Possibilities of limiting formaldehyde content in particleboards to a level characteristic of natural wood

Frąckowiak I., Warcok F., Bendowska R., Idziak A.

Drewno : prace naukowe, doniesienia, komunikaty

2014

vol. 57, nr 191

71--85

The article presents the results of research on the influence of selected technological parameters, changed within a range similar to values presently used in industry, on the properties of three-layer particleboards produced from pine particles obtained from sawmill waste. The particles were glued with amine resins. The panels, produced using urea-formaldehyde resin modified with melamine, were characterised by the lowest content of formaldehyde, i.e. below 2 mg/100 g of ovendry board, after conversion into a value corresponding to the moisture content of the panels equalling 6.5%. The emissions of formaldehyde determined by the chamber and gas analysis methods were much lower than the threshold values recommended in international regulations and used as a basis for the classification of particleboards.

W artykule przedstawiono wyniki badań wpływu wybranych parametrów technologicznych, zmienianych w przedziale zbliżonym do wartości aktualnie stosowanych w przemyśle, na właściwości trzywarstwowych płyt wiórowych wytwarzanych z wiórów sosnowych pozyskanych z odpadów tartacznych. Do zaklejania wiórów stosowano żywice aminowe. Najmniejszą zawartością formaldehydu, poniżej 2 mg/100g zupełnie suchej płyty, po przeliczeniu na wartość odpowiadającą wilgotności płyt – 6,5%, charakteryzowały się płyty wytworzone z żywicą mocznikowo-formaldehydową modyfikowaną melaminą. Emisja formaldehydu badana metoda komorową i analizy gazowej była znacznie mniejsza od wartości granicznych, obowiązujących i proponowanych w przepisach międzynarodowych, jako podstawa klasyfikacji płyt wiórowych.

The influence of UF molar ratio on selected particleboard properties

Frąckowiak I., Warcok F., Fuczek D., Andrzejak C.

Drewno : prace naukowe, doniesienia, komunikaty

2011

vol. 54, nr 186

39-49

This paper presents the preliminary research results of a project whose main objective is to quantify the impact of formulations and technological parameters on formaldehyde content in and emission from particleboards produced using urea-formaldehyde resin with a low molar ratio of F/U. The formaldehyde content reduction is possible by using a resin with a molar ratio of F/U of 1.065 hardened with 3% solution of urea and ammonium nitrate or a resin with a molar ratio of F/U of 0.96 to which 3% urea was added. For these variants, reductions by 22% and 21% respectively of formaldehyde content in particleboards were obtained, while at the same time, strength properties that meet the requirements of the EN-312: 2011 standard for P2 particleboards were maintained.

Przedstawiono wyniki badań pierwszego etapu projektu, którego głównym założeniem jest próba kwantyfikacji wpływu receptur i parametrów technologicznych na zawartość i emisję formaldehydu z płyt wiórowych wytwarzanych z zastosowaniem żywicy mocznikowo- formaldehydowej o niskim stosunku molowym F/U. Spośród przeprowadzonych badań wybrano dwa optymalne warianty. Pierwszy dotyczy żywicy o stosunku molowym F/U 1,065 utwardzanej roztworem saletrzano-mocznikowym w ilości 3%, drugi żywicy o stosunku molowym F/U 0,96 utwardzanej azotanem amonu dodanego w ilości 2% w stosunku do suchej masy kleju, do której dodano 3% mocznika. W obydwu wariantach uzyskano obniżenie zawartości formaldehydu w płycie odpowiednio o 22% oraz 21% przy jednoczesnym zachowaniu właściwości wytrzymałościowych spełniających wymagania normy EN-312: 2011 dla płyt wiórowych klasy P2.