Mechanical properties of aluminium/copper bimetallic sheets subjected to cyclic bending

Żaba Krzysztof, Puchlerska Sandra, Rusz Stanislav, Fejkiel Romuald

Advances in Mechanical and Materials Engineering

2023

Vol. 40, nr 1

47--54

The aim of this study is to evaluate the influence of the roll bonding (RB) process on the mechanical properties of Al/Cu bimetallic strip specimens. A specially designed test instrument for the cyclic bending test of strip specimens produced by RB has been proposed. The test consists in repeated pulling of a strip of sheet metal through a system of cylindrical countersamples. Samples cut along and across the sheet rolling direction were tested. The specimens were subjected to preliminary microstructural tests using an optical microscope with Nomarski contrast and scanning electron microscopy. The tests showed a slight influence of the orientation of the samples on the change of the mechanical properties of the bimetallic sheets in the cyclic bending process. In the case of samples oriented along the sheet rolling direction, discontinuities in the transition layer were found. The samples oriented perpendicularly to the rolling direction were free of this defect.

Celem artykułu jest ocena wpływu procesu walcowania na właściwości mechaniczne próbek w postaci pasów blachy bimetalowej Al/Cu. Zaproponowano specjalnie zaprojektowany przyrząd do cyklicznego gięcia próbek wytwarzanych metodą walcowania. Test polega na wielokrotnym przeciąganiu paska blachy przez układ cylindrycznych przeciwpróbek. Badaniom poddano próbki cięte wzdłuż i w poprzek kierunku walcowania blachy. Próbki poddano wstępnym badaniom mikrostrukturalnym przy użyciu mikroskopu optycznego z kontrastem Nomarskiego oraz skaningowego mikroskopu elektronowego. Badania wykazały niewielki wpływ orientacji próbek na zmianę właściwości mechanicznych blach bimetalicznych w procesie cyklicznego zginania. W przypadku próbek zorientowanych wzdłuż kierunku walcowania blachy stwierdzono nieciągłości w warstwie przejściowej. Próbki zorientowane prostopadle do kierunku walcowania były wolne od tej wady.

Analysis of tribological performance of new stamping die composite inserts using strip drawing test

Żaba Krzysztof, Kuczek Łukasz, Puchlerska Sandra, Wiewióra Marcel, Góral Marek, Trzepieciński Tomasz

Advances in Mechanical and Materials Engineering

2023

Vol. 40, nr 1

55--62

This article assesses the tribological performance of new composite tool sets for stamping dies. Four sets of composite countersamples were tested. These consisted of polyurethane resin with mineral filler (base variant) and modified with aluminium powder (10wt%) and roving fabric (5wt%). Strip samples for the strip drawing tests were cut from AMS5599 (Inconel 625) corrosion-resistant nickel alloy, AMS5510 (321) corrosion and heat-resistant steel and AMS6061-T4 heat treatable aluminium alloy sheet metals. The influence of the type of sample material on the coefficient of friction (COF) was observed. The smallest values of the COF over the entire range of clamping force values used on AMS5599 and AMS5510 sheets were observed during tests with countersamples made of the base variant of composite. When testing the AMS6061-T4 aluminium alloy sheet, the countersamples modified with roving fabric provided the lowest value of COF, which stabilised at a value of about 0.197 as pressure was increased.

Celem artykułu jest ocena właściwości tribologicznych nowych kompozytowych wkładek do tłoczników. Badaniom poddano cztery zestawy przeciwpróbek kompozytowych składających się z żywicy poliuretanowej z wypełniaczem mineralnym (wariant bazowy) oraz modyfikowanych proszkiem aluminiowym (10% mas.) i tkaniną rowingową (5% mas.). Próbki do testu przeciągania pasa blachy wycięto z blach AMS5599, AMS5510 i AMS6061-T4. Zaobserwowano wpływ rodzaju materiału przeciwpróbki na współczynnik tarcia. Najmniejsze wartości współczynnika tarcia w całym zakresie zmian siły docisku dla blach AMS5599 i AMS5510 zaobserwowano podczas badań z przeciwpróbkami wykonanymi z bazowego wariantu kompozytu. Podczas badania blachy ze stopu aluminium AMS6061-T4 przeciwpróbki modyfikowane tkaniną rowingową zapewniły najmniejszą wartość współczynnika tarcia, która w zakresie ustabilizowanym osiągnęła wartość około 0,197.