Electrolytic Ni-P-TiO2 composite layers for the hydrogen electroevolution

Łosiewicz B., Stępień A., Gierlotka D., Budniok A.

Archiwum Nauki o Materiałach

1998

t. 19, nr 3

157-166

Ni-P-TiO2 active cathodes were prepared by simultaneous electrodeposition of Ni and TiO2 on a Cu substrate from a solution in which TiO2 particles were suspended by stirring. Electrodeposition was carried out under galvanostatic conditions in the range of current densities: 200-240 mA . cm-2 for 0,5 h. For comparison Ni-P layers were also obtained under the same conditions. X-ray diffractometer, scanning electron microscope and atomic absorption spectroscope were used for physical and chemical characterization of the layers. It was ascertained that the introduction of TiO2 to the amorphous Ni-P layers, irrespective of environment, leads to an increase in the rate of hydrogen evolution in comparison with conventional Ni-P layers.

Aktywne katody Ni-P-TiO2 otrzymywano przez jednoczesne elektroosadzanie Ni i TiO2 na podłożu Cu z roztworu, w którym cząstki TiO2 utrzymywano w zawiesinie, stosując ciągłe mieszanie. Elektroosadzanie prowadzono w warunkach galwanostatycznych w zakresie gęstości prądowych: 200-240 mA.cm-2 przez 0,5 h. W celach porównawczych otrzymano w tych samych warunkach warstwy Ni-P. Do fizycznej i chemicznej charakterystyki warstw użyto dyfraktometru rentgenowskiego, skaningowego mikroskopu elektronowego i spektrometru atomowej absorpcji. Dowiedzono, że - niezależnie od środowiska - wbudowanie TiO2 do amorficznych warstw Ni-P prowadzi do wzrostu prędkości wydzielania wodoru w porównaniu z konwencjonalnymi wartwami Ni-P.

Electrolytic composite Ni-P-NiO and Ni-P-Ni(OH)2 layers for the hydrogen electroevolution

Popczyk M., Gierlotka D., Budniok A.

Archiwum Nauki o Materiałach

1998

t. 19, nr 1

9-20

Electrodeposited composite Ni-P-NiO and Ni-P-Ni(OH)2 layers were obtained in galvanostatic conditions at 298 K from the nickel plating bath containing nickel oxide in one case and nickel nitrate in the other. For comparison the Ni-P composite layers were also obtained and investigated in the same manner. X-Ray diffraction method was used to determine phase composition of the layers and the atomic absorption spectrometry was applied to specify their chemical composition. The behaviour of this obtained layers was investigated in the process of hydrogen evolution from alkaline environment. Tafel equation parameters and exchange currents were calculated form the measured polarization curves. The results obtained were used to estimate the ability of a given electrode material to facilitate hydrogen evolution in alkaline environment. It was found that the activating of nickel by incorporation of Ni(OH)2 improved the rate of hydrogen evolution in an alkaline environment.

Elektrolityczne warstwy kompozytowe Ni-P-NiO i Ni-P-Ni(OH)2 otrzymano w warunkach galwanostatycznycyh, w temperaturze 298 K, z elektrolitu do niklowania zawierającego w jednym przypadku tlenek niklu, a w drugim - azotan niklu. Dla celów porównawczych otrzymano również warstwy Ni-P, które poddano identycznym badaniom, jak pozostałe. Analizę składu fazowego otrzymanych warstw przeprowadzono na dyfraktometrze firmy PHILIPS. Analizę składu chemicznego przeprowadzono metodą atomowej absorpcji za pomocą spektrofotometru atomowej absorpcji. Otrzymane warstwy poddano elektrochemicznej charakterystyce w procesie elektrowydzielania wodoru w środowisku alkalicznym. Na podstawie otrzymanych krzywych polaryzacji obliczono parametry równania Tafela oraz wartości prądu wymiany. Uzyskane wyniki posłużyły jako kryterium oceny zdolności danego materiału elektrodowego do wydzielania wodoru w środowisku alkalicznym. Stwierdzono, że aktywowanie niklu za pomocą Ni(OH)2 zwiększa szybkość wydzielania wodoru w środowisku alkalicznym.