Polyols from recycled poly(ethylene terephthalate) flakes and rapeseed oil for polyurethane foams

Paberza A., Fridrihsone-Girone A., Abolins A., Cabulis U.

Polimery

2015

T. 60, nr 9

572--578

Bio/recycled polyols from rapeseed oil (RO) and poly(ethylene terephthalate) (PET) were prepared using a continuous, two-step synthesis method. The bio/recycled polyol properties were compared to RO and commercially available PET based polyols. Rigid polyurethane foams with a unified apparent density of 40—45 kg/m3 were prepared from these polyols. The thermal conductivity, thermal properties, water absorption and mechanical properties of foams were tested. The results indicated that the RO/PET polyols can be successfully used for preparing polyurethane foams as energy efficient thermal insulation material.

Otrzymano biorecyklowane poliole z oleju rzepakowego i poli(tereftalanu etylenu), na drodze ciągłej dwuetapowej syntezy. Porównano ich właściwości z właściwościami poliolu uzyskanego z oleju rzepakowego i dostępnego w handlu poliolu na bazie poli(tereftalanu etylenu). Z syntetyzowanych polioli wytworzono sztywne pianki poliuretanowe o gęstości pozornej w zakresie 40—45 kg/m3 . Oznaczono przewodność cieplną, właściwości termiczne, chłonność wody oraz właściwości mechaniczne otrzymanych pianek. Uzyskane wyniki wskazują, że poliole zsyntetyzowane z oleju rzepakowego i poli(tereftalanu etylenu) mogą być stosowane do produkcji pianek poliuretanowych przeznaczonych do celów termoizolacyjnych.

Characterization of polyurethane networks based on rapeseed oil derived polyol

Fridrihsone-Girone A., Stirna U.

Polimery

2014

T. 59, nr 4

333--338

Bio-based rapeseed oil (RO) polyol was synthesized by transesterification with triethanolamine. Synthesized RO/triethanolamine ester was modified with triethylene glycol (TEG) to obtain a polyol system with higher hydroxyl value, as well as with e-caprolactone (CL) to increase the carbon chain length and decrease the hydroxyl value. From these polyols there were synthesized polyurethane (PU) networks which showed good mechanical properties. It was established that with increasing urethane groups concentration and increasing crosslinking, polyurethane networks showed higher modulus of elasticity (E) and tensile strength (s). Polyurethane networks also showed higher elongation at break (e) with decreasing urethane groups concentration and decreasing crosslinking.

Poliol z oleju rzepakowego (RO) otrzymano metodą transestryfikacji trietanoloaminą. Otrzymany ester RO/trietanoloamina modyfikowano glikolem trietylenowym (TEG), w celu uzyskania układu poliolowego o większej zawartości grup OH, lub e-kaprolaktonem (CL) w celu zwiększenia długości łańcucha węglowego i zmniejszenia zawartości grup OH. Z otrzymanych polioli syntezowano sieci poliuretanowe (PU), które charakteryzowały się dobrymi właściwościami mechanicznymi. Stwierdzono, że wraz ze wzrostem stężenia grup uretanowych i zwiększeniem usieciowania, sieci PU charakteryzują się większym modułem sprężystości (E) i większą wytrzymałością na rozciąganie (s). Wykazano również, że zmniejszenie usieciowania i zawartości grup uretanowych w sieciach poliuretanowych wpływa na zwiększenie wydłużenia przy zerwaniu (e).