In vitro tests of dense hydroxyapatite materials

Sobczak A., Kida A., Kowalski Z., Wzorek Z.

Polish Journal of Chemical Technology

2009

Vol. 11, nr 1

44-49

The paper presents the results of the calcining process of deproteinised and defatted bone pulp called bone sludge. The calcining process was performed in two stages. The first step of the calcining process was realized at the temperature of 600°C in a rotary kiln. In the second stage the obtained bone ashes were calcined at five different temperatures from 650°C to 950°C for 2 hours in a chamber kiln and in air atmosphere. The products of the calcining process were characterized by the XRD method. Calcium content was determined by titration whereas the contents of total phosphorus and acid-soluble phosphorus - by the spectrophotometric method. The X-ray analysis confirmed that hydroxyapatite is the main component of the calcining products. Calcium and phosphorus contents were kept at the level of 40% and 17.5%, respectively, which corresponded to the Ca/P ratio of not stechiometric hydroxyapatite. In vitro studies, in the simulated body fluid, Ringer liquid and distilled water were realised. The measurements of pH value of SBF and Ringer fluid were realized. Additionally electrical conductivity as well as pH for distilled water where conducted. The goal of these tests was to evaluate chemical durability of dense hydroxyapatite materials.

Evaluation of the biomedical properties of hydroxyapatite obtained from bone waste

Sobczak A., Kida A., Kowalski Z., Wzorek Z.

Polish Journal of Chemical Technology

2009

Vol. 11, nr 1

37-43

The method of obtaining hydroxyapatite by thermal treatment of deproteinised and defatted bone pulp called bone sludge was presented. The products of the calcining process were characterized with X-ray diffraction (XRD) and Fourier transformed infrared spectroscopy (FT-IR). The calcium content was determined with titration, whereas the contents of total phosphorus - with a spectrophotomertric method. X-ray investigations confirmed that hydroxyapatite was the main component of the calcining products in the calcining process. The FT-IR spectra confirmed that all organic substances were removed during the calcining process. On the basis of the research into physiological liquids the propensity to resorption of hydroxyapatite bioceramic was evaluated.