Diversification of Intermetallic Zn Phases Growth on Steel During Hot-Dip Galvanizing

• Autorzy: Węgrzynkiewicz S. , Jędrzejczyk D. , Szłapa I. , Hajduga M. , Boczkal S.

Identyfikatory

DOI

10.1515/amm-2016-0091

• Języki publikacji: EN

Abstrakty

EN

The steel substrate formed as the result of oxy-acetylene cutting (OAB) was treated differently - using: softening annealing, grinding and electro-polishing. Investigations were focused on the influence of additional processing on the structure and corrosion resistance of the deposited zinc coating. The hot - dip Zn galvanizing process was conducted in industrial conditions. Parameters were fixed: temperature 457 °C, dipping time 150 s. The coating thickness diversification dependent on the sub-surface steel structure was analysed and compared to the previous results. The correlation between conducted treatment and coatings morphology was determined.

Słowa kluczowe

EN

hot-dip zinc galvanizing; heat-affected zone; softening annealing; oxy-acetylene cutting

• Wydawca: Institute of Metallurgy and Materials Science of Polish Academy of Sciences ; Committee of Materials Engineering and Metallurgy of Polish Academy of Sciences
• Czasopismo: Archives of Metallurgy and Materials
• Rocznik: 2016
• Tom: Vol. 61, iss. 2A
• Strony: 515--520
• Opis fizyczny: Bibliogr. 18 poz., rys., tab.

Twórcy

autor

Węgrzynkiewicz S.

• BELOS-PLP S.A., 74. Gen. J. Kustronia Str., 43-300 Bielsko-Biała, Poland

autor

Jędrzejczyk D.

• University of Bielsko-Biała, 2 Willowa Str., 43-309 Bielsko-Biała, Poland

autor

Szłapa I.

• BISPOL S.A, 30 Towarowa Str., 43-300 Bielsko- Biała, Poland

autor

Hajduga M.

• University of Bielsko-Biała, 2 Willowa Str., 43-309 Bielsko-Biała, Poland

autor

Boczkal S.

• Institute of Non-Ferrous Metals, 19 Pilsudskiego Str., 32-050 Skawina, Poland

Bibliografia

• [1] PN -EN ISO 14713-2:2010 Powłoki cynkowe - Wytyczne i zalecenia dotyczące ochrony przed korozją konstrukcji ze stopów żelaza - Część 2: Cynkowanie zanurzeniowe.
• [2] J. Maćkowiak., N.R. Short, International Metals Reviews l, 1-19 (1979).
• [3] C. E. Jordan, A. R. Marder, Journal of Materials Scienc 32, 5593-5602 (1997).
• [4] K. Kurski, Cynkowanie ogniowe, WNT (1970).
• [5] N. Dreulle, P. Dreulle, J. C. Vacher, Metall 34, 834-838 (1980).
• [6] J. Pelerin, J. Hoffmann, V. Leroy, Metall 35, 879-873 (1981).
• [7] H. Woźnica, L. Baryła, Acta Metallurgica Slovaca 8, 355-360 (2002).
• [8] H. Woźnica, M. Michalik, Ochrona przed Korozją 11A, 157-163 (2002).
• [9] O. Kubaschewski, Iron-Binary Phase Diagrams, Springer- Verlag (1982).
• [10] P. B. Burton, P. Perrot, Phase Diagram of Binary Iron Alloys, American Society for Metals, Metal Park. OH, 459-466 (1993).
• [11] T. B. Massalski, Binary Alloy Phase Diagrams, ASM International (1990).
• [12] D. Kopyciński, Monograph, AG H Kraków (2006)
• [13] W. Wołczyński, E. Guzik, K. Kurzydłowski, J. Kloch, J. Janczak-Rusch, Archives of Metallurgy and Materials 50, 231-240 (2005).
• [14] PN -EN ISO - 1461:2011 Powłoki cynkowe nanoszone na wyroby stalowe i żeliwne metodą zanurzeniową - Wymagania i metody badań.
• [15] J. Sobieszczański, Spajanie, OWPW, Warszawa (2004).
• [16] S. Trela, Mechanik 12, 877-878 (2004).
• [17] PN -EN ISO 6507-1:2007 Metale - Pomiar twardości sposobem Vickersa - Część 1: Metoda badań.
• [18] PN -EN ISO 9227:2012 - Badania korozyjne w sztucznych atmosferach - Badania w rozpylonej solance.