On the forming and fracture limits of sheet metals

Korhonen A. S., Manninen T., Yoon J. W.

Computer Methods in Materials Science

2009

Vol. 9, No. 1

143-147

It became apparent in the late 1980 that all manufacturing processes in the future would be first simulated before industrial implementation. Sheet metal forming was one of the most important applications where this technology could be applied. One of the issues was to represent the plastic behavior of sheet materials. For accurate numerical simulations information is needed on the initial yielding, subsequent work-hardening and final localization of plastic flow and/or fracture. The forming limits have been studied since the mid-1940s, when Gensamer and Lankford and coworkers carried out their tests with steel and aluminum. In this work we discuss the forming and fracture limits of low carbon steel, stainless steel and aluminum. Experimental results on stretch forming, deep drawing and tensile testing will be presented. Hydraulic bulge testing is employed in the stretch forming experiments. Marciniak-type in-plane tests are carried out to study the limit strains in deep drawing. Laser marked grids are used to measure the surface strains and scanning electron microscopy is employed to measure the thickness strains and to study the fracture surfaces.

Badaniom poddane zostały ograniczenia możliwości odkształcania i pojawianie się pęknięć w blachach ze stali nierdzewnej i aluminium. Test hydraulicznego wybrzuszenia został przeprowadzony w procesie formowania z rozciąganiem. Test typu Marciniaka oraz testy rozciągania zostały przeprowadzone w celu zbadania granicznej odkształcalności. Siatka naniesiona metodą sitodruku i laserem została użyta do pomiaru odkształceń powierzchni próbki. Ponadto, użyto mikroskopu skaningowego do pomiaru odkształceń na grubości i badania powierzchni pęknięć.

Forming limits of austenitic stainless steel sheets

Korhonen A., Manninen T., Kanervo K.

Computer Methods in Materials Science

2006

Vol. 6, No. 3-4

178-187

The forming limits of austenitic stainless steel sheets were studied. It was found that the observed limit of straining in stretch forming, when both of the principal stresses are positive, is not set by localized necking, but instead by shearing fracture in the through thickness direction. Thus, the Marciniak-Kuczynski type of analysis, which has recently been successfully applied to both low-carbon steels and aluminum, may not apply to austenitic stainless steels. It appears that the forming limits of austenitic stainless steels may be predicted fairly well by using the classical localized and diffuse necking criteria developed by Hill. The fracture criterion of Ritchie and Thompson seems to overestimate the fracture limit. Better models are needed for the work hardening and to develop better limit strain criteria, since the work hardening seems to depend strongly on both strain rate and temperature. The formability of austenitic stainless steels appears to remain good even when coated with hard TiN, although unavoidable cracks will appear with continuing straining.

Przedmiotem pracy jest odkształcalność graniczna stali austenitycznych. Zaobserwowano, że odkształcalność przy dwuosiowym rozciąganiu, gdy dwa naprężenia główne są dodatnie, nie jest wyznaczana przez lokalne tworzenie się szyjki, ale przez pękanie wywołane przez ścinanie w kierunku grubości blachy. Dlatego metoda Marciniaka-Kuczynskiego, która jest z powodzeniem stosowana do stali nisko-węglowych i aluminium, może nie stosować się do stali austenitycznych. Okazuje się, że odkształcenia graniczne stali austenitycznych mogą być poprawnie przewidywane przez zastosowanie opracowanego przez Hilla klasycznego kryterium lokalizacji i rozprzestrzeniania się szyjki. Kryterium pękania Ritchie-Thompsona wydaje się przeszacowywać granicę pękania. Ponieważ umocnienie zależy mocno od prędkości odkształcenia i temperatury, lepsze modele są potrzebne do opisu umocnienia i opracowania poprawnego kryterium granicznych odkształceń. Odkształcalność graniczna stali austenitycznej utrzymuje się na dobrym poziomie nawet wtedy, gdy stal jest pokryta TiN, chociaż nieuniknione pęknięcia pojawią się w czasie odkształcenia.