The purpose of this study was to determine how global effort affects the rhythm of multi-joint coordination in the global task. We wanted to examine how this specific kind of fatigue impacts sense of rhythm. Methods: In this study, fourteen non-professsional runners performed two effort trials of different intensity, where speed was set individually according to the speed of running when participants reached lactate threshold. Before and after each effort trial they had to perform the rhythm test. Results: Two-way analysis of variance ANOVA did not reveal significant differences among the variables of pre- and post-effort rhythm test. It is suggested that these results are supported by the application of different movement strategies to compensate for fatigue, and possible motor learning effect of simple timing performance. Conclusions: In our opinion the training workout routine should include cyclic technical exercises after fatigue. Not only to develop and improve energetics of movement, but also to learn and perfect different movement patterns and develop novel movement strategies.
The pearlite spheroidization in Fe-0.76%C high purity steel was investigated. The samples of a coarse pearlite microstructure were isothermal annealed at 700, 680, 660, 640 and 620°C for various times, up to 800 hours. For quantitative description of the spheroidization process stereological parameter, SV (ferrite/cementite interface surface density) was used. The activation energy 104.8±11.4 kJ/mol was found for the spheroidization process. This value shows good agreement with the activation energy for iron and carbon diffusion along a ferrite/cementite interface, so the coupled interface diffusion is the rule-controlling process.
3
Dostęp do pełnego tekstu na zewnętrznej witrynie WWW
The objective of this study was to evaluate the reliability and validity of two alternative systems used for jumping performance measurement. Methods: Two groups of subjects were tested. The first group consisted of 15 male adults (21.3 ± 1.7 years ) and the second group consisted of 16 female volleyball players (17.2 ± 0.9 years). We used three different systems of data collection in the study. Two of the used systems are based on optoelectric components. The Optojump Next system is referred to as the optoelectric system, and BTS Smart-E is refered to as the video system. Concurrent validity of these systems was verified with the use of “gold standard” which is force platform. All systems were used to estimate the height of vertical jumps. Results: Both optoelectric systems occurred to be highly reliable with the ICCs=0.98 for Optojump and 0.9 for BTS Smart. Their concurrent validity with the force platform data was also very high r=0.99 and r=0.97 respectively. Conclusions: Comparison of these two systems shows distinct differences between them where Optojump system is more suitable for quick and reliable sports testing, when BTS-Smart for research and clinical testing.
Problems related with abrasive wear of tangential-rotary picks during cutting process and its limitations, have been discussed in the present study. Essential for the parameters of cutting process geometrical, kinematic and material parameters of tangential-rotary picks and types of their wear, have been discussed. Testing procedure in aspect of the wear of tangential-rotary picks and their durability estimation, has been described. Manners of the abrasion of pick body and pick edge of the tangential-rotary picks, have been determined. Particular attention was paid to procedure of hard facing of the pick operational part and its influence onto mining process. Results of examination of tangential-rotary picks with hard facing layer on operational part near insert made of abrasion sintered carbide are also cited.
PL
W artykule przedstawiono problemy związane z zużyciem ściernym noży styczno-obrotowych podczas procesu frezowania oraz sposoby jego ograniczenia. Omówiono istotne ze względu na proces skrawania parametry geometryczne, kinematyczne i materiałowe noży styczno-obrotowych oraz rodzaje ich zużycia. Przedstawiona została metoda prowadzenia badań noży w aspekcie szybkości ich zużycia oraz oceny ich trwałości. Przedstawiono sposoby zwiększania odporności na ścieranie korpusów jak i ostrzy noży styczno-obrotowych. Głównie skupiono się na metodzie związanej z napawaniem części roboczej noża oraz jej wpływem na proces urabiania. Przedstawione zostały również wyniki badań noży styczno-obrotowych z wykonaną na części roboczej napoiną w pobliżu wkładki z węglika spiekanego materiałem odpornym na ścieranie.
The quality of rail steel is conditioned by its high mechanic qualities, which greatly depend on the presence of undesired nonmetallic inclusions. The paper is devoted to the segregation of components, mainly sulphur, and the formation of manganese sulphide in the process of steel solidification, at the casting rate of 100 and 500 K/min. Sulphur is a steel component which disadvantageously influences its numerous parameters. The oxide-sulphide and sulphide precipitations cause cracks and lower the strength of the material. This phenomenon was modeled with the use of author’s computer program based on Matsumiya interdendritic microsegregation model. The main assumptions of this model and thermodynamic conditions of inclusion formation during casting of steel are discussed in this paper. Two cases were analyzed: in the first one the MnS was assumed to form a pure and constant compound, whereas in the other one the manganese sulfide was precipitated as a component of a liquid oxide solution, and its activity was lower than unity. The final conclusion is that chemical composition of steel is the major parameter deciding about the formation of MnS inclusions.
A lamellar microstructure is, beside a granular and dispersive one, the most frequently observed microstructure in the case of metal alloys. The most well-known lamellar microstructure is pearlite, a product of a eutectoidal transformation in the Fe-Fe3C system. The lamellar morphology of pearlite - cementite and ferrite lamellae placed interchangeably within one structural unit described as a colony - is dominant. The durability of the lamellar morphology is much diversified: in the microstructure of spheroidizingly annealed samples, one can observe areas in which the cementite is thoroughly spheroidized, next to very well-preserved cementite lamellae or even whole colonies of lamellar pearlite. The mentioned situation is observed even after long annealing times. The causes of such behaviour can vary. The subject of the previous work of the authors was the effect of the orientation between the ferrite and the cementite on the stability of the lamellar morphology. This work constitutes a continuation of the mentioned paper and it concerns the effect of the true interlamellar spacing on the stability of the lamellar morphology of cementite.
PL
Mikrostruktura płytkowa to obok ziarnistej i dyspersyjnej jedna z najczęściej spotykanych w przypadku stopów metali. Najbardziej znaną mikrostrukturą płytkową jest perlit, produkt przemiany eutektoidalnej w układzie Fe-Fe3C. Morfologia płytkowa perlitu –płytki ferrytu i cementytu ułożone na przemian w obrębie jednej jednostki strukturalnej określanej mianem kolonii - jest dominująca. Trwałość morfologii płytkowej jest bardzo zróżnicowana - w mikrostrukturze próbek wyżarzanych sferoidyzująco obserwuje się obszary, w których cementyt jest zupełnie zesferoidyzowany obok bardzo dobrze zachowanych płytek cementytu lub wręcz całych kolonii perlitu płytkowego. Opisana sytuacja ma miejsce nawet po długich czasach wyżarzania. Przyczyny takiego zachowania mogą być różne. Przedmiotem wcześniejszej pracy autorów był wpływ orientacji pomiędzy ferrytem a cementytem na stabilność morfologii płytkowej. Niniejszy artykuł stanowi kontynuację pracy wspomnianej wcześniej i dotyczy wpływu rzeczywistej odległości międzypłytkowej na stabilność morfologii płytkowej cementytu.
7
Dostęp do pełnego tekstu na zewnętrznej witrynie WWW
Pomimo projektowania osi pojazdów szynowych w zakresie tzw. nieograniczonej wytrzymałości zmęczeniowej, wobec podwyższania prędkości pojazdów oraz występowania złożonych zjawisk eksploatacyjnych i materiałowych, rejestrowane są kolejne przypadki występowania uszkodzeń takich osi. W artykule przedstawiono wyniki badań nieniszczących 120 szt. osi pojazdów szynowych, dla których po ok. 4 latach eksploatacji, dla 8 szt. osi stwierdzono występowanie pęknięć zmęczeniowych. Badania defektoskopowe wykonane metodami ultradźwiękową i magnetyczno-proszkową pozwoliły wytypować element, z którego pobrano próbki do wykonania badań składu chemicznego materiału, pomiarów twardości, badań mikroskopowych i fraktograficznych. Analiza uzyskanych wyników badań wykazała, że przyczyną wykrytych pęknięć zmęczeniowych osi było powstanie pęknięć hartowniczych w obszarze karbu geometrycznego.
EN
Despite axis design of rail vehicles for so-called unlimited fatigue strength, towards increase of the speed of vehicles and occurrence of a number of operational and materials complex phenomena, more cases of damages to such axis are recorded. This article presents the results of non-destructive testing of 120 pcs of axis of rail vehicles, for which after about four years of operation, for eight pieces of axis fatigue cracks were found. Completed nondestructive examination, using ultrasonic and magnetic-particle methods, helped predict the element from which were taken samples for testing the material chemical composition, hardness measurements, microscopic and fractographic examination. Analysis of the tests results showed that the cause of detected fatigue cracks of axis were quenching cracks arisen in the notch geometry.
8
Dostęp do pełnego tekstu na zewnętrznej witrynie WWW
The paper presents issues concerning determination of forging and controlled cooling conditions in aspect of application of direct cooling of as-forged microalloyed steel. The study concerns realization of thermomechanical treatment directly after forging, oriented at producing desired microstructure and required final mechanical properties. In order to determine forging conditions and most favourable cycle of cooling, numerical modelling with finite element method was used. To select appropriate forging temperature, actual temperature in critical locations of the part was traced during the entire forging cycle. On assumption of predefined parameters of forging process and subsequent forced-air continuous cooling, effectiveness of forced-air acceleration was investigated from the standpoint of producing necessary cooling rate. The direct cooling regimes were verified with tensile testing and hardness measurement, illustrating qualitative analysis of obtained microstructure. Determined forging/cooling conditions served as guidelines for industrial realization of controlled processing of drop forged automotive lever oriented at fine-grained ferrite–pearlite or acicular ferrite microstructure and required level of mechanical properties.
W pracy zastosowano chemiczną metodę osadzania ZnO, zwaną "solution growth method" z użyciem roztworów octanu cynku oraz urotropiny poddając je odpowiedniej obróbce termicznej z różnymi czasami wygrzewania. Stosowano również inny wariant metody wzrostu z wykorzystaniem roztworu octanu cynku z CTAOH oraz azotanu cynku i urotropiny. Jest to metoda dwustopniowa gdzie w pierwszym etapie przeprowadza się zarodkowanie, a w drugim następuje wzrost nanostruktur ZnO. Struktury te wykorzystywane są do wytwarzania warstw gazoczułych w sensorach. Przeprowadzono również badania dyfrakcyjne i odbicia rentgenowskiego otrzymanych struktur na różnych podłożach.
EN
In research the "solution growth method" was applied for deposition of ZnO, using solutions of zinc acetate dehydrate and methenamine with adequate annealing processes. In the second option the solution was prepared from zinc acetate, cetyltrimethylammonium hydroxide (CTAOH) and zinc nitrate with methenamine. The second option is the two stage method, where in the first stage the nucleation process occurs and in the second stage the ZnO nanostructures grow. ZnO nanostructures can be utilized as sensing layers in gas sensors. The investigations of X-ray diffraction and reflection at small angles were also performed.
Dwuetapowe laboratoryjne walcowanie zmiękczonych pierścieni łożyskowych w walcarkach skośnych obejmuje: walcowanie tulei rurowych o mikrostrukturze cienkopłytkowego perlitu; kontrolowane walcowanie pierścieni, uwzględniające warunki Verhoevena dla wyżarzania sferoidyzującego stali 100Cr6. W mikrostrukturze otrzymanych pierścieni ze stali 100Cr6 dominuje drobny sferoidyt, twardość pierścieni jest mniejsza od 250 HB.
EN
Two-stage laboratory rolling of soft bearing rings in helical rolling mills includes: rolling of tube blanks with microstructure of fine lamellar pearlite; controll rolling of rings under consideration of Verhoeven spheroidizing anneealing conditions for 100Cr6 steel. In the obtained soft bearing rings from 100Cr6 steel dominate spheroidized microstructure wich hardness below 250 HB.
Direct extrusion of magnesium alloy AZ31 and changes in microstructure resultant from low-speed small-reduction extrusion are presented. The results show possibilities of grain refinement and improvement of mechanical properties associated with limited amount of generated deformation heat in aspect of using as-extruded material as a forging stock.
PL
Praca przedstawia wyniki prób wyciskania współbieżnego stopu AZ31, obrazujące zmiany zachodzące w mikrostrukturze po wyciskaniu z małym stopniem przerobu oraz małymi prędkościami. Ukazują one szerokie możliwości rozdrobnienia ziarna oraz towarzyszącą im poprawę własności materiału spowodowaną ograniczeniem ilości generowanego ciepła odkształcenia w aspekcie zastosowania wyciskanych prętów jako wsadu do kucia matrycowego.
The aim of the studies performed was to assess an influence of crystallographic orientation relationship (OR) between pearlitic ferrite and cementite on a stability of cementite plates. Diffraction analysis made with an electron microscope showed the existence of the Bagaryatski OR and the Pitsch OR both in the pearlite structure after eutectoid transformation and after each tested time of the sphe-roidization annealing. The obtained results indicate that the crystallographic orientation relationship does not influence the stability of cementite showing lamellar morphology.
PL
Celem przeprowadzonych badań była ocena wpływu orientacji krystalograficznej faz perlitu w stali na stabilność płytek cementytu. Analiza dyfrakcyjna wykonana za pomocą mikroskopu elektronowego wykazała występowanie relacji orientacji krystalograficznych Bagariackicgo oraz Pitscha zarówno w strukturze perlitu po przemianie eutektoidalnej, jak i po każdym badanym etapie wyżarzania sferoidyzującego. Otrzymane wyniki badań dyfrakcyjnych wskazują, że na stabilność cementytu wykazującego morfologie płytkową nic wpływa orientacja krystalograficzna cementytu i ferrytu w strukturze wyjściowej.
Cieplnoplastyczne walcowanie pierścieni łożysk tocznych wymaga wysokiej jakości półwyrobów: prętów do walcowania tulei wstępnych i odwalcowanych tulei. Przedmiotem pracy są badania metalograficzne (mikroskopia świetlna) półwyrobów. Badania dostarczonego przez hutę pręta okrągłego wykazały, że spełnia on wymagania jakości ze względu na: wtrącenia niemetaliczne, pozostałość siatki węglików wtórnych, pasmowość i segregację węglików oraz odwęglenie. Natomiast sferoidyt nie jest jednorodny (w mikrostrukturze, w pobliżu powierzchni pręta zawartość perlitu jest istotnie większa niż w pobliżu środka). Nie powinno to mieć niekorzystnego wpływu na proces walcowania rur i pierścieni. Badania metalograficzne tulei wstępnych, odwalcowanych w warunkach laboratoryjnych, wykazały zbyt duże odwęglenie zewnętrznej warstwy przypowierzchniowej (nastąpiło ono podczas nagrzewania wsadu przed walcowaniem). Takie odwęglenie jest niedopuszczalne przy cieplnoplastycznym walcowaniu pierścieni.
EN
Thermomechanical rolling of antifriction bearing rings requires high quality semi-finished products, i.e., the round bars for rolling of tube blanks and the tube blanks as well. Subject of the article is the metallographic examination (by light microscopy) of semi-finished steel products for thermomechanical rolling of bearing rings. Microscopic investigation of a given round bar (in a supplied state) shows that the material quality satisfias requirements with respect to: non-metallic inclusions, remaines of carbide network, carbide banding, carbide segregation and surface decarburization. However the spheroidite is not homogeneous (in microstructure near the round bar surface, the amount ofpearlite is higher than in the central region). Presumably, this inhomogenities do not have unfavourable effects on the rolling process of tubes and rings as well The metallographic examination of tube blanks, which were rolled in laboratory mill, shows significant decarburization of the outer blank surface regions. It is a consequence of the heating prior to rolling. Such a decarburization is unacceptable for the thermomechanical rolling of bearing rings.
In this paper the assembly and failure analysis of Plastic Ball-Grid-Array (PBGA) "dummy" components mounted on a PCB by reflow soldering were investigated. X-ray microscopy, scanning acoustic (SAM) microscopy and metallographic examinations of solder joint cross-sections as well as electrical measurements of daisy chains were used for diagnostic.
PL
Przedstawiono metodę montażu i analizy uszkodzeń układów testowych BGA w obudowach plastykowych (PBGA), zamontowanych na płytkach drukowanych metodą lutowania rozpływowego. Są układami tzw. "pustymi" przeznaczonymi do testowania połączeń lutowanych - są replikami rzeczywistych układów BGA, ale bez chipów krzemowych pod plastykowymi obudowami układów. Układy testowe mają również system połączeń między kulkami układu BGA, odpowiadający systemowi połączeń między polami lutowniczych na płytce PCB tak, aby po zastosowaniu lutowania rozpływowego możliwe było sprawdzenie poprawności montażu przez pomiar rezystancji pomiędzy polami kontrolnymi układu.
A system of non-overlapping random spheres, whose diameters have the Weibull distribution may be used as a model for the graphite in nodule cast iron. For a given material the model probability density function of the Weibull distribution may be determined (as the first approximation) by fitting the PDF of model profile diameters to the one of graphite particle sections. The Weibull distribution may be used as the basis for quantitative metallography of the graphite phase in nodular cast iron.
PL
Układ nienakładających się losowych kul, których średnice mają rozkład Weibulla, może być geometryczno-stochastycznym modelem dla grafitu w żeliwie sferoidalnym. Dla danego żeliwa gęstość prawdopodobieństwa rozkładu Weibulla można wyznaczyć stereologiczną metodą parametryczną poprzez dopasowanie modelowej gęstości prawdopodobieństwa rozkładu średnic przekrojów kul do danych doświadczalnych. Rozkład Weibulla może być podstawą dla metalografii ilościowej grafitu w żeliwie sferoidalnym.
16
Dostęp do pełnego tekstu na zewnętrznej witrynie WWW
Spheroidization of cementite in an eutectoid carbon steel, whose pearlite phases (ferrite and cementite) possess crystallographic texture, has been investigated by light microscopy and X-ray diffraction. During spheroidization the microstructural changes are accompanied by the ones of cementite texture. In particular, the ideal orientations (010)[201] and (010)[100] describe the main texture component of cementite in pearlite and spheroidized cementite, respectively.
PL
Przedmiotem pracy jest izotermiczna sferoidyzacja cementu w grubopłytkowym perlicie stali węglowej eutektoidalnej. W wyniku badań metalograficznych i rentgenograficznych zostało wykazane, że z jakościowymi i ilościowymi zmianami mikrostruktury cementu sa związane określone zmiany krystalograficznej tekstury faz: ferrytu i cementytu.
A Nimonic type alloy was subjected to the heat treatment which included homogenization (1200 degrees centigrade) and ageing (750 degrees centigrade) up to 850 hours. The precipitation process was examined by means of the following methods: transmition electron microscopy, light microscopy and microhardness measurements. The hardness changes have been analysed in connection with the precipitation morphology.