Polyols from recycled poly(ethylene terephthalate) flakes and rapeseed oil for polyurethane foams

Paberza A., Fridrihsone-Girone A., Abolins A., Cabulis U.

Polimery

2015

T. 60, nr 9

572--578

Bio/recycled polyols from rapeseed oil (RO) and poly(ethylene terephthalate) (PET) were prepared using a continuous, two-step synthesis method. The bio/recycled polyol properties were compared to RO and commercially available PET based polyols. Rigid polyurethane foams with a unified apparent density of 40—45 kg/m3 were prepared from these polyols. The thermal conductivity, thermal properties, water absorption and mechanical properties of foams were tested. The results indicated that the RO/PET polyols can be successfully used for preparing polyurethane foams as energy efficient thermal insulation material.

Otrzymano biorecyklowane poliole z oleju rzepakowego i poli(tereftalanu etylenu), na drodze ciągłej dwuetapowej syntezy. Porównano ich właściwości z właściwościami poliolu uzyskanego z oleju rzepakowego i dostępnego w handlu poliolu na bazie poli(tereftalanu etylenu). Z syntetyzowanych polioli wytworzono sztywne pianki poliuretanowe o gęstości pozornej w zakresie 40—45 kg/m3 . Oznaczono przewodność cieplną, właściwości termiczne, chłonność wody oraz właściwości mechaniczne otrzymanych pianek. Uzyskane wyniki wskazują, że poliole zsyntetyzowane z oleju rzepakowego i poli(tereftalanu etylenu) mogą być stosowane do produkcji pianek poliuretanowych przeznaczonych do celów termoizolacyjnych.

Wheat straw lignin as filler for rigid polyurethane foams on the basis of tall oil amide

Paberza A., Cabulis U., Arshanitsa A.

Polimery

2014

T. 59, nr 6

477--481

Rigid polyurethane (PUR) foams with the apparent density in the range of 45—60 kg/m 3 were produced from tall oil polyol (TOP) and organosolv wheat straw lignin as filler. PUR foams were filled with lignin in the amount of 0—6.3 wt %. Mechanical properties, dimensional stability, water absorption and thermal conductivity of prepared foams were investigated. The use of lignin increased the content of renewable materials in the end product, reaching together with TOP the value of 23.6 wt %. The viscosity of polyol system and foaming process parameters (cream time, gel time, tack-free time and full rise time) were determined. The viscosity of polyol system rose exponentially when concentration of lignin in the PUR foam was increased. The maximum value of compressive strength (0.35 MPa parallel to the foaming direction) was reached in the PUR sample where the concentration of lignin in foam was 1.2 wt %. It was concluded that wheat straw lignin can be used as a filler to obtain rigid PUR foams having the characteristics of thermal insulation material.

Stosując poliol z oleju talowego (TOP) oraz ligninę ze słomy pszenicznej jako napełniacz otrzymano sztywne pianki poliuretanowe (PUR) o gęstości pozornej 45—60 kg/msub>3. Wyznaczono właściwości mechaniczne, stabilność wymiarową, chłonność wody oraz współczynnik przewodzenia ciepła przygotowanych materiałów w zależności od zawartości ligniny (0—6,3 % mas.). Wprowadzenie ligniny spowodowało zwiększenie udziału surowców odnawialnych w końcowym produkcie, które razem z TOP osiągają 23,6 % mas. W ramach pracy wyznaczono lepkość przedmieszki poliolowej oraz parametry technologiczne procesu spieniania (czas startu, czas żelowania, czas wzrostu, oraz czas suchego lica). Lepkość przedmieszki poliolowej wzrastała wykładniczo wraz ze zwiększaniem zawartości ligniny. Największą wytrzymałość na ściskanie (0,35 MPa w kierunku równoległym do wzrostu pianki) otrzymano w przypadku pianki PUR o zawartości ligniny 1,2 % mas. Stwierdzono, że lignina ze słomy pszenicznej może być użyta jako napełniacz w procesie otrzymywania sztywnych pianek PUR mających cechy materiałów termoizolacyjnych.