In situ cerium hexaaluminate platelets reinforcement of ED-machinable ZTA-TiC ceramics

Gommeringer A., Schmitt-Radloff U., Kern F., Gadow R

Materiały Ceramiczne

2017

T. 69, nr 1

4--9

Electrical discharge machinable ceramics open new applications fields by combining good mechanical properties such as high strength, hardness, abrasion resistance and high temperature resistance with the possibility to produce complex shape customized components. Alumina based ceramics with dispersions of zirconia and a conductive refractory carbide offer enhanced hardness and abrasion resistance compared to other ED-machinable ceramics based on silicon nitride or Y-TZP based compounds, however only a moderate toughness. In the present study cerium hexaaluminate (CA6) platelets were introduced in the material system of zirconia toughened alumina with 24 vol.% titanium carbide by in situ reaction sintering to further improve the fracture resistance. With addition of CA6 the fracture resistance and strength increases while hardness and electrical conductivity were incrementally reduced. CA6 addition leads to a slight reduction in material removal rate in die sinking EDM and reduction of roughness in machined surfaces.

Elektroerozyjnie obrabialna ceramika otwiera nowe pola zastosowań poprzez połączenie dobrych właściwości mechanicznych takich jak wysoka wytrzymałość, twardość, odporność na ścieranie i wysoka odporność temperaturowa z możliwością wytwarzania złożonego kształtu komponentów stosownie do wymagań klienta. Ceramika oparta na tlenku glinu zawierająca dyspersje tlenku cyrkonu i przewodzącego węglika ogniotrwałego oferuje podwyższoną twardość i odporność na ścieranie w porównaniu z pozostałą ceramiką obrabialną elektroerozyjnie opartą na azotku krzemu lub Y-TZP, ale jedynie umiarkowaną odporność na pękanie. W prezentowanych badaniach do układu materiałowego tlenku glinu wzmocnionego tlenkiem cyrkonu zawierającego 24% obj. węglika tytanu wprowadzono płytki sześcioglinianu ceru (CA6) drogą in situ spiekania reakcyjnego, aby poprawić odporność na pękanie. Wraz z dodatkiem CA6 zwiększyły się odporność na pękanie i wytrzymałość, podczas gdy twardość i przewodność elektryczna zostały przyrostowo zredukowane. Dodatek CA6 prowadzi do nieznacznego zmniejszenia szybkości usuwania materiału w trakcie elektrodrążenia wgłębnego EDM i redukcji chropowatości obrabianej powierzchni.

Electrical discharge machinable alumina zirconia niobium carbide composites - Influence of stabilizer content

Schmitt-Radloff U., Kern F., Gadow R.

Materiały Ceramiczne

2017

T. 69, nr 3

272--278

Manufacturing of customized components of hard and tough structural ceramics by conventional technologies suffers from high cost in the final hard machining step. Electric discharge machining can be a cost efficient alternative as the machining process is contact-free and thus material removal becomes independent on mechanical properties. To be ED-machinable, ceramics require a certain electrical conductivity, which can be achieved by addition of an electrically conductive phase. In this study materials containing a micron-size conductive dispersion of 24 vol.% of niobium carbide in a sub-micron-size matrix of zirconia toughened alumina containing 17 vol.% of zirconia of various yttria stabilizer contents were studied. Starting powders were alloyed by a mixing and milling process in 2-propanol and samples were produced by subsequent hot pressing at 1525 °C for 2 h at 40 MPa axial pressure in a graphite die. Mechanical properties, microstructure and phase composition were studied. The ED-machinability in a wire cutting process was investigated with respect to machining speed, surface quality and ED-induced subsurface damage. It was found that yttria stabilizer content affects mechanical properties. A maximum fracture resistance was found at a stabilizer content of 1 mol.% while bending strength varied little with stabilizer content. ED-machinability was unaffected by stabilizer content.

Wysokie koszty finalnej obróbki skrawaniem negatywnie oddziałują na wytwarzanie na zamówienie komponentów z twardej i wytrzymałej ceramiki konstrukcyjnej za pomocą tradycyjnych technologii. Obróbka elektroerozyja może stanowić kosztowo efektywną alternatywę, ponieważ proces obróbki jest bezkontaktowy i dlatego usuwanie materiału staje się niezależne od właściwości mechanicznych. Aby być obrabialną elektroerozyjnie, ceramika wymaga pewnej przewodności elektrycznej, którą można osiągnąć poprzez dodanie fazy przewodzącej elektrycznie. W niniejszej pracy badano materiały zawierające przewodzącą dyspersję węglika niobu w ilości 24% obj. w submikronowej osnowie tlenku glinu wzmacnianego tlenkiem cyrkonu, która zawierała 17% obj. tego tlenku z różną zawartością stabilizatora. Wyjściowe proszki homogenizowano drogą mieszania i mielenia w 2-propanolu, a próbki wytwarzano poprzez następcze prasowanie na gorąco w 1525 °C przez 2 h pod jednoosiowym ciśnieniem 40 MPa w formie grafitowej. Zbadano właściwości mechaniczne, mikrostrukturę i skład fazowy. Obrabialność elektroerozyjną w procesie cięcia włóknem badano w odniesieniu do szybkości obróbki, jakości uzyskanej powierzchni i podpowierzchniowego uszkadzania, wywołanego obróbką elektroerozyjną. Stwierdzono, że zawartość stabilizatora w postaci tlenku itru oddziałuje na właściwości mechaniczne. Maksymaną odporność na pękanie stwierdzono przy udziale stabilizatora wynoszącym 1% mol., podczas gdy wytrzymałość na zginanie zmieniała się nieznacznie wraz z zawartością stabilizatora. Obrabialność elektroerozyjna nie zależała od zawartości stabilizatora.