Analysis of the influence of the dressing feed rate of a grinding wheel with sintered corundum on the surface roughness of AMS6308 steel after carburising in plunge grinding

• Autorzy: Habrat Witold , Sałata Marcin , Ordon Tomasz

Identyfikatory

DOI

10.17814/mechanik.2025.8-9.7

Warianty tytułu

PL

Analiza wpływu prędkości posuwu obciągania ściernicy z domieszką korundu spiekanego na chropowatość powierzchni stali AMS6308 po nawęglaniu w procesie szlifowania wgłębnego

• Języki publikacji: EN

Abstrakty

EN

The influence of the grinding wheel dressing speed on the surface roughness of AMS6308 steel after carburising during plunge grinding was investigated. A single-grain CVD diamond dresser and a grinding wheel with a 50% admixture of sintered corundum were applied. An increase in the dressing feed rate resulted in an increase in the surface roughness parameters after grinding.

PL

Badano wpływ prędkości obciągania ściernicy na chropowatość szlifowanej powierzchni stali AMS6308 po nawęglaniu podczas szlifowania wgłębnego. Zastosowano jednoziarnisty obciągacz słupkowy z diamentu CVD oraz ściernicę z 50% domieszką korundu spiekanego. Wzrost posuwu obciągania powodował wzrost parametrów chropowatości powierzchni po szlifowaniu.

Słowa kluczowe

EN

plunge grinding; carburising; single-grain dresser; surface roughness

PL

szlifowanie wgłębne; nawęglanie; obciągacz jednoziarnisty; chropowatość powierzchni

• Wydawca: Stowarzyszenie Inżynierów i Techników Mechaników Polskich
• Czasopismo: Mechanik
• Rocznik: 2025
• Tom: R. 98, nr 8-9
• Strony: 6--9
• Opis fizyczny: Bibliogr. 6 poz., rys., wykr.

Twórcy

autor

Habrat Witold

• Politechnika Rzeszowska, Rzeszów, Polska

• https://orcid.org/0000-0002-9010-8175

autor

Sałata Marcin

• Politechnika Rzeszowska, Rzeszów, Polska

• https://orcid.org/0000-0002-2338-4380

autor

Ordon Tomasz

• Pratt & Whitney Rzeszów S.A.

Bibliografia

• [1] R. Fularski i R. Filip, „The Effect of Chip Binding on the Parameters of the Case-Hardened Layer of Tooth Surfaces for AMS 6308 Steel Gears Processed by Thermochemical Treatment”, Materials 2021, Vol. 14, Page 1155, t. 14, nr 5, s. 1155, mar. 2021, doi: 10.3390/MA14051155.
• [2] A. Wojtyczka i B. Iżowski, „Microstructure and hardness of Pyrowear 53 steel after low-pressure vacuum carburizing at 921°C”, Advances in Manufacturing Science and Technology, t. 44, nr 4, s. 109-112, grudz. 2020, doi: 10.2478/AMST-2019-0020.
• [3] L. Wang, L. Yang, L. Wang, X. Tang, i G. Liu, „Influence mechanism of grinding surface quality of 20CrMnTi steel on contact failure”, Scientific Reports 2024 14:1, t. 14, nr 1, s. 1-11, cze. 2024, doi: 10.1038/s41598-024-64320-0.
• [4] J. Sawicki, B. Kruszyński, i R. Wójcik, „The influence of grinding conditions on the distribution of residual stress in the surface layer of 17crni6-6 steel after carburizing”, Advances in Science and Technology. Research Journal, t. 11, nr 2, s. 17-22, cze. 2017, doi: 10.12913/22998624/67671.
• [5] Habrat, W.F. “Effect of Bond Type and Process Parameters on Grinding Force Components in Grinding of Cemented Carbide”. Procedia Eng. 2016, 149, 122-129, https://doi.org/10.1016/j.proeng.2016.06.646.
• [6] Sałata, M.; Babiarz, R.; Kęcik, K. “Detection of Defects in Solid Carbide Cutting Tools During Creep-Feed Flute Grinding (CFG) Using Recurrence Analysis”. Materials 2025, 18, 2743 https://doi.org/10.3390/ma18122743

Uwagi

This study was supported by the Ministry of Education and Science under the Implementation Doctorates Project (4th edition - Doktorat Wdrożeniowy)