An in vitro examination of fluoride ions release from selected materials – resin-modified glass-ionomer cement (Vitremer) and nanohybrid composite material (Tetric EvoCeram)

Kosior Piotr, Klimas Sylwia, Nikodem Anna, Wolicka Justyna, Diakowska Dorota, Watras Adam, Wiglusz Rafał J., Dobrzyński Maciej

Acta of Bioengineering and Biomechanics

|

2023

|

Vol. 25, no. 1

101--115

EN

The aim of this study was to examine a short-term fluoride ions release from selected materials – resin-modified glass ionomer –Vitremer (3M ESPE) and nanohybrid universal composite – Tetric EvoCeram (IvoclarVivadent). Release of fluoride ions [µg/mm2 /h] from Tetric EvoCeram and Vitremer into nine environments (artificial saliva – AS, deionized water and 0.9% NaCl) differing in composition of the solution and pH was determined. Six samples were prepared for each solution. In the short-term study, the measurements were taken after 1, 3, 24, 48, 72 and 168 hours. The cumulative values as well as levels of fluoride ions released at concrete time intervals were compared. Within 7 days (168 hours), both materials showed variable levels of fluoride ions release. The highest value of fluoride ions release from nanohybrid Tetric EvoCeram material was reported in deionized water (8) after 24 hours (1.550 ± 0.014 [µg/mm2 /h]) and the lowest value was read in the artificial saliva AS pH 7.5 (5) after 1 hour (0.022 ± 0.001 [µg/mm2 /h]). What’s more, the highest value of Frelease from Vitremer was found in deionized water (8) after 168 hours of immersion (24.021 ± 2.280 [µg/mm2 /h]) and the lowest value was in the artificial saliva AS (without Ca2+) pH 4.5 (6) (0.303 ± 0.249 [µg/mm2 /h]) after 168 hours. Cumulated release of F– after 7 days was notably higher from resin- modified glass ionomer material – Vitremer in all artificial saliva solutions (1–7) which imitated the environment of oral cavity. Therefore, we can assume that Vitremer has better remineralization potential and it may constitute a more effective method of tooth decay prevention.

2

Evaluation of the microbial, cytotoxic and physico-chemical properties of the stainless steel crowns used in pediatric dentistry

Sztyler Klaudia, Pajączkowska Magdalena, Nowicka Joanna, Rusak Agnieszka, Chodaczek Grzegorz, Nikodem Anna, Wiglusz Rafał J., Watras Adam, Dobrzyński Maciej

Acta of Bioengineering and Biomechanics

|

2022

|

Vol. 24, no. 4

127--137

EN

Preformed stainless steel crowns are used in pediatric dentistry to obtain full crown restoration of primary molar teeth. They are consider the best restoration in terms of durability and effectiveness. The purpose of this study is to evaluate microbial, cytological and physio-chemical properties to determine whereas stainless steel crown are biocompatible, safe for surrounding tissue and helpful in avoiding micro-organisms influence on the tooth tissue. Based on the results, it was determined that stainless steel crowns used in pediatric dentistry represent no cytotoxic risk to the surrounding tissues, have a low probability of developing hypersensitivity to the coronal material and also that their biological properties make them suitable to use in pediatric dentistry for the reconstruction of damaged primary molar tissue.

3

Wykorzystanie biometrii ultradźwiękowej w nieinwazyjnej diagnostyce tkanek przyzębia

Zakrzewska Aneta, Zakrzewski Łukasz, Dobrzyński Maciej

Inżynier i Fizyk Medyczny

|

2021

|

Vol. 10, nr 6

493--496

PL

Znajomość morfologii tkanek miękkich jest niezbędna w diagnostyce i planowaniu leczenia stomatologicznego, ortodontycznego, protetycznego, implantologicznego oraz w zabiegach z zakresu chirurgii plastycznej tkanek przyzębia. Metoda pomiaru grubości tkanek miękkich przyzębia wykorzystująca ultradźwięki UGTM (ang. ultrasonic gingival thickness measurement) jest prosta, nieinwazyjna, a samo badanie jest bezbolesne i komfortowe dla pacjenta. Wykorzystanie biometru ultradźwiękowego ułatwia diagnostykę i monitorowanie stanu tkanek przyzębia, co polepsza profilaktykę, ułatwia planowanie oraz leczenie stomatologiczne, a także pośrednio przyczynia się do osiągnięcia sukcesu terapeutycznego.

EN

The knowledge of the soft tissues’ morphology is essential in the diagnosis and planning of dental, orthodontic, prosthetic and implantological treatment as well as in periodontal plastic surgery procedures. The method of measuring the thickness of periodontal soft tissues using ultrasonic gingival thickness measurement (UGTM) is simple and non-invasive. The examination is painless and comfortable for the patient. The use of an ultrasound biometer facilitates the diagnosis and monitoring of the periodontal tissues condition. It improves prophylaxis, facilitates dental treatment and its planning as well as indirectly contributes to the achievement of therapeutic success.

4

The assessment of temperature amplitude arising during the implant bed formation in relation to variable preparation parameters – in vitro study

Kosior Piotr, Nikodem Anna, Kozuń Marta, Dudek Krzysztof, Janeczek M., Dobrzyński Maciej

Acta of Bioengineering and Biomechanics

|

2021

|

Vol. 23, no. 3

163--173

EN

The main purpose of this study was to analyse the temperatures generated during the bone bed preparation, given the internal structure of the bone bed, the geometry of the hole, and the treatment parameters such as the type of cooling and the rotational speed of the drill. The investigated material was domestic pig ribs, in which holes were drilled three times using two drill bit systems used for Hiossen® and Paltop® dental implantation. The ThermaCAM® P640 thermal imaging camera was used for measurement of drilling temperatures. After the holes were drilled, each rib was examined using the 1172 SkyScan microtomograph, Bruker®, to compare the geometry of the machined holes. The presented study proved that larger diameter drill bits (Hiossen® drill bits) generate more heat during the machining process, as evidenced by higher temperatures obtained for the Hiossen system in each case. It was proved that rotational speed, drill bit diameter and cooling system have a significant effect on the amount of heat generated during bone tissue preparation. The density and type of bone tissue in which the hole is prepared are significant factors affecting the amount of heat generated.

5

Przyrostowe wytwarzanie indywidualizowanych wypełnień ubytków kostnych na bazie materiałów ceramicznych

Rusińska Małgorzata, Chlebus Edward, Dobrzyński Maciej

Przegląd Mechaniczny

|

2020

|

nr 9

25--32

PL

W artykule przedstawiono metodę oraz wyniki badań obejmujące próbę dostosowania przyrostowej technologii selektywnego łączenia ziaren proszku do wytwarzania indywidualizowanych ceramicznych uzupełnień ubytków kostnych z zastosowaniem syntetycznego hydroksyapatytu. W dobie intensywnego rozwoju nowoczesnych technologii wytwórczych pojawia się coraz więcej możliwości ich wykorzystania w medycynie, szczególnie z uwagi na zapewnienie precyzyjnego odwzorowania anatomii pacjenta, opartego na danych pochodzących z obrazowania medycznego. Przyrostowe wytwarzanie znalazło już zastosowanie w wytwarzaniu trójwymiarowych modeli fizycznych umożliwiających szczegółową analizę skomplikowanych przypadków oraz służących do planowania i symulacji operacji w celu zmniejszenia ryzyka oraz skrócenia czasu trwania zabiegu. Znane są również przypadki przeprowadzenia implantacji z wykorzystaniem indywidualizowanych implantów. Najczęściej wykorzystywanym materiałem w takich przypadkach są stopy tytanu, co niesie liczne ograniczenia: brak dopasowania własności mechanicznych, brak degradacji czy niepożądane reakcje obronne organizmu. Z tego powodu nieustannie trwają badania nakierowane na wytwarzanie bioakceptowalnych i biodegradowalnych materiałów, które posłużą wytwarzaniu czasowych konstrukcji wspomagających odbudowę naturalnej tkanki w miejscach ubytków. W artykule zaprezentowano metodę wytwarzania oraz przygotowania wszczepów z zastosowaniem biomateriału ceramicznego. W ramach prowadzonych badań wykonano analizę oraz dobrano odpowiednie materiały, parametry procesowe i przeanalizowano ich wpływ na jakość wytwarzanych modeli. Otrzymany w przygotowanej metodzie materiał do zastosowań medycznych poddano testom in vitro, w celu weryfikacji właściwości biologicznych.

EN

The paper presents the method and results comprising adjustment of the incremental technology of selective connection of the powder particles. It is used for the manufacturing of ceramic restorations of individualized bone defects based on synthetic hydroxyapatite. In the era of intensive development of modern technologies of manufacturing, there are more and more opportunities to use their extensive capabilities in medicine, particular by the precise mapping of the patient’s anatomy based on data from medical imaging. Incremental manufacturing has already found application in the manufacture of three-dimensional physical models enabling a detailed analysis of complicated cases and used for planning and simulation of operations to reduce the risk and duration of treatment. There are also known some cases of carrying out the implantation with the use of individualized implants. The most commonly used material in such cases are titanium alloys which cause many restrictions i.e., no matching of mechanical properties, lack of degradation or adverse reactions of the body’s defenses. For this reason, many research is being continuously conducted focusing on manufacturing bioacceptable and biodegradable materials, which will be used in manufacture of temporary structures supporting the restoration of the natural tissue in places of cavities. This paper presents a method of manufacturing and preparing implants using ceramic biomaterial. In this study, appropriate materials as well as process parameters have been chosen and their impact on the quality of the generated models was analyzed. Obtained material for medical use has been tested in vitro to verify biological properties.

6

Odporność na cykliczne zmęczenie wybranych endodontycznych narzędzi maszynowych w świetle piśmiennictwa

Piekielny Martyna, Jarmołowicz Marcin, Dobrzyński Maciej

Inżynier i Fizyk Medyczny

|

2020

|

Vol. 9, nr 2

143--144

PL

Narzędzia Ni-Ti, zarówno rotacyjne, jak i recyprokalne, znacznie usprawniły poszerzanie kanałów korzeniowych, odkąd tylko pojawiły się na rynku. Równocześnie z przyspieszeniem czasu pracy lekarza wystąpił problem łamania się narzędzi w kanałach zagiętych, w których narzędzia maszynowe niekiedy ulegały złamaniu łatwiej niż narzędzia ręczne. Skłoniło to producentów i praktyków do wykonywania testów odporności wierteł endodontycznych na działanie różnych czynników mechanicznych, które mogą wpływać na podatność narzędzi do łamania się. W związku z pojawieniem się na rynku w ostatnich latach licznych nowości w dziedzinie wierteł maszynowych do opracowywania kanałów korzeniowych, dokonano przeglądu wybranych narzędzi wykonanych ze stopów NiTi oraz porównano je pod kątem wytrzymałości na zmęczenie cykliczne. Wykorzystano dane biomechaniczne do sformułowania wniosków dotyczących zmęczenia cyklicznego endodontycznych wierteł maszynowych. Ocenie zostały poddane czynniki takie jak: rozmiar wg ISO, rodzaj stopu Ni-Ti, z jakiego zostało stworzone narzędzie, giętkość i pamięć kształtu oraz rodzaj ruchu, jaki wykonuje.

EN

Ni-Ti tools, both rotational and reciprocal, have significantly improved root canal widening since they appeared on the market. Simultaneously with the acceleration of dentist’ work, the problem of breaking tools in bent channels appeared, in which sometimes machine tools broke more easily than hand tools. This prompted manufacturers and practitioners to test endodontic drills for resistance to various mechanical factors that may affect tool breakability. Due to the appearance on the market of many new products in the field of machine drills in recent years, a review of selected NiTi machine endodontic drills available on the market for the development of root canals and their comparison in terms of resistance to cyclic fatigue was carried out. Biomechanical data were used to formulate conclusions about the cyclic fatigue of machine drills. The following factors were assessed: ISO size, type of Ni-Ti alloy from which the tool was created, flexibility and shape memory as well as the type of movement it makes.

7

Charakterystyka kompozytowych materiałów stomatologicznych stosowanych w gabinetowych systemach CAD/CAM

Rogula Jakub, Kuźniar-Folwarczny Agnieszka, Sulewski Mikołaj, Błaszczyk Anna, Sulewska Agnieszka, Kosior Piotr, Dobrzyński Maciej

Inżynier i Fizyk Medyczny

|

2020

|

Vol. 9, nr 1

57--61

PL

Praca zawiera charakterystykę materiałów kompozytowych i hybrydowych stosowanych w gabinetowych systemach CAD/ CAM, jak również opis procedury zabiegowej podczas leczenia pacjenta z zastosowaniem jednego z nich. Materiały kompozytowe stosowane powszechnie do odbudowy bezpośredniej zębów posiadają wady, które zostały wyeliminowane w prefabrykowanych bloczkach zdatnych do obróbki skrawaniem. Frezowanie pracy ostatecznej podczas tej samej wizyty umożliwia uzyskanie uzupełnienia o lepszych właściwościach fizyko-chemicznych, lepszej estetyce i pozbawionego takich wad jak skurcz polimeryzacyjny, w podobnym czasie, co standardowe leczenie zachowawcze.

EN

The work contains the characteristics of composite and hybrid materials used in the office CAD/CAM systems, as well as a description of the procedure during treatment of the patient using one of them. Composite materials commonly used for direct tooth reconstruction have defects that have been eliminated in prefabricated blocks suitable for machining. Milling the final work during the same visit makes it possible to obtain a restoration with better physico-chemical properties, better aesthetics and free of defects such as polymerization shrinkage. All that is at a similar time as standard conservative treatment.

8

Assessment of cytotoxic and antimicrobial activity of selected gingival haemostatic agents – in vitro study

Szymonowicz Maria, Rusak Agnieszka, Pajączkowska Magdalena, Nowicka Joanna, Wiśniewska Kamila, Żywicka Bogusława, Żywicka Bogusława, Rybak Zbigniew, Dobrzyński Maciej

Acta of Bioengineering and Biomechanics

|

2020

|

Vol. 22, no. 3

185--198

EN

Purpose: The present research aimed to determine whether and how the aluminium chloride – based materials affect the cell line of the bacterial line and fungi. Methods: Cytotoxicity of haemostatic astringents: Alustat (liquid), Alustat (gel), Alustat (foam), Alustin, Hemostat, Racestyptine and Traxodent containing AlCl3 was conducted on L929 cell line with the use of MTT and SRB assays. The antimicrobial activity (CFU and MIC) against C. albicans, S. mutans, L. rhamnosus was determined. Results: In the MTT results, cell viability for all agents were very low. In SRB, the lowest cytotoxicity was demonstrated for Hemostat and Alustat (foam), Traxodent and Racestyptine. Total reduction of the CFU of S. mutans was observed. Alustat (gel) and Alustat (liquid) completely inhibited the growth of C. albicans, S. mutans and L. rhamnosus. Conclusions: The viability of L929 cells obtained in the SRB assay is more reliable than that obtained in the MTT assay, in the case of gingival haemostatic agents.

9

Zgodność barwy spolimeryzowanych stomatologicznych kompozytów światłoutwardzalnych z nazewnictwem producentów w oparciu o klucz kolorystyczny VITA : badania doświadczalne przy użyciu elektrooptycznego urządzenia Shade Star® Dentsplay

Berdzik-Janecka Marta, Jawor-Moczulska Natalia, Kosior Piotr, Dobrzyński Maciej, Dudek Krzysztof, Gajos Błażej

Inżynier i Fizyk Medyczny

|

2019

|

Vol. 8, nr 1

69--72

PL

Materiał kompozytowy jest najbardziej popularnym materiałem wykorzystywanym w stomatologii odtwórczej. Jedną z jego najważniejszych zalet jest wysoka estetyka możliwa do osiągnięcia dzięki szerokiej gamie kolorystycznej. W celu uproszczenia pracy lekarzom klinicystom, zarówno stomatologii zachowawczej, dziecięcej, jak i protetyki, wprowadzono ujednolicony szablon kolorystyczny wg VITA. Producenci dostępnych na rynku materiałów stomatologicznych do bezpośredniej rekonstrukcji zębów oferują zestawy kompozytów o nazewnictwie barwy opartym wg wspomnianego kolornika. Zaobserwowano jednak istotne różnice między barwą materiału odtwórczego określoną przez klinicystę na podstawie kolornika a uzyskanym finalnym efektem kolorystycznym wypełnienia. W pracy podjęto zagadnienie porównania w warunkach doświadczalnych barwy próbki spolimeryzowanego materiału złożonego z barwą sugerowaną przez producenta.

EN

A composite material is the most popular material used in restorative dentistry. One of its main advantages is the high aesthetics achievable with a wide range of colors. In order to simplify the work of clinicians, both conservative dentistry, pediatric and prosthetics, introduced a unified template color by VITA. Manufacturers of dental materials available on the market, to direct tooth reconstruction offer sets of composites- based naming colors mentioned by the shade guide. However, it has been observed a significant differences between the color of the restorative material as determined by the clinician based on the shade guide and the final color result of the filling. The paper presents an the problem of the comparison under the experimental conditions color of the sample of polymerized composite material with the color recommended by producer.

10

Kliniczno-terapeutyczne aspekty próchnicy korzenia z uwzględnieniem lasera Er:YAG i ozonoterapii

Wolska Agnieszka, Kiryk Jan, Rogula Jakub, Sulewski Mikołaj, Han Anna, Wiglusz Rafał J., Dobrzyński Maciej

Inżynier i Fizyk Medyczny

|

2019

|

Vol. 8, nr 2

153--156

PL

Próchnica korzenia jest chorobą cementu korzeniowego występującą zazwyczaj u osób starszych. Przyczyną jest odsłonięcie cementu korzeniowego i zalegająca płytka nazębna. Odsłonięcie następuje poprzez obniżenie przyczepu nabłonkowego w wyniku recesji lub choroby przyzębia. Czynnikami ryzyka próchnicy korzenia są zła higiena, dieta bogata w węglowodany, zaburzenia wydzielania śliny. Zasadnicze leczenie polega na eliminacji czynników ryzyka, profilaktyce fluorkowej, leczeniu odtwórczym. Obecnie coraz częściej wykorzystuje się ozonoterapię oraz opracowywanie chorobowo zmienionych tkanek przy pomocy lasera erbowo-yagowego.

EN

The root caries is a root’ cement disease that usually occurs in older people. The cause is the exposure of the root cement and residual plaque. Exposure occurs by lowering the epithelial attachment as a result of recession or periodontal disease. Risk factors for root caries are poor hygiene, a carbohydrate-rich diet, salivary flow disorders. The basic treatment consists in the elimination of risk factors, fluoride prophylaxis and restorative treatment. Currently, the ozone therapy and the erbium-yag laser are more often used in root caries treatment.

11

Charakterystyka ceramicznych materiałów stomatologicznych stosowanych w gabinetowych systemach CAD/CAM

Kuźniar-Folwarczny Agnieszka, Sulewski Mikołaj, Błaszczyk Anna, Sulewska Agnieszka, Kosior Piotr, Dobrzyński Maciej

Inżynier i Fizyk Medyczny

|

2019

|

Vol. 8, nr 6

479--487

PL

Gabinetowe systemy CAD/CAM pozwalają wykonywać uzupełnienia protetyczne podczas jednej wizyty. Zaspokojenie wysokich wymagań pacjentów związanych z estetyką uzupełnień protetycznych uwarunkowane jest dostępnością materiałów niezbędnych do ich wykonania. Materiały, z których wykonuje się uzupełnienia, to bloczki ceramiki skaleniowej, ceramik wzmacnianych leucytem lub dwukrzemianem litu, a także ceramiki hybrydowej. Spektrum uzupełnień możliwych do wykonania w danym systemie zależy od rozmiaru posiadanej maszyny frezującej, rozmiaru bloczka i właściwości wybranego materiału. Celem pracy było przedstawienie charakterystyki ceramik dentystycznych stosowanych w gabinetowych systemach CAD/CAM oraz zalet wynikających z wykorzystania tego systemu w codziennej praktyce. Opisano także postępowanie kliniczne zalecane podczas pracy z tą technologią z uwzględnieniem różnic w zależności od zastosowanego materiału do odbudowy. Wybór odpowiedniego materiału do danej sytuacji klinicznej jest zadaniem lekarza dentysty i wymaga uwzględnienia wielu czynników.

EN

Chairside CAD/CAM systems allow dental practitioners to provide their patients with restorations made during a single appointment. Satisfying the high requirements of patients associated with aesthetic restorations results for the availability of materials necessary for their performance. Materials for these restorations comprise blocks made of feldspar, leucite- and lithium disilicate-reinforced ceramics and also hybrid ceramics. The spectrum of restorations that can be fabricated with a chairside system depends on the size of the milling machine, the size of material block, and the properties of the selected material. The aim of this study was to present characteristics of dental ceramics used in chairside CAD/CAM systems and to show the benefits of using it in daily practise. Also, the clinical treatment recommendations were described based on the differences between the used material blocks. The choice of the best material to match the clinical situation is a dentist’task and many factors must be taken into account.

12

Thermographic evaluation of experimental pleurisy induced by carrageenan and modified by 2,3,7,8-tetrachlorodibenzo-p-dioxin (TCDD)

Kuropka Piotr, Dobrzyński Maciej, Tarnowska Małgorzata, Dymarek Robert, Leśków Anna, Wiglusz Rafał J.

Acta of Bioengineering and Biomechanics

|

2019

|

Vol. 21, no. 3

23--29

EN

The use of a thermal imaging camera may improve the detection of changes during inflammation process propagation in animals and humans that could be caused by numerous factors like 2,3,7,8-tetrachlorodibenzo-p-dioxin (TCDD). Methods: Rats were randomised and divided into two groups, C group, in which experimental pleural inflammatory reaction was evoked and TCDD group, in which a single dose was applied 21 days before administration of 1% carrageenan solution. Infrared thermograms were taken with a microbolometer thermal imaging camera MobIR M8. The surface temperature distribution was measured in three randomly selected animals. Results: In the analysis of correlation we found negative results between both groups. In the C group, the pleurisy was developed and allowed to develop freely. It can be observed that both the average maximum temperature and the average minimum temperature were the highest after 48 hours after injection of the 1% carrageenan in solution. In TCDD group, lowered temperature in all days of experiments was noted. However, the increase of temperature after carrageenan injection was similar. The main changes observed in the lungs were oedema, hyperemia with clot formation and changes in lung structure. Several proliferative changes in the lungs were noted. Moreover, increased number of goblet cells as well and increased release of the surfactant was observed. The activation of fibroblasts and synthesis of collagen fibers was noted. Conclusions: The TCDD administration results in the reduction of superficial temperature, which is easily detectable by thermal imaging camera that can be effectively used in monitoring the course of inflammation.