Microstructure and mechanical properties of HR3C austenitic steel after service

Golański G., Kolan C., Zieliński A., Klimaszewska K., Merda A., Sroka M., Kłosowicz J.

Archives of Materials Science and Engineering

2016

Vol. 81, nr 2

62--67

Purpose: The purpose of the investigations was to determine changes in the microstructure and mechanical properties of HR3C creep resisting austenitic steel after service. Design/methodology/approach: The investigations were performed on test specimens taken from a part of the steam superheater tube. The range of the investigations included: microstructural investigations - light and SEM microscope; analysis of precipitates - carbide isolates; investigations of mechanical properties - hardness measurement, static tensile test, impact test. Findings: The precipitation processes at the grain boundaries lead to increase in intergranular corrosion of the HR3C steel resulting in loss of grains in the structure. The impact strength testing on test specimens with reduced width may result in overestimation of crack resistance of the material after service. Research limitations/implications: The comprehensive analysis of precipitation processes requires TEM examinations. Finding the correlation between the impact strength determined on standard vs. non-standard test specimens with reduced width. Practical implications: The obtained results of investigations are used in industrial practice for diagnosis of pressure parts of power boilers. Test procedures developed based on comprehensive materials testing conducted under laboratory conditions are used in upgrading and design of pressure parts of steam boilers. The results of investigations are also the element of database of the materials characteristics of steels and alloys as well as welded joints made of them working under creep conditions developed by the Institute for Ferrous Metallurgy. Originality/value: The results and analysis of the investigations of microstructure and mechanical properties of HR3C steel after service under actual boiler conditions are presented.