtexture development during the alpha -> gamma phase transformation in steel.

Bruckner G., Pospiech J., Seidl I., Gottstein G.

Inżynieria Materiałowa

|

1998

|

R. XIX, nr 3

204-208

EN

In a microalloyed low carbon steel diffusion controlled alpha -> gamma phase transformation was investigated by use of EBSD. Orientation Microscopy was performed on a marked spot both in the ferritic and after transformation in the austenitic state. Through an appropriate process the austenitic state was preserved even at room temperature. In the phase transformation the Kurdjumov - Sachs (K-S) relation dominates.