Tensile-tensile Fatigue Behavior of Multi-axial Warp-knitted Reinforced Composite

• Autorzy: Gao X. , Tao N. , Chen S. , Wang L. , Wu W.

Identyfikatory

DOI

10.5604/01.3001.0010.7800

Warianty tytułu

PL

Ocena właściwości mechanicznych i zmęczeniowych kompozytowych dzianin wieloosiowych

• Języki publikacji: EN

Abstrakty

EN

An experimental study was carried out on the fatigue behaviour of multi-axial warp-knitted fabric composites. Composite samples reinforced with multi-axial warp-knitted fabric/matrix were manufactured by the vacuum-assisted resin transfer moulding method. Tensile-tensile fatigue cycling was carried out at different load levels, and S-N curves, tensile stress-strain curve and stiffness degradation of the multi-axial composite samples were obtained. Finally post-fatigue tensile tests were done at a stress level of 75%, at the stages of 1/3N and 2/3N, and the equivalent residual strength and stiffness degradation were obtained.

PL

Dokonano oceny właściwości mechanicznych i zmęczeniowych kompozytowych dzianin wieloosiowych. Kompozyty wzmocnione dzianiną wieloosiową wytworzono przy zastosowaniu próżniowej metody formowania. Dokonano oceny zmęczenia materiału i właściwości wytrzymałościowych przy różnych poziomach obciążenia. Przedstawiono krzywe S-N, krzywą naprężenie-odkształcenie i degradację sztywności wieloosiowych próbek kompozytowych. Wykonano również testy zmęczenia materiału przy poziomie naprężenia 75%, w etapach 1/3N i 2/3N. Omówiono równoważną wytrzymałość szczątkową i degradację sztywności kompozytowych dzianin wieloosiowych.

Słowa kluczowe

EN

multi-axial warp-knitted fabric composite; fatigue behavior; S-N curve; equivalent residual strength

PL

kompozytowe dzianiny wieloosiowe; zmęczenie materiału; krzywa S-N; równoważna wytrzymałość resztkowa

• Wydawca: Sieć Badawcza Łukasiewicz - Łódzki Instytut Technologiczny
• Czasopismo: Fibres & Textiles in Eastern Europe
• Rocznik: 2018
• Tom: Vol. 26, no. 1 (127)
• Strony: 73--80
• Opis fizyczny: Bibliogr. 13 poz., rys., tab.

Twórcy

autor

Gao X.

• Inner Mongolia University of Technology, College of Light Industry and Textile, Inner Mongolia, Hohhot, 010051, China

autor

Tao N.

• Inner Mongolia University of Technology, College of Light Industry and Textile, Inner Mongolia, Hohhot, 010051, China

autor

Chen S.

• Inner Mongolia University of Technology, College of Light Industry and Textile, Inner Mongolia, Hohhot, 010051, China

autor

Wang L.

• Inner Mongolia University of Technology, College of Light Industry and Textile, Inner Mongolia, Hohhot, 010051, China

autor

Wu W.

• Inner Mongolia University of Technology, College of Light Industry and Textile, Inner Mongolia, Hohhot, 010051, China

Bibliografia

• 1. Stolyarov O, Quadflieg T, Gries T. Effects of fabric structures on the tensile properties of warpknitted fabrics used as concrete reinforcements. Text Res J. 2015; 85: 1934-1945.
• 2. Loendersloot R, Lomov SV Akkerman R. Carbon composites based on multiaxial multiply stitched preforms. Compos Part A-Appl S. 2006; 37:103-113.
• 3. Lomov SV, Belov EB, Bischoff T. Carbon composites based on multiaxial multiply stitched preforms. Part 1. Geometry of the preform. Compos Part A-Appl. S. 2002; 33: 1171-1183.
• 4. Shokrieh MM, Lessard LB. Progressive Fatigue Damage Modeling of Composite Materials, Part I: Modeling. J Compos Mater. 2000; 34: 1056 - 1080.
• 5. Ivanov DS, Lomov DS, Stepan V, Bogdanovich, AE, Karahan M,Verpoest I. A comparative study of tensile properties of non-crimp 3D orthogonal weave and multi-layer plain weave E-glass composites. Part 2: Comprehensive experimental results. Compos Part A-Appl. S. 2009; 40: 11441157.
• 6. Sun BZ, Yao Y, Jin LM, Gu BH. Finite element analyses of stress distributions of threedimensional angle-interlock woven composite subjected to three-point bending cyclic loading. J Text I. 2013; 104: 1186-1194.
• 7. Jin LM, Jin BC, Sun BZ, Gu BH. Comparisons of static bending and fatigue damage between 3D angle-interlock and 3D orthogonal woven composites. J Reinf Plast Comp. 2012; 31: 935-945.
• 8. Jin LM, Hu H, Sun BZ, Gu BH.Three-point bending fatigue behavior of 3D angle-interlock woven composite. J Compos Mater. 2012; 46: 883-894.
• 9. Sun BZ, Niu ZL, Jin LM, Zhang Y, Gu BH. Experimental investigation and numerical simulation of three-point bending fatigue of 3D orthogonal woven composite. J Tex I. 2012; 103: 1312-1327.
• 10. Zhao Q, Jin LM, Jiang LL, Zhang Y, Sun BZ, Gu BH. Experimental characterizations of bending fatigue of a four-step 3-D braided rectangular composite under different stress levels. J Reinf Plast Comp. 2011; 30: 1571-1582.
• 11. Jin L, et al., Tension–tension fatigue behavior of layer-to-layer 3-D angle-interlock woven composites. Mater Chem Phys. 2013; 140: 183-190.
• 12. Vallons K, Lomov SV, Verpoest I. Fatigue and post-fatigue behaviour of carbon/epoxy non-crimp fabric composites. Compos Part A-Appl. S. 2009; 40: 251-259.
• 13. Karahan M, et al., Fatigue tensile behavior of carbon/epoxy composite reinforced with non-crimp 3D orthogonal woven fabric. Compos Sci Technol. 2011; 71: 1961-1972.

Uwagi

PL

Opracowanie rekordu w ramach umowy 509/P-DUN/2018 ze środków MNiSW przeznaczonych na działalność upowszechniającą naukę (2018).