The properties of (Pb_0.97Ba_0.03)[(Zr_0.98Ti_0.02)_1-zSn_z]O₃ ceramics with 0 < z < 0.08

• Autorzy: Brzezińska D. , Skulski R. , Wawrzała P. , Dercz G.

Identyfikatory

DOI

10.2478/amm-2013-0178

Warianty tytułu

PL

Właściwości ceramiki (Pb_0.97Ba_0.03)[(Zr_0.98Ti_0.02)_1-zSn_z]O₃ o wartościach 0 < z < 0,08

• Konferencja: Composites and Ceramic Materials - Technology, Application and Testing (13 ; 13-15.05.2013 ; Białowieża, Poland)
• Języki publikacji: EN

Abstrakty

EN

We present the results of obtaining and investigations of (Pb_1-x Ba_x )((Zr_1-yTi_y) _1-zSn_z )O₃ (PBZTS) ceramics with x =const =0.03, y =const=0.02, z =0, 0.02, 0.04, 0.06 and 0.08. Investigated compositions are close to rhombohedral-orthorhombic morphotropic phase boundary. Ceramic samples have been obtained by conventional ceramic technology from oxides PbO, ZrO₂, TiO₂, SnO₂ and barium carbonate BaCO₃. The calcined powders were crushed and next pressed into discs and sintered free sintering (FS) method. For such obtained samples the following investigations have been done: EDS, XRD, microstructure of fractured samples, dielectric measurements, P-Ehysteresis loops investigations at various temperatures.

PL

Przedstawiono wyniki badań ceramiki (Pb_1-x Ba_x )((Zr_1-yTi_y) _1-zSn_z )O₃ (PBZTS) dla stałych wartości parametrów ,v =0,03 i y =0,02 oraz z =0, 0,02, 0,04, 0,06 i 0,08. Badane składy PBZTS znajdują się w pobliżu granicy fazowej między fazami o romboedrycznej i ortorombowej deformacji komórek elementarnych. Ceramiczne próbki PBZTS zostały otrzymane z prostych tlenków PbO, ZrO₂, TiO₂, SnO₂ i węglanu baru BaCO₃. Proszki po kalcynacji zostały rozdrobnione, a następnie uformowano z nich wypraski i zagęszczono metodą swobodnego spiekania (FS). Dla otrzymanych próbek PBZT/PBZTS przeprowadzono badania EDS, XRD, badania mikrostruktury przełamów, badania podstawowych właściwości dielektrycznych, badania pętli histerezy w różnych temperaturach.

Słowa kluczowe

EN

PBZT ceramics; PBZTS ceramics; phase transitions; dielectric properties

PL

ceramika PBZT; ceramika PBZTS; przejście fazowe; właściwości dielektryczne

• Wydawca: Institute of Metallurgy and Materials Science of Polish Academy of Sciences ; Committee of Materials Engineering and Metallurgy of Polish Academy of Sciences
• Czasopismo: Archives of Metallurgy and Materials
• Rocznik: 2013
• Tom: Vol. 58, iss. 4
• Strony: 1377--1380
• Opis fizyczny: Bibliogr. 12 poz., rys., tab.

Twórcy

autor

Brzezińska D.

• University of Silesia, Faculty of Computer Science and Materials Science, Materials Science Department, 2 Śnieżna Str., 41-200 Sosnowiec, Poland

autor

Skulski R.

• University of Silesia, Faculty of Computer Science and Materials Science, Materials Science Department, 2 Śnieżna Str., 41-200 Sosnowiec, Poland

autor

Wawrzała P.

• University of Silesia, Faculty of Computer Science and Materials Science, Materials Science Department, 2 Śnieżna Str., 41-200 Sosnowiec, Poland

autor

Dercz G.

• Institute of Materials Science, 75 Pułku Piechoty 1a Str., 41-500 Chorzów, Poland

Bibliografia

• [1] R. Skulski, Diffused phase transitions in selected groups of ferroelectrics and relaxors, University of Silesia, Katowice 1999 (in Polish).
• [2] R. Skulski, E. G. Fesenko, Z. Surowiak, Ferroelectric Letters 28, 145-153 (2001).
• [3] R. Zachariasz, D. Bochenek, Arch. Metall. Mater. 54, 895-902 (2009).
• [4] D. Bochenek, R. Zachariasz, Arch. Metall. Mater. 54, 903-910 (2009).
• [5] T. Ikeda, J. Phys. Soc. Japan 14, 168-174 (1959).
• [6] G. Li, G. H. Haertling, Ferroelectrics 166, 31-45 (1995).
• [7] Z. Ujma, M. Adamczyk, J. Handerek, J. Eur. Ceram. Soc. 18, 2201-2007 (1998).
• [8] J. Handerek, M. Adamczyk, Z. Ujma, Ferroelectrics 233, 253-270 (1999).
• [9] D. Brzezińska, R. Skulski, P. Wawrzała, Arch. Metall. Mater. 56, 1243-1247 (2011).
• [10] D. Bochenek, R. Skulski, P. Wawrzała, D. Brzezińska, Ferroelectrics 418, 82-87 (2011).
• [11] T. Bongkarn, Ch. Thiangchit, Ferroelectrics 383, 78-83 (2009).
• [12] G. Shirane, Phys. Rev. 86, 219-227 (1952).