Bipolar transport of charge carriers in thin films of 9,10-dimethylanthracene and 1-acenaphthenol

Kania S., Kuliński J., Marciniak B., Różycka-Sokołowska E

Scientific Bulletin. Physics / Lodz University of Technology

|

2014

|

Vol. 35

33--39

EN

The current-voltage (I-U) characteristics we have been measured for thin films of 1-acenaphthenol and 9,10-dimethylanthracene prepared from their commercially available materials as products with purity ≥ 10-3 mass %. Using the method of differential processing of the characteristics, charge transport mechanism in these films was assessed.

PL

Stosując kryteria dyskryminujące zasięg występowania mechanizmów przewodzenia można postawić hipotezę, że prądy płynące przez warstwy 9,10 dimetyloantracenu są bipolarne, zaś w przypadku 1-acenaftolu prądy mogą być monopolarne lub bipolarne. Wysokie wartości ruchliwości dla obu materiałów wskazują na ich duży potencjał do potrzeb elektroniki organicznej. Bipolarność prądów płynących przez 9,10 dimetyloantracen w połączeniu ze stabilnością chemiczną i mechaniczną uzyskiwanych z niego warstw pozwala traktować ten materiał jako wysoce przydatny dla potrzeb optoelektroniki.

2

Some electrical properties of thin layers of 9,10-dimethylanthracene and 1-acenaphthenol

Kania S., Kuliński J., Marciniak B., Różycka-Sokołowska E

Scientific Bulletin. Physics / Lodz University of Technology

|

2013

|

Vol. 34

35--42

EN

Spectral grade materials obtained in zone-melting process from commercially available 1-acenaphthenol and 9,10-dimethyl-anthracene were characterized electrically. The layers vaporized in 10-5 Torr vacuum posses high resistivity of the order of 1011 - 1012 Ωm and the concentration of traps lower than 1015cm-3.

PL

Zbadano własności elektryczne materiałów o czystości spektralnej uzyskanych metodą dodatkowego oczyszczania strefowego komercyjnie dostępnych 1-acenaftolu i 9,10-dimetyloantracenu. Warstwy wymienionych związków, naparowywane w próżni 10-5 Tr, wykazywały wysoką oporność właściwą w granicach 1011 - 10 12 Ωm i charakteryzowały się bardzo niską zawartością pułapek rzędu 1011 - 10 14 cm-3. Wyniki świadczą o stabilności molekuł badanych materiałów w warunkach naparowywania termicznego w próżni 10-5 Tr oraz o ich zdolności do łatwej nukleacji na złotych elektrodach. Warstwy wykazują stabilność rezystancji aż do wartości pola polaryzacji 2 · 107 V/m.

3

Nucleation behaviour of the growth solutions of fluoranthene in 1,2-dichloroethane

Różycka-Sokołowska E., Szyrej M., Kończyk J., Balińska A., Marciniak B.

Prace Naukowe. Chemia i Ochrona Środowiska / Wyższa Szkoła Pedagogiczna w Częstochowie

|

2003

|

Vol. 7

85--98

EN

The nucleation kinetics of fluoranthene in 1,2-dichloroethane solution from which good quality crystals of that hydrocarbon were previously grown have been studied. Measurements of the metastable zone width (MSZW), represented by the maximum undercooling ((ΔΘmax), which were carried out by means of the density, ultrasonic velocity and transparency techniques, have shown the great influence of the detection manner of the crystallisation onset on the determined values of the first precipitation temperatures (Tp) as well as on the MSZW values. Moreover, from the assessment of this parameter as a function of cooling rate (b), the linear dependence between log b and log ΔΘmax was established. Basing on the nucleation orders (m) and the nucleation rate constants (kN) resulting from this assessment, the nucleation rate (RN) and the interfacial tension (ysl) values for fluoranthene in the solution at the growth temperature of its crystals have been determined. A good agreement obtained between the ysl values derived from the MSZW determined by these three techniques may be treated as one of the most interesting results of this study.

PL

Badano kinetykę zarodkowania fluorantenu w roztworze 1,2-dichloroetanu. z którego otrzymano wcześniej dobrej jakości kryształy tego węglowodoru. Pomiary szerokości obszaru metastabilnego, wyrażonego w postaci maksymalnego przechłodzenia (ΔΘmax), które przeprowadzono przy użyciu trzech różnych technik opartych na badaniu gęstości, prędkości rozchodzenia się fal ultradźwiękowych i przezroczystości próbek badanego roztworu, wykazały duży wpływ sposobu detekcji początku krystalizacji fluorantenu, zarówno na wyznaczone w ten sposób wartości temperatur odpowiadających temu początkowi (Tp), jak i wartości szerokości obszaru metastabilnego. Ponadto na podstawie oszacowania wartości ΔΘmax w funkcji szybkości ochładzania (b) roztworu ustalono, że spełniona jest dla niego liniowa zależność pomiędzy log b i log ΔΘmax. Następnie, opierając się na wynikających z tego oszacowania wartościach rzędu zarodkowania (m) oraz stałej szybkości zarodkowania (kN), wyznaczono wartości szybkości zarodkowania (RN) oraz oszacowano na ich podstawie wartości międzyfazowego napięcia powierzchniowego (γsl) fluorantenu w temperaturze wzrostu jego kryształów. Dobra zgodność, którą uzyskano pomiędzy wartościami γsl wyznaczonymi na podstawie szerokości obszaru metastabilnego, zmierzonego przy użyciu trzech różnych technik pomiarowych, może być traktowana jako jeden z najbardziej interesujących wyników przeprowadzonych przez nas badań.

4

The morphology of crystals of a metastable anthracene phase, formed during their growth from the vapour phase

Różycka-Sokołowska E., Marciniak B., Pawliuk W.

Prace Naukowe. Chemia / Wyższa Szkoła Pedagogiczna w Częstochowie

|

2001

|

Vol. 5

57--65