Functional Properties and Electromagnetic Shielding Behaviour of Elastic Warp-knitted Fabrics

Yu Z. C., He H. L., Lu Y. H., Zhang J. F., Lou C. W., Chen A. P., Lin J. H.

Fibres & Textiles in Eastern Europe

|

2015

|

Vol. 23, no. 5 (113)

78--83

EN

An investigation was made on the electromagnetic shielding behaviour and other functional properties for manufactured multifunctional elastic warp-knitted fabrics. Bamboo charcoal polyester/Crisscross-section polyester (BC-PET/CSP) blended yarns were used as the back of the warp-knitted fabric while conductive composite yarns were used as the front. The variation in the far infrared emissivity and anion density of elastic-warp knitted fabrics produced with different proportions of BC-PET content were studied in detail. Moreover the electromagnetic shielding effectiveness (EMSE) of the fabrics with different elongation was measured in this study. The experimental results showed that increased elongation almost did not significantly affect the EM shielding behaviour of fabric K1 in the elongation range of 0 - 40%. Finally to increase the EMSE of the fabric, the lamination method was used in this study. EMSE measurement results showed that two layer K1 warpknitted fabrics with 90° interval displayed a better shielding effect against the EM wave compared to that with a 0° interval.

PL

Przeprowadzono badania właściwości ekranujących przed polem elektromagnetycznym i innych właściwości funkcyjnych wyprodukowanych wielofunkcyjnych elastycznych dzianin kolumienkowych. Zastosowano przędze kompozytowe z mieszanek zawierających drut ze stali kwasoodpornej, ciągłe włókna poliamidowe i poliestrowe oraz cięte włókna ze regenerowanej celulozy z surowca bambusowego. Badano emisyjność w dalekiej podczerwieni i gęstość anionową dzianin kolumienkowych wytworzonych przy rożnych proporcjach zastosowanych składników. Poza tym badano efektywność ochrony elektromagnetycznej dzianin przy rożnych wydłużeniach. Wyniki eksperymentów pokazują, że zwiększone wydłużenie prawie nie wpływa istotnie na właściwości ekranujące. Dla zwiększenia efektu ekranowania zastosowano metodę laminacji.

2

Moisture Comfort and Antibacterial Properties of Elastic Warp-Knitted Fabrics

Yu Z. C., Zhang J. F., Lou C. W., He H. L., Chen A. P., Lin J. H.

Autex Research Journal

|

2015

|

Vol. 15, no. 1

60--66

EN

Multifunction elastic warp-knitted fabrics were fabricated on a crochet machine with the use of metal composite yarns/viscose yarn and bamboo polyester/ crisscross-section polyester hybrid yarns as the front face and back face of the knitted fabric structure, respectively. We investigated the effect of the blend ratio of bamboo charcoal/ crisscross-section polyester multiply yarns on the fabric's moisture comfort properties, such as water vapour transmission (WVT), water evaporation rate (WER), and water absorbency. The results showed that blending ratio significantly influenced WVT and WER. Moreover, antibacterial activity of the elastic warp-knitted fabric was tested against Staphylococcus aureus and Escherichia coli in accordance with AATCC 90-2011. Finally, the extension-stress value curves were used to analyse the elastic stretching property, and the fabric exhibited greater breaking elongation and lower stress value in the walewise than in the weft direction.

3

Evaluation of the Manufacturing and Functions of Complex Yarn and Fabrics

Lin C. M., Lin C. W., Yang Y. C., Lou C. W., Chen A. P., Lin J. H.

Fibres & Textiles in Eastern Europe

|

2012

|

Vol. 20, no. 4 (93)

47--50

EN

In this research, bamboo charcoal/spandex (BC/S) complex yarn was fabricated using spandex as the core yarn, which was then wrapped with bamboo charcoal nylon textured yarn. The core yarn was first expanded and then wrapped with the wrapping yarn on a rotor twister machine at speeds of 4000, 6000, 8000, 10000, and 12000 r.p.m. The wrapping amount of the BC/S complex yarns were 2, 3, and 4 turns/cm. In order to evaluate the physical properties of the BC/S complex yarn, the maximum breaking strength, elongation, and elastic recovery rate were tested. We fabricated BC/S fabrics using circular knitting based on optimal manufacturing parameters. The BC/S complex yarn had an optimum elastic recovery rate of 98.89% when the rotor speed was 10000 r.p.m and the wrap number 4 turns/cm. The optimum tenacity of the yarn containing 44.0 dtex spandex was 4.22 cN/dtex when the rotor speed was 4000 r.p.m. and the wrap number 2 turns/cm. The anion density of the BC/S fabric increased with the wrap number; in particular, the fabric containing 76.9 dtex spandex displayed an optimum anion density of 54 anions/cc.

PL

Badano przędze składające się ze zwęglonych włókien bambusowych oraz wysokoelastycznych włókien typu spandex, których użyto jako włókien rdzeniowych. W pierwszej fazie włókna typu spandex ulegały rozciąganiu, a następnie były owijane włóknami bambusowymi przy wykorzystaniu wirnikowej maszyny skręcającej. Dla określenia właściwości fizycznych wyprodukowanych włókien hybrydowych określono wytrzymałość na zerwanie, wydłużenie i stopień odprężności. Wyprodukowano dzianiny na cylindrycznej maszynie dziewiarskiej przy optymalnych parametrach pracy dla uzyskania określonych właściwości dzianiny. Maksymalna wytrzymałość wyprodukowanych włókien hybrydowych wynosiła około 4 cN/dtex. Gęstość anionowa dzianiny wzrastała ze wzrostem ilości oplotów przędzy.

4

Evaluation of a Manufacturing Technique of Polyamide Bamboo Charcoal/ Polyurethane Complex Yarns and Knitted Fabrics and Assessment of their Electric Surface Resistivity

Lin C. M., Huang C. C., Lou C. W., Chen A. P., Liou S. E., Lin J. H.

Fibres & Textiles in Eastern Europe

|

2011

|

Vol. 19, no. 2 (85)

28-32

EN

In this research, bamboo charcoal polyamide / polyurethane (BCP/PU) complex yarns and knitted fabrics were produced from bamboo charcoal polyamide textured yarn and polyurethane fbres. Te polyurethane fbres were expanded and then wrapped with the bamboo charcoal polyamide textured yarn. Tree manufacturing parameters were depicted as follows: the speeds of the rotor twister were 4000-12000 r.p.m., the wrapped counts of the BCP/PU complex yarns - 200 - 400 turns/m; and the expanded multiple of the polyurethane fbres was 3. Aferwards we fabricated BCP/PU complex knitted fabrics using a circular knitting machine. Te tenacity of the BCP/PU complex yarns was 37258.4 cN/tex when the speed of the rotor twister was 4000 r.p.m. and the wrapped counts - 200 turns/m. Meanwhile, the elongation of the BCP/P complex yarns was 35.77% when the speed of the rotor twister was 4000 r.p.m. and the wrapped counts - 400 turns/m. Te lower electric surface resistivity of the BCP/PU knitted fabrics was 3.33×1010 (?/Square) when the wrapped counts were 400 turns/m and the polyurethane fbres - 78 dtex. Moreover, when the wrapped counts were 200 turns/m, the optimum air permeability of the BCP/PU complex knitted fabrics with 44 dtex polyurethane fbres was 47.2 cm3/cm2/s, which was better than that with 78 dtex polyurethane fbres.