Due to urbanization, the population in the major cities in Malaysia is approximately 72.8% of its total population. The increase of population density has directly increased the amount of sewerage sludge waste that poses threat to the environment. In line with the green initiatives, alternative method to develop good quality concrete material from sewerage sludge waste can be further explored. Traditionally, sewerage sludge waste is processed using incinerator that require high energy and it is time consuming. In this study, microwave heating which require less energy consumption and less time consuming is used for sewerage sludge preparation. Prior to heating process, sewerage sludge waste is over dried at 105°C for 24 hours. Three types of microwave heating namely medium heating, medium high heating and high heating has been used. The chemical and physical properties microwaved sewerage sludge ash (MSSA) was tested using X-Ray Fluorescence (XRF), X-Ray Diffraction (XRD) and Scanning Electron Microscopy (SEM). Based on the result, the recommended temperature for the MSSA production for the concrete is High Mode Temperature. This is due to the result of MSSA for X-Ray Fluorescent test as its shows the highest in the content for pozzolanic element which are SiO2 and Fe2O3 that produce after the microwave burning process. The mineralogical composition and the crystalline phase of the High temperature MSSA due to X-Ray Diffraction test also shows high content of SiO2 as the major component as it is good for pozzolanic reaction in concrete. From the Scanning Electron Microscope test, it is observed that particle of High heated MSSA are slightly smaller than other temperature. Also, the densification occurs at High temperature MSSA. Hence, the optimal burning temperature mode for MSSA is High Mode temperature.
With the rapid development of industry, abundant industrial waste has resulted in escalating environmental issue. Steel slag is the by-product of steel-making and can be used as cementitious materials in construction. However, the low activity of steel slag limits its utilization. Much investigation has been conducted on steel slag, while only a fraction of the investigation focuses on the effect of steel slag particle size on the properties of mortar. The aim of this study is to investigate the effect of steel slag particle size as cement replacement on properties of steel slag mortar activated by sodium sulphate (Na2SO4). In this study, two types of steel slag, classified as fine steel slag (FSS) with particle sizes of 0.075 mm and coarse steel slag (CSS) with particle sizes of 0.150 mm, were used for making alkali activated steel slag (AASS) mortar. Flow table test, compressive strength test, flexural strength test and UPV test were carried out by designing and producing AASS mortar cubes of (50x50x50) mm at 0,10%, 20% and 30% replacement ratio and at 0.85% addition of Na2SO4. The results show that the AASS mortar with FSS possess a relatively good strength in AASS mortar. AASS mortar with FSS which is relatively finer shows a higher compressive strength than CSS up to 38.0% with replacement ratio from 10% to 30%. This study provided the further investigation on the combined influence of replacement ratio and particle size of SS in the properties of fresh and hardened AASS.
JavaScript jest wyłączony w Twojej przeglądarce internetowej. Włącz go, a następnie odśwież stronę, aby móc w pełni z niej korzystać.