Effect of Ti Addition on the Residual Aluminium Content and Mechanical Properties of the B4C-Al Composites Produced by Vacuum Infiltration

Xiaozhou C, Chao W., Xiangxin X., Gongjin C.

Archives of Metallurgy and Materials

2015

Vol. 60, iss. 4

2493--2498

The effect of Ti addition on the residual Al content and mechanical properties of B4C-Al composites fabricated by vacuum infiltration was investigated in the present study. The B4C-Al composite materials were fabricated using [Ti+B4C] preforms preheated at 1700ºC for 1 h and Al alloys infiltrated in vacuum atmosphere at 1100ºC for 2 h. The phase composition indicated that TiB2 has high wettability to Al as a result of the preheating. SEM and EDX results revealed a number of Al dimples are on the fracture surface due to the existence of TiB2. When the content of added Ti increases to 30%, the [Ti+B4C] preform is characterized by a minimal porosity (33.11%) and a maximal density, a corresponding amount of residual Al of 33.11% and a minimal fracture toughness (5.03 MPa·m1/2) with a hardness of up to 63 HRC. The residual Al and the mechanical properties of the composite material preform were determined by the Ti content of the preform.

Zbadano wpływ dodatku tytanu na resztkową zawartość Al i właściwości mechaniczne kompozytów B4C-Al wytworzonych przez infiltrację próżniową. Kompozyty B4C-Al lzostały wytworzone przez infiltrację stopów Al, w próżni, w 1100ºC przez 2 godziny, do wstępnie wygrzanych w 1700ºC przez 1 godzinę preform [Ti+B4C]. Faza TiB2 charakteryzuje się wysoką zwilżalnością przez Al na skutek wstępnego wygrzania. Wyniki analizy SEM i EDX ujawniły pewną liczbę wgłębień Al znajdujących się na powierzchni pęknięcia z uwagi na obecność TiB2. Gdy zawartość dodanego Ti wzrasta do 30%, preforma [Ti+B4C] charakteryzuje się minimalną porowatością (33,11%) i maksymalną gęstością, odpowiednią ilością resztkowego Al tj. 33.11%, minimalną odpornością na kruche pękanie (5,03 MPa·m1/2), i twardością do 63 HRC. Resztkowe Al i właściwości mechaniczne materiału kompozytowego preformy determinowane są przez zawartość Ti w preformie.

The effect of Ti addition on the microstructure and fracture toughness of BN-Al composite materials synthesized by vacuum infiltration

Chao W, Xiangxin X, Xiaozhou C, He Y, Gongjin Ch

Archives of Metallurgy and Materials

2013

Vol. 58, iss. 2

509--512

In this paper, we studied the effect of Ti addition on the microstructure and fracture toughness of Boron nitride- Aluminum (BN-Al) composite materials that were synthesized by vacuum infiltration. The BN-Al composite materials were fabricated by preheating the [Ti+BN] preforms at 1700º for 1 hour before Al alloys were infiltrated into the preforms in a vacuum atmosphere at 1100º for 2 hours. X-ray diffraction (XRD) patterns showed that the diffraction peaks of titanium diboride (TiB2) appeared when the [Ti+BN] preforms were preheated. It is thought that metal Al protected are visible and this could be achieved by the generation of TiB2 when Al infiltrated into the preform from fractography. The matching fracture toughness of the [Ti+BN] preforms gradually improve when Ti content was increased.

W niniejszej pracy badano wpływ dodatku Ti na mikrostrukturę i odporność na pękanie kompozytów aluminium-azotek boru (BN-Al), które zostały zsyntetyzowane przez infiltracje w próżni. Kompozyty BN-Al zostały wykonane przez podgrzewanie preform [Ti+BN] w 1700ºC przez 1 godzinę, po czym stopy aluminium infiltrowano do preform w atmosferze próżni w temperaturze 1100ºC przez 2 godziny. Dyfrakcja rentgenowska (XRD) wykazała, że piki dyfrakcyjne diborku tytanu (TiB2) pojawiły się gdy preformy [Ti+BN] zostały podgrzane. Uważa się, że aluminium jest chronione co widoczne jest na przełomach i może to być osiągniete przez wytwarzanie TiB2 gdy Al przeniknęło do preformy. Odporność na pękanie preform [Ti+BN] stopniowo poprawia się, gdy zawartość Ti została zwiększona.