Effect of Particle Size of a Powder upon the Properties and Microstructure of Boron-modified Fe-Ni-Mo-Cu Sinters

Karwan-Baczewska Joanna, Perek-Nowak Małgorzata, Majchrowska Magdalena, Rosso Mario

Journal of Casting & Materials Engineering

|

2023

|

Vol. 7, no. 1

1--8

EN

The article discusses the effect of different particle fractions of prealloyed iron powder on the microstructure, density and hardness of sintered material. Each particle fraction (apart from 160–200 µm, which is a trace fraction) was modified with boron, its contents being, respectively, 0.2 wt.%, 0.4 wt.% and 0.6 wt.%. Next, the powder mixtures were pressed under a pressure of 600 MPa, and the final compacts were subject to sintering at 1200°C for 60 min in a hydrogen atmosphere. It was observed that the higher values of density and hardness were found in samples made from finer fractions of powder. A higher homogeneity of the microstructure and the highest degree of compactness was obtained in sinters from powder of 40–56 µm particle size, with 0.4 wt.% boron. Due to the use of small particle fractions of prealloyed powder, a higher degree of compactness in sinters was obtained with lower boron content. Also indicated was which particle fraction of Fe-Ni-Mo-Cu powder should be applied to obtain density in sinters with boron addition equal to almost 100% of the relative density of the analyzed alloy. The presented studies have both scientific and technological aspects.

2

Efekt mechanicznej syntezy na mikrostrukturę kompozytów na osnowie miedzi umacnianych cząstkami azotku tytanu. Wytwarzanie i właściwości Cu-5% wag. TiN

Franczak Aleksandra, Karwan-Baczewska Joanna

Hutnik, Wiadomości Hutnicze

|

2021

|

Vol. 88, nr 2

2--7

PL

W artykule przedstawiono sposób wytworzenia kompozytów na osnowie miedzi umacnianych dodatkiem 5% wag. azotku tytanu. W tym celu zastosowano proces mechanicznej syntezy (MA) i iskrowego spiekania plazmowego (SPS). Zaobserwowano, że 10-cio godzinny proces mechanicznej syntezy doprowadził do utworzenia się struktury płatkowej mieszanki kompozytowej Cu-TiN. Cząstki azotku tytanu znajdują się wewnątrz plastycznej osnowy, jednakże ich rozmieszczenie nie jest w pełni równomierne. Artykuł przedstawia mikrostrukturę mieszanki kompozytowej uzyskanej zarówno podczas mechanicznej syntezy jak i po jej zakończeniu, a także mikrostrukturę uzyskanych spieków po procesie iskrowego spiekania plazmowego. Zamieszczono wyniki dotyczące gęstości, twardości i przewodności elektrycznej kompozytów.

EN

In the presented work, Cu matrix composites reinforced with 5% wt. of TiN were prepared by mechanical alloying (MA) and spark plasma sintering (SPS) method. During experiments it was observed that 10 hours of MA lead to a flake-like particle morphology. Titanium nitride particles are located inside copper matrix but their distribution is not completely homogeneous. This article shows microstructure of the powders during and after MA as well as SPS method. Density, hardness and electrical conductivity of the composites are also presented.

3

Kompozyty na osnowie miedzi - analiza literaturowa

Franczak Aleksandra, Karwan-Baczewska Joanna

Rudy i Metale Nieżelazne Recykling

|

2019

|

R. 64, nr 4

21--25

PL

W artykule przedstawione zostały wybrane metody wytwarzania kompozytów metalowych na osnowie miedzi. Artykuł ma charakter poglądowy, w którym w zależności od fazy umacniającej wybrano stosowną metodę wytwarzania. Analiza literaturowa dotyczy artykułów z ostatnich lat badań.

EN

This paper presents methods for the production of metal composites on a copper matrix. The article is of an illustrative nature, in which an appropriate method of production was selected depending on the strengthening phase. The review focuses on articles from recent years of research.

4

Wybrane właściwości kompozytów o osnowie Al pochodzącego z odzysku materiałowego

Pietrzak Krystyna, Karwan-Baczewska Joanna, Makuch Anna, Majchrowska Magdalena, Franczak Aleksandra, Klasik Adam

Inżynieria Powierzchni

|

2019

|

nr 2

22--33

PL

Do wytworzenia kompozytów metodą SPS wykorzystano aluminium pochodzące z odzysku materiałowego po obróbce skrawaniem. Dzięki metodzie SPS możliwe było uzyskanie praktycznie bezporowatych spieków. Wytworzono trzy typy kompozytów Al + SiC oraz hybrydowe Al + (WC + 12Co) i A[SiC + (WC + 12 Co)] określono ich gęstość, odporność na zużycie przez tarcie oraz parametry topograficzne powierzchni przed i po testach tribologicznych. W oparciu o uzyskane wyniki badań wykazano, że kompozyty hybrydowe wykazują lepsze charakterystyki tribologiczne w porównaniu do kompozytów umacnianych tylko cząstkami SiC. Wykazano również, że współczynnik tarcia zależy głównie od różnicy twardości występującej pomiędzy trzpieniem i tarczą. Większa różnica powoduje, że współczynnik tarcia przyjmuje większe wartości.

EN

Recyclable aluminum after machining was used to make composites using the SPS method. Due to the SPS method, it was possible to obtain the sinters practically without pores. Three types of composites Al + SiC and hybrid composites such as Al + (WC + 12Co) and Al + [SiC + (WC + 12 Co)] were produced. Their density, resistance to friction wear and surface topographic parameters have been determined. Based on the results, it has been shown that in the case of hybrid sinters, better tribological characteristics compared to composites reinforced with SIC particles only can be obtained. It was also shown that the friction coefficient primarily depends on the difference between the hardness of the pin and the disc. The greater difference in hardness causes the values of the friction coefficient to be higher.