Content available The Influence of Layer Height on the Tensile Strength of Specimens Printed in the FDM Technology
Miazio Łukasz
Technical Sciences / University of Warmia and Mazury in Olsztyn
|
2021
|
nr 24(1)
51--56
EN
This article analyzes the influence of layer height on the tensile strength of PLA specimens printed in the Fused Deposition Modeling (FDM) technology. The maximum breaking force of specimens with 30% and 100% infill density was determined at layer height of 0.05 mm, 0.1 mm, 0.2 mm and 0.3 mm. In the case of 30% infill, the highest value of the force was obtained for a layer with a height of 0.05 mm (which corresponds to 22.7 MPa), and for a 100% infill for a layer of 0.2 (which corresponds to 40 MPa). Over this layer height of 0.2 mm is the most poly-optimal due to the time prints and strength (which corresponds to 19.7 MPa).
2
Wpływ obniżonej temperatury na wytrzymałość aluminium serii 5xxx
Dudda Waldemar, Miazio Łukasz
Hutnik, Wiadomości Hutnicze
|
2021
|
Vol. 88, nr 5-6
6--7
PL
W artykule przedstawiono badania nad wpływem niskiej temperatury na wytrzymałość aluminium 5754 i 5083. Wykonano próbę rozciągania statycznego w temperaturze pokojowej oraz ujemnej -20°C. Na podstawie przeprowadzonych prób rozciągania badanych stopów aluminium zaobserwowano niewielki wzrost właściwości wytrzymałościowych, tj. granicy plastyczności oraz wytrzymałości na rozciąganie.
EN
Research on low temperature contribution on the strength of 5754 and 5083 aluminum are presented in this article. Static tensile tests were carried out at room and negative temperature of -20°C. A slight increase in strength properties, i.e. the yield strength and the tensile strength of studied aluminum alloys, was observed on the basis of conducted tensile tests.
3
Wpływ obniżonej temperatury na wytrzymałość aluminium serii 5xxx
Dudda Waldemar, Miazio Łukasz
Przegląd Mechaniczny
|
2019
|
nr 7-8
36--38
PL
W artykule przedstawiono badania nad wpływem niskiej temperatury na wytrzymałość aluminium 5754 i 5083. Wykonano próbę rozciągania statycznego w temperaturze pokojowej oraz ujemnej -20°C. Na podstawie przeprowadzonych prób rozciągania badanych stopów aluminium zaobserwowano niewielki wzrost właściwości wytrzymałościowych, tj. granicy plastyczności oraz wytrzymałości na rozciąganie.
EN
Research on low temperature contribution on the strength of 5754 and 5083 aluminum are presented in this article. Static tensile tests were carried out at room and negative temperature of -20°C. A slight increase in strength properties, i.e. the yield strength and the tensile strength of studied aluminum alloys, was observed on the basis of conducted tensile tests.
4
Content available Impact of print speed on strength of samples printed in FDM technology
Miazio Łukasz
Agricultural Engineering
|
2019
|
Vol. 23, No. 2
33--38
EN
This paper presents research on the impact of printing speed on the strength of a manufactured object and is the next stage of the author's research on the impact of technological parameters of 3D printing on the strength of printed models. The tested universal specimens were printed using the FDM (Fused Deposition Modeling) method from PLA (polylactic acid, polylactide). The paper presents the maximum breaking force of the samples and the time of printing samples depending on the printing speed, which varied from 20 mm·s -1 to 100 mm·s -1. The research indicates that the strength of samples decreases with increasing speed. In the range of 50-80 mm·s -1, the strength of the specimens remined at a similar level, however, above 80 mm·s -1, it decreased significantly.
PL
W niniejszym artykule przedstawiono badania nad wpływem prędkości drukowania na wytrzymałość wytwarzanego obiektu. Badane kształtki uniwersalne wydrukowano metodą FDM (Fused Deposition Modeling) z tworzywa PLA (ang. polylactic acid, polylactide). Artykuł jest kolejnym etapem badan autora nad wpływem parametrów technologicznych druku 3D na wytrzymałość wydrukowanych modeli. W artykule przedstawiono maksymalne silę zrywającą próbki oraz czas wydruku próbek w zależności od prędkości drukowania. Prędkość drukowania zmieniano od 20 mm·s -1 do 100 mm·s -1 . Z przedstawionych badań wynika, że wraz ze wzrostem prędkości maleje wytrzymałość próbek. W zakresie 50-80 mm·s -1 wytrzymałość kształtek była na porównywalnym poziomie. Natomiast powyżej prędkości 80 mm·s -1 wytrzymałość już znacząco spada.