1
Content available Examinations of the Welded Joint T91 Steel After Service at Elevated Temperature
Golański G., Merda A., Klimaszewska K., Wieczorek P.
Archives of Metallurgy and Materials
|
2020
|
Vol. 65, iss. 1
237--242
EN
The article provides results of the microstructure examinations and mechanical properties (hardness and microhardness tests) of the welded joint T91 steel taken from the live steam pipeline. Examined joint has been exploited for about 45 000 hours in a temperature of 535°C and the steam pressure equals to 13.5 MPa. Examined joint was made as a double bead by the additional materials with a different chemical composition. It was proved that the joint was characterized by a differential microstructure on the cross-section of the weld. Moreover, decarburized zone in the lower alloyed material and carbides zone in the higher alloyed material were revealed in the weld line and on the boundary penetration of beads. Furthermore, it was shown that the main mechanism of a joint degradation is a privileged precipitation of carbides on the grain boundaries, and an increase of their size.
2
Content available Metallurgical analysis of the causes of failure of the hardening furnace conveyor belt
Merda A., Klimaszewska K., Sroka M., Golański G.
Archives of Materials Science and Engineering
|
2019
|
Vol. 98, nr 2
68--73
EN
Purpose: The aim of the tests was to analyze the microstructure and mechanical properties of a section of the hardening furnace conveyor belt serviced at the temperature of 880-920°C in the carburizing atmosphere, in the context of determining the probable causes of its failure. Design/methodology/approach: The scope of performed tests included: chemical composition analysis of the steel and particles, microstructure investigated using optical and scanning electron microscopy, X-ray phase analysis. Findings: The analysis of the chemical composition showed that the examined material was austenitic steel X15CrNiSi25-21 (S310). Performed metallurgical tests showed that after the service the examined steel was characterized by austenitic structure with numerous precipitates of diverse morphology. In the structure the sigma phase particles and probably the M23C6 carbides precipitates were observed. The continuous grid of precipitates on the boundaries of grains (mainly the sigma phase) and the influence of the cyclic changing heat loads (or thermo-mechanical loads) were the main causes of failure of the analysed detail. Research limitations/implications: The aim of the work was to determine the probable causes of damage of the material used for a conveyor belt of a hardening furnace. Practical implications: The results of investigation and analysis of the metallographic of het-resisting austenitic steel X15CrNiSi25-21 (S310) after service at the temperature of 880-920°C are presented. Originality/value: The paper presents the results of research on the microstructure and mechanical properties of the section of hardening furnace conveyor belt made of creepresisting austenitic steel. The aim of the performed tests was to determine the probable causes of damage of the analysed detail.
3
Content available remote Ocena jakości złącza różnoimiennego ze stali HARDOX 450® i Strenx 700 MC®
Klimaszewska K., Lis R., Słania J., Golański G.
Przegląd Spawalnictwa
|
2018
|
R. 90, nr 8
9--12
PL
W pracy poddano weryfikacji pod względem jakości złącze spawane ze stali HARDOX 450® i Strenx 700MC®. W tym celu wykonano różnoimienne złącze doczołowe metodą MAG z wykorzystaniem materiału dodatkowego w postaci drutu w gatunku 4Si1. Zakres badań obejmował badania nieniszczące: badania wizualne (VT), penetracyjne (PT) oraz radiograficzne (RT). Wykonano także badania niszczące polegające na obserwacjach makro- i mikroskopowych na przekroju złącza. Przeprowadzone badania wykazały, że zastosowanie materiału dodatkowego w postaci drutu w gatunku 4Si1 do łączenia stali HARDOX 450® ze stalą Strenx 700MC® zapewnia uzyskanie wymaganej jakości „B” połączeń spawanych. Analizowane złącze charakteryzowało się typową mikrostrukturą dla użytych materiałów rodzimych.
EN
The paper presents the results of quality assessment of welded joints. The scope of the work was to investigate the non-destructive testing: visual testing (VT), penetration testing (PT) and radiological testing (RT). The study included also the survey breaking the macro- and microstructural test on the welded joint section. The research has shown that the use of the welding consumables in form of a wire 4Si1 to joint HARDOX 450® with Strenx 700MC® ensures the required "B" quality of welded joints in accordance with regulatory requirements. The analyzed joint was characterized by typical microstructure for native materials used.
4
Content available remote Aspekty strukturalne różnorodnych złączy spawanych ze stali Super 304H i T91
Klimaszewska K., Słania J., Wieczorek P., Urbańczyk P., Golański G.
Przegląd Spawalnictwa
|
2018
|
R. 90, nr 6
24--28
PL
W pracy przedstawiono wyniki badań makro- i mikroskopowych różnorodnych złączy spawanych ze stali Super 304H i T91, wykonane metodą 141 (TIG) w pozycji PF. Materiałem dodatkowym był pręt lity Metrode EPRI P87. Badaniom metalograficznym poddano złącze po spawaniu (S1) i po obróbce cieplnej (S2), która została dobrana pod kątem składu chemicznego stali T91 i polegała na wyżarzaniu odprężającym w temperaturze 760 °C w czasie wygrzewania 2 godziny. Proces spawania, jak i obróbka cieplna w obszarze strefy wpływu ciepła (SWC) w przypadku stali Super 304H przyczyniły się do powstania procesów wydzieleniowych głównie na granicach ziaren. W SWC stali T91 zabiegi te spowodowały powstanie gruboziarnistej i zdegradowanej struktury martenzytycznej z licznymi wydzieleniami o zróżnicowanej morfologii.
EN
The paper presents the results of macro- and microscopic tests of heterogeneous welded joints made of Super 304H steel and T91 steel. The examined welded joints were made with the 141 (TIG) method in the PF welding position, using a Metrode EPRI P87 wire as the additional material. The tests were performed on the joint after welding and after heat treatment which consisted in the stress relief annealing at the temperature of 760 °C and soaking time of 2 hours. The investigated joints were marked respectively: S1 (the joint without heat treatment) and S2 (the joint after heat treatment). The process of welding, as well as the heat treatment in the area of the heat-affected zone (HAZ) in the case of Super 304H steel contributed to the precipitation processes mostlyon the boundaries of grains. In the HAZ of T91 steel these processes caused the development of a degraded martensitic structure with numerous precipitates of diverse morphology.
5
Content available Microstructure and mechanical properties of a similar T24 steel welded joint after service
Merda A., Golański G., Urbańczyk P., Klimaszewska K.
Prace Instytutu Metalurgii Żelaza
|
2018
|
T. 70, nr 2
37--41
EN
The material under investigation was a welded joint made of 7CrMoVTiB10-10 (T24) steel after 36,000 hours of use at the temperature of 540°C and pressure of 27 MPa. The test samples for the study were taken from a membrane wall of a USC steam boiler. The research scope included: analysis of chemical composition of the original and the additional material (weld pass), investigation of the microstructure using optical microscopy and scanning electron microscopy, as well as tests of mechanical properties of the joint - hardness measurement. It was proved that the investigated joint was characterised by a regular structure, without any welding defects, which probably resulted from the application of the additional material based on the CrMo steel from the weld root side. The observation showed that the microstructure of the original material consisted of granular bainite with numerous precipitates. In the heat affected zone and in the weld, the microstructure of lath bainite (bainitic-martensitic microstructure) was observed, also with numerous precipitates. The hardness of the analysed joint was lower than the limiting value of 350HV.
PL
Badaniu poddano jednoimienne złącze spawane stali 7CrMoVTiB10-10 (T24) po ok. 36 000 godzinach eksploatacji w temperaturze 540°C i ciśnieniu 27 MPa. Próbki do badań pobrano z wycinka ściany szczelnej kotła energetycznego na parametry nadkrytyczne. Zakres przeprowadzonych badań obejmował: analizę składu chemicznego materiału rodzimego oraz materiału dodatkowego, badania mikrostrukturalne za pomocą mikroskopii świetlnej i skaningowej mikroskopii elektronowej oraz badania właściwości mechanicznych złącza - pomiar twardości. Wykazano, że badane złącze charakteryzuje się prawidłową budową, bez niezgodności spawalniczych, co zapewne wynika z zastosowania od strony grani materiału dodatkowego na bazie stali CrMo. Przeprowadzone obserwacje wykazały, że mikrostruktura materiału rodzimego składa się z bainitu ziarnistego z licznymi wydzieleniami. W strefie wpływu ciepła i spoinie obserwowano mikrostrukturę bainitu listwowego (bainityczno-martenzytyczną) również z licznymi wydzieleniami. Twardość analizowanego złącza była niższa od wartości granicznej wynoszącej 350HV.
6
Content available remote Microstructure and mechanical properties of the Sanicro 25 steel after ageing
Merda A., Sroka M., Klimaszewska K., Golański G.
Journal of Achievements in Materials and Manufacturing Engineering
|
2018
|
Vol. 91, nr 1
5--11
EN
Purpose: The purpose of the research was to determine and analyse the changes in the microstructure and mechanical properties of the Sanicro 25 steel in the as-received condition and after ageing at 600, 650 and 700°C for up to 10,000 hours. Design/methodology/approach: The scope of the investigations included: microstructural investigation – SEM microscopy, analysis of precipitation performed using TEM microscopy, investigation of mechanical properties, Vickers hardness measurement. Findings: In the as-received condition, the Sanicro 25 steel was characterised by austenitic microstructure with annealing twins and numerous primary precipitates. The analysis of Sanicro 25 steel microstructure after ageing at 600 and 700°C for up to 10,000 hours revealed significant changes in the microstructure consisting mainly in a tendency to create unfavourable morphology of secondary precipitates – M23C6 carbides that form continuous carbide systems along the grain boundaries. The observations have shown that during long-term ageing the secondary carbides were also precipitated inside the grains and at the interface of three grain boundaries – σ phase. Research limitations/implications: The analysis of the microstructure of the examined steel using SEM and TEM was performed to determine the influence of ageing on the processes of changes in the precipitate morphology. Practical implications: The results obtained based on the performed research constitute a building block for the degradation characteristics of the microstructure and mechanical properties of the 23/25-type austenitic steels. Originality/value: The results of the investigation and analysis of the metallographic and mechanical properties of the Sanicro25 austenitic steel in as-received condition and after ageing are presented.
7
Nowe żarowytrzymałe stale o strukturze austenitycznej dla energetyki
Golański G., Merda A., Klimaszewska K.
Hutnik, Wiadomości Hutnicze
|
2018
|
Vol. 85, nr 12
410--416
PL
Rozwój przemysłu energetycznego determinowany jest obecnie wymaganiami środowiskowymi Unii Europejskiej, co wymusza stosowanie rozwiązań proekologicznych, których celem jest ograniczenie negatywnego wpływu tej dziedziny gospodarki na środowisko. Jednym z takich rozwiązań jest wzrost parametrów pracy bloków energetycznych, celem ograniczenia emisji zanieczyszczeń oraz podwyższenie ich sprawności. Wzrost parametrów pracy bloków wymusza wprowadzenie nowych, żarowytrzymałych materiałów konstrukcyjnych między innymi nowoczesnych, żarowytrzymałych stali austenitycznych. W artykule na podstawie badań własnych oraz danych literaturowych przedstawiono podstawową charakterystykę nowoczesnych żarowytrzymałych stali austenitycznych w stanie dostawy – TP374HFG, Super 304H, HR3C oraz Sanicro 25.
EN
The development of the power industry is currently determined by the environmental requirements of European Union, which forces the use of proecological solutions. The aim of these solutions is limiting the negative influence of this branch of economics on the environment. One of these solutions consists in raising the working parameters of power units to limit the emission of pollution and increase the efficiency. The growth of the parameters of work of power units forces the introduction of modern creep-resisting construction materials, among other, the modern creep-resisting austenitic steels. The paper presents the basic characteristics of modern creep-resisting austenitic steels in delivery condition: TP374HFG, Super 304H, HR3C and Sanicro 25 on the basis of the authors’ research and the literature data.
8
Analiza mikrostruktury i właściwości mechanicznych stali VM12-SHC po eksploatacji
Klimaszewska K., Merda A., Urbańczyk P., Golański G.
Hutnik, Wiadomości Hutnicze
|
2018
|
Vol. 85, nr 12
424--426
PL
Badaniom poddano stal VM12-SHC po eksploatacji w temperaturze 545-560°C przy ciśnieniu pary 4,5 MPa po czasie 18 301 godzin. Zakres przeprowadzonych badań obejmował: określenie składu chemicznego zrealizowane za pomocą spektrometru iskrowego SpectroLab K2 oraz analizę mikrostrukturalną wykonaną za pomocą skaningowego mikroskopu elektronowego (SEM). Zakres przeprowadzonych badań mechanicznych obejmował: pomiar twardości metodą Vickers’a, statyczną próbę rozciągania oraz próbę udarności. Analizę wydzieleń przeprowadzono za pomocą metody izolatów węglikowych. Badana stal po eksploatacji charakteryzowała się strukturą martenzytyczną z licznymi wydzieleniami węglików M23C6, fazy Lavesa oraz złożonych azotków CrNbN (faza Z). Przeprowadzone badania mikrostruktury i właściwości mechanicznych stali VM12-SHC wykazały względnie niewielki stopień degradacji badanego materiału, co przełożyło się na zachowane nadal wysokie właściwości mechaniczne badanej stali.
EN
The investigated material was VM12-SHC steel after service at the temperature of 545-560°C and steam pressure of 4.5 MPa after 18 301 hours. The scope of the research included: the study of the chemical composition using a spark spectrometer SpectroLab K2, and microstructural tests by a scanning electron microscope (SEM). The scope of mechanical tests included: the hardness measurement by the Vickers method, the static test of tension and the impact strength test. The analysis of precipitates was performed using the method of carbide isolates. The examined steel after service was characterised by a martensitic structure with numerous precipitations of M23C6 carbides, Laves phase and CrNbN (Z phase). The tests performed on the microstructure and mechanical properties of VM12-SHC steel showed a relatively minor degree of degradation of the examined material, which was reflected in high mechanical properties of the investigated steel.
9
Wpływ starzenia na mikrostrukturę i właściwości stali HR3C
Klimaszewska K., Golański G., Urbańczyk P.
Energetyka
|
2018
|
nr 11
622--624
PL
Badaniom metaloznawczym poddano stal HR3C w stanie dostawy oraz po procesie starzenia w temperaturze 600°C i 700°C w czasie do 10 000 godzin. Zakres przeprowadzonych badań obejmował: badania strukturalne za pomocą skaningowej mikroskopii elektronowej oraz badania mechaniczne: pomiar twardości i próbę udarności. Stal HR3C w stanie dostawy dostarczana jest po ­przesycaniu. Charakteryzuje się mikrostrukturą austenityczną z bliźniakami wyżarzania oraz z licznymi wydzieleniami pierwotnymi. Struktura ta zapewnia uzyskanie wysokiej ciągliwości (praca łamania na poziomie 212 J) i względnie niskiej twardości 176 HV30. Obserwacje mikroskopowe stali HR3C po procesie starzenia ujawniły istotne zmiany mikrostruktury polegające głównie na tendencji do tworzenia niekorzystnej morfologii wydzieleń faz wtórnych na granicach ziaren, wewnątrz ziaren oraz na pojedynczych granicach bliźniaczych. Procesy te przyczyniły się do spadku ciągliwości badanej stali przy jednoczesnym wzroście twardości. Bardziej zaawansowane procesy wydzieleniowe obserwowano w stali starzonej w temperaturze 700°C.
EN
The physical metallurgical tests were performed on HR3C steel in the as-received state and after the process of ageing at the temperature of 600°C and 700°C, at times up to 10 000 hours. The range of the conducted tests included: structural tests using the scanning electron ­microscopy and mechanical tests: measurement of hardness and impact strength tests. The HR3C steel in the as-received condition was delivered after supersaturation and was characterised by the austenitic microstructure with annealing twins and numerous primary precipitates. Such a structure ensured obtaining high ductility (notch toughness at the level of 212 J) and relatively low hardness of 176 HV30. The microscopic observations of the HR3C steel after the ageing process revealed significant changes in the microstructure consisting mostly in the tendency to form unfavourable morphology of the secondary phases precipitates on the boundaries of grains, inside the grains, as well as on single twin boundaries. These processes contributed to a decrease in ductility of the examined steel, at the concurrent growth of hardness. The more advanced precipitation processes were observed in the steel aged at the temperature of 700°C.
10
Content available remote Analysis of the microstructure and properties of T92 steel after long-term service
Merda A., Klimaszewska K., Sroka M., Wieczorek P, Golański G.
Archives of Materials Science and Engineering
|
2018
|
Vol. 93, nr 1
5--11
EN
Purpose: The purpose of the investigation was to determine and analyse the changes in the microstructure and mechanical properties of the T92 steel after service in creep conditions of the following parameters: temperature – 575°C, pressure – 28.2 MPa, service time – 41914 hrs. Design/methodology/approach: The tests were performed on the test samples taken from a pipe section of a steam superheater after long-term service. The range of the investigations included: microstructural investigation – the optical and SEM microscopy, the analysis of precipitation – carbide isolates, the investigation of mechanical properties: the Vickers hardness measurement, the impact test and static tensile test. Findings: The performed tests showed a slight degree of exhaustion of the structure of the analysed T92 steel. The relatively small changes in the microstructure of the examined steel were reflected in the still retained high mechanical properties. Research limitations/implications: he analysis of the microstructure of the examined steel using SEM was performed to determine the influence of the service on the processes of changes in the precipitate morphology. Practical implications: The metal science investigation of the sections taken from the elements of the power installations after long-term service is one of the basic elements of building the data base of materials and their joints used in the power industry. The results obtained from the performed research constitute a building block for the degradation characteristics of the microstructure and mechanical properties of martensitic steels of the 9-12%Cr type. Originality/value: The results of investigation and analysis of the metallographic and mechanical properties of martensitic T92 steel after long-term service are presented.
11
Content available remote Microstructure and mechanical properties of HR3C austenitic steel after service
Golański G., Kolan C., Zieliński A., Klimaszewska K., Merda A., Sroka M., Kłosowicz J.
Archives of Materials Science and Engineering
|
2016
|
Vol. 81, nr 2
62--67
EN
Purpose: The purpose of the investigations was to determine changes in the microstructure and mechanical properties of HR3C creep resisting austenitic steel after service. Design/methodology/approach: The investigations were performed on test specimens taken from a part of the steam superheater tube. The range of the investigations included: microstructural investigations - light and SEM microscope; analysis of precipitates - carbide isolates; investigations of mechanical properties - hardness measurement, static tensile test, impact test. Findings: The precipitation processes at the grain boundaries lead to increase in intergranular corrosion of the HR3C steel resulting in loss of grains in the structure. The impact strength testing on test specimens with reduced width may result in overestimation of crack resistance of the material after service. Research limitations/implications: The comprehensive analysis of precipitation processes requires TEM examinations. Finding the correlation between the impact strength determined on standard vs. non-standard test specimens with reduced width. Practical implications: The obtained results of investigations are used in industrial practice for diagnosis of pressure parts of power boilers. Test procedures developed based on comprehensive materials testing conducted under laboratory conditions are used in upgrading and design of pressure parts of steam boilers. The results of investigations are also the element of database of the materials characteristics of steels and alloys as well as welded joints made of them working under creep conditions developed by the Institute for Ferrous Metallurgy. Originality/value: The results and analysis of the investigations of microstructure and mechanical properties of HR3C steel after service under actual boiler conditions are presented.
12
Content available Charakterystyka mikrostruktury i własności wybranych gatunków staliw
Maruszczyk A., Klimaszewska K., Kolan C.
Journal of Technology and Exploitation in Mechanical Engineering
|
2015
|
Vol. 1, nr 1-2
59--79
PL
W pracy wykazano jak ważną grupę materiałów inżynierskich stanowią staliwa. Przedstawiono główne sektory, w których stosuje się wyroby staliwne. Omówiono najważniejsze zalety oraz wady staliw. Przedstawiono ogólny podział stopów żelaza ze szczególnym uwzględnieniem staliw. Omówiono technologię wytwarzania wyrobów staliwnych. Scharakteryzowano najczęściej występujące w wyrobach staliwnych wady odlewnicze. Omówiono wpływ składu chemicznego staliw na mikrostrukturę oraz własności. Dokonano podziału staliw na poszczególne grupy, takie jak: staliwa narzędziowe, niestopowe (węglowe), żaroodporne, żarowytrzymałe, odporne na korozję oraz na ścieranie. Scharakteryzowano każdą z grup pod kątem zastosowania, składu chemicznego oraz własności. Część badawcza pracy obejmuje charakterystykę mikrostrukturalną wybranych gatunków staliw niestopowych(węglowych) oraz odpornych na ścieranie. Analizie mikrostrukturalnej poddano próbki następujących gatunków staliw niestopowych (węglowych): GS52 oraz 270-480W, oraz próbki następujących gatunków staliw odpornych na ścieranie: L45G oraz L35GSM. Przeprowadzona analiza mikrostruktur wykazała duże zróżnicowanie pomiędzy staliwami należącymi do grupy staliw niestopowych (węglowych), a grupą staliw odpornych na ścieranie. W strukturze badanych gatunków staliw niestopowych (węglowych) zauważono obecność ferrytu Widmanstättena. Obserwacja mikrofotografii próbek staliw odpornych na ścieranie pozwoliła stwierdzić, iż posiadają one znaczenie bardziej drobną strukturę, niż badane staliwa niestopowe (węglowe).Co więcej, zestawiono również skład chemiczny założony w normach przedmiotowych dla danych gatunków staliw z rzeczywistym składem chemicznym badanych próbek. Przedstawiono wyniki pomiarów twardości badanych gatunków staliw. W pracy wykazano bezpośredni związek pomiędzy mikrostrukturą badanych staliw, a ich twardością.
EN
A theme of the paper emphasizes the importance of cast steel. It also presents the major sectors in which cast steel products are used. Main advantages and disadvantages of cast steel were described in the paper. It also presents a general iron alloys classification including a cast steel classification. The paper characterizes the technologies of cast steel generation. The most common defects of cast steel products were also indicated. The impact of chemical composition on cast steel microstructure and properties was discussed. What is more, the paper shortly describes the division of cast steel groups which include tool steel, non-alloy (carbon) cast steel, heat resistant steel, creep-resisting steel, wear resistant and nonweathering steel. Each of them has been characterized in terms of its application, chemical analysis and properties. The theoretical part of the paper focuses mainly on non-alloy (carbon) cast steel and wear resistant steel, whereas the research concerns the microstructural characteristic of particular types of non-alloy (carbon) cast steel. The specimens of non-alloy (carbon) cast steel, such as GS52, 270-480W, and wear resistant cast steel, such as L45G and L35GSM were analyzed. The analysis showed great differences between groups of non-alloy (carbon) cast steel and wear resistant cast steel. The structure of analyzed non-alloy (carbon) cast steel indicated the presence of Widmanstätten ferrite. An observation of the specimens of wear resistant cast steel proved that they have significantly finer structure than non-alloy (carbon) cast steel. Moreover, the chemical analysis assumed for particular types of cast steel was collated with the actual chemical analysis of specimens. The paper presents the results of hardness testing of different types of cast steel and collates them with the standard values for particular steel types. It also portrays a direct relationship between the microstructure and hardness of analyzed types of cast.
13
Content available remote Wykorzystanie różnych form opadów i osadów atmosferycznych do oceny zanieczyszczenia środowiska w różnych regionach geograficznych Polski. Cz. 3, Szron i sadź
Sobik M., Polkowska Ż., Błaś M., Klimaszewska K., Walna B., Namieśnik J.
Ecological Chemistry and Engineering. S
|
2009
|
Vol. 16, nr 1
81-105
PL
Przedstawiono badania dotyczące oznaczenia stężeń wybranych związków nieorganicznych i organicznych w próbkach szronu i sadzi. Próbki pobierano w dziewięciu punktach na terenie całej Polski. Miejsca pobierania próbek podzielono ze względu na ich różny charakter: teren wiejski, teren miejski w głębi lądu oraz wybrzeże o charakterze miejskim (szron); szczyt górski, kotlina górska oraz wybrzeże o charakterze miejskim (sadź). Oznaczano stężenia następujących analitów: anionów (Cl-, F-, Br-, NO2,NO3-, SO4(2-)- i PO4(3-), kationów (K+, Na+, NH4+ Mg2+ i Ca2+), formaldehydu, sumy fenoli. Wykonano również pomiar pH i przewodności elektrolitycznej. Wyniki przeprowadzonych analiz mogą być źródłem' informacji o stanie środowiska na terenie aglomeracji miejskich (tereny silnie zurbanizowane) i wiejskich. Przeprowadzone analizy pokazały różne poziomy stężeń oznaczanych analitów w zależności od miejsca pobierania próbek, a także panujących, w okresie pobierania próbek, warunków meteorologicznych.
EN
Abstract: Research of hoarfrost and rime samples was made in order to determine the concentration level of selected organic and inorganic compounds. The samples were collected at nine sampling points in Poland. The sampling sites were divided according to the type of land topography: rural, inland urban and coastal urban areas (hoarfrost); mountain top, mountain concave and coastal urban areas (rime). The concentration levels of the following analytes were determined: cations (NH4+ , Ca2+, K+, Mg2+, Na+), anions (Cl-, F-, Br-, NO2, NO3-, SO4(3-), PO4(3-), formaldehyde and sum of phenols. The sampies were also analyzed for pH and conductivity. The obtained results can be a source of information about the state of environment in urban agglomerations (highly urbanized regions) and rural areas. The conducted analyses confirmed the relationships between concentration levels of the determined compounds and such factors, as: land topography (sampling site) and meteorological conditions prevailing during the sampling period.
14
Content available remote Wykorzystanie różnych form opadów i osadów atmosferycznych do oceny zanieczyszczenia środowiska w różnych regionach geograficznych polski - część II - Rosa
Polkowska Ż., Błaś M., Sobik M., Klimaszewska K., Małek S., Namieśnik J.
Ecological Chemistry and Engineering. S
|
2008
|
Vol. 15, nr 4
529-560
PL
Przeprowadzono analizy 235 próbek rosy i 65 próbek deszczu zebranych na 8 stacjach na terenie Polski w okresie od sierpnia 2004 do listopada 2006 roku. W zależności od położenia oraz charakteru 'la emisji zanieczyszczeń stacje pogrupowano na: rolnicze (Wrocław, Dziemiany); miejskie w strefie wybrzeża (Gdańsk, Gdynia, Sopot) i miejskie, położone poza strefą wybrzeża (Bytów, Kraków, Mława). Próbki opadu i osadu atmosferycznego badano w celu uzyskania informacji o składzie jakościowym i ilościowym. Oznaczono stężenia następujących analitów: kationów ( NH4+, Ca2+, K+, Mg2+ i Na+), anionów (CI-, F, NO2-, NO3-, SO4 3- i PO3-4), formaldehydów i całkowitej zawartości fenoli. Wykonano również pomiar przewodności i odczynu pH. Uzyskane wyniki pozwoliły zarówno na porównanie chemizmu osadów i opadów atmosferycznych, jak również na określenie ładunków zanieczyszczeń wprowadzanych do środowiska. Przeprowadzone analizy potwierdziły wyższy stopień zanieczyszczenia rosy niż opadu atmosferycznego. Przeprowadzone badania potwierdziły zależność stężeń poszczególnych analitów od lokalizacji i ukształtowania terenu, na którym zostały zebrane próbki opadów i osadów atmosferycznych, a także od warunków meteorologicznych.
EN
The analyses of 235 dew and 65 atmospheric precipitation samples collected from eight measurement stations in Poland from August 2004 to November 2006 were made. Taking into account the type of land use and characteristics of pollutant emissions, the sampling sites were divided into three groups: rural stations (located in agricultural areas: Wrocław, Dziemiany); coastal urban stations (close to the coastline: Gdansk, Gdynia, Sopot) and inland urban stations (the chemical composition of precipitation in a town, with increasing traffic intensity and industry: Bytów, Mława, Kraków). The samples of atmospheric precipitation and deposits were analyzed in order to obtain information regarding qualitative and quantitative composition. The concentration levels of the following analytes were determined: cations ( NH4+, Ca2+, K+, Mg2+, Na+), anions (Cl-, F-, NO2-, NO3-, SO2-4, PO3-4), formaldehyde and sum of phenols. The samples were also analyzed for pH and conductivity. The obtained results allowed both to compare the chemical composition of atmospheric precipitation and deposits and evaluate the load of pollutants entering the environment. The conducted research confirmed the higher pollution level of dew, when compared with atmospheric precipitation, and the relationship between concentration levels of selected analytes and such factors, as: location, land topography, from which the samples of atmospheric precipitation and deposits were collected and meteorological conditions.
15
Content available remote Wykorzystanie różnych form opadów i osadów atmosferycznych do oceny zanieczyszczenia środowiska w różnych regionach geograficznych Polski - Część I - Mgła
Błaś M., Polkowska Ż., Sobik M., Klimaszewska K., Nowiński K., Namieśnik J.
Chemistry-Didactics-Ecology-Metrology
|
2008
|
R. 13, NR 1-2
81--93
PL
Wykonano badania zebranych próbek opadu zawieszonego (mgła) w celu oznaczenia w nich poziomu zawartości wybranych związków organicznych i nieorganicznych. Próbki pobierano w dwóch punktach na terenie Polski. Miejsca pobierania próbek podzielono ze względu na ich różny charakter: teren nizinny i szczyt górski. Stwierdzono obecność wybranych zanieczyszczeń na różnych poziomach stężeń w próbkach mgły oraz że poziom ten zależy od lokalizacji, ukształtowania terenu i warunków meteorologicznych, jakie panowały w okresie pobierania próbek.
EN
Research on suspended precipitation (fog) samples was made in order to determine the concentration level of selected organic and inorganic compounds. The samples were collected at two sampling points in Poland. The sampling sites were divided according to the type of land topography: lowland area and mountain summit. On the basis of the conducted research it was concluded that the selected pollutants were determined on different concentration levels in fog samples and this level depends on location, land topography and meteorological conditions prevailing during the sampling period.
first rewind previous Strona / 1 next fast forward last
JavaScript jest wyłączony w Twojej przeglądarce internetowej. Włącz go, a następnie odśwież stronę, aby móc w pełni z niej korzystać.