In this paper, the Rubiaceae Chinese Fevervine stem was used as raw material, with pool dipping, manual decorticating, acid dipping and sodium hydroxide scouring twice as the degumming method, to produce Chinese Fevervine Fibre (CF fibre). Through an orthogonal experiment, optimised two-fold sodium hydroxide degumming using refining technology was achieved: in the first alkali degumming, the NaOH concentration was 1.4% at a temperaturę of 95 °C for 3.5 hours; in the second , the NaOH concentration was 0.8% at a temperature of 95 °C for 2.5 hours; and in the acid dipping, the sulfuric acid concentration was 6% at room temperature for 0.5 hours. The CF fibre produced has a spinnability of 39.90 mm length, a linear density of 2.82 dtex, a tenacity of 18.56 cN/dtex, and a break elongation of 2.81%.
PL
W pracy omówiono proces wytwarzania chińskiego włókna Fevervine (włókno CF). Poprzez eksperyment ortogonalny uzyskano zoptymalizowane dwukrotne odklejanie wodorotlenkiem sodu przy użyciu technologii rafinacji: w pierwszym odklejaniu alkalicznym stężenie NaOH wynosiło 1.4% w temperaturze 95 °C przez 3.5 godziny; w drugim stężenie NaOH wynosiło 0.8% w temperaturze 95 °C przez 2.5 godziny; a podczas zanurzania w kwasie stężenie kwasu siarkowego wynosiło 6% w temperaturze pokojowej przez 0.5 godziny. Wytworzone włókno CF miało zdolność przędzenia i długości 39.90 mm, gęstość liniową 2.82 dtex, wytrzymałość na rozciąganie 18.56 cN/dtex oraz wydłużenie przy zerwaniu 2.81%.
first rewind previous Strona / 1 next fast forward last
JavaScript jest wyłączony w Twojej przeglądarce internetowej. Włącz go, a następnie odśwież stronę, aby móc w pełni z niej korzystać.