Rebounding process of moulding sands-thermal degradation of bentonite binding qualities

• Autorzy: Dańko R.
• Języki publikacji: EN

Abstrakty

EN

Problems related to a gradual degradation of binding qualities of montmorillonite, the main component of foundry bentonites, are presented in the paper. This degradation is caused by high temperatures originated from liquid metal influencing moulding sands. Laboratory measurements of an active binding agent content in classic moulding sands prepared with two types of bentonite and subjected to a controlled heating to high temperatures – were performed. These laboratory examinations were compared to industrial tests, in which a temperature distribution was being determined in several places in the thickness of the casting ingot mould for 24 hours from the moment of pouring liquid metal. On the basis of the performed examinations, the method allowing to determine optimal additions in the rebounding process of the tested bentonites was developed.

Słowa kluczowe

EN

mould production; bentonite sand; green sand; rebounding process

PL

masa formierska; masa bentonitowa; proces formowania

• Wydawca: Komisja Odlewnictwa Polskiej Akademii Nauk Oddział w Katowicach
• Czasopismo: Archives of Foundry Engineering
• Rocznik: 2010
• Tom: Vol. 10, iss. 1 spec.
• Strony: 233--236
• Opis fizyczny: Bibliogr 4 poz., rys., tab., wykr.

Twórcy

autor

Dańko R.

• Faculty of Foundry Engineering, AGH University of Science and Technology , Reymonta 23 str., 30-059 Kraków, Poland

Bibliografia

• [1] Lewandowski J.L., Dańko J., Dańko. R.: Selekcja mas zużytych w Odlewniach Polskich S.A. w Starachowicach. Przegląd Odlewnictwa Vol. 54, No 2, 2004, pp. 120-126.
• [2] Dańko J., Dańko R, Łucarz M. Processes and devices for reclamation of used moulding sands. Edited by Wydawnictwo Naukowe “Akapit”, Kraków 2007, s. 291.
• [3] Wdrożenie nowej konstrukcji i technologii form z mas samoutwardzalnych oraz mas bentonitowych w produkcji odlewów masywnych z żeliwa. Projekt celowy KBN nr 10 TO8 011 2000 C/5214. Kierownik J. Dańko.
• [4] Dańko J., Fedoryszyn A., Dańko R.: Badania przemysłowe odświeżania masy formierskiej w mieszarce wirnikowej MTI-500 w cyklu długookresowym. VII konferencja odlewnicza TECHNICAL 2004 : Nowa Sól 03.06–04.06 2004 r. s. 103–111.