Microstructure of V3Ga superconducting wire using high Ga content Ti-Ga/V precursor composite material

• Autorzy: Murakami S. , Matsuda K. , Kawabata T. , Hishinuma Y , Ikeno S.

Warianty tytułu

PL

Mikrostruktura nadprzewodzącego drutu V3Ga wytworzonego przy użyciu związku TiGa3 o wysokiej zawartości Ga

• Języki publikacji: EN

Abstrakty

EN

Our co-workers, Hishinuma et. al. have fabricated the V3Ga compound wire by a new process using a high Ga content Ti-Ga compound in order to improve the superconducting property of the wire. In this study, we investigated microstructures of this wire to clarify the existence of V3Ga phase. The different contrasts of the matrix, two V-Ga phases and Ti-Ga core were observed by SEM observation. Two V-Ga phases were also confirmed. The ratio of V to Ga for two V-Ga phases was respectively 3:1 and 6:5 according to the EDS result. And these two phases were confirmed as V3Ga and V6Ga5.

PL

Hishinuma i współpracownicy wytworzyli drut związku międzymetalicznego V3Ga przy użyciu nowej metody wykorzystującej związek międzymetaliczny Ti-Ga o wysokiej zawartości Ga celem poprawy właściwości nadprzewodzących drutu. Zbadaliśmy mikrostrukturę drutu, aby zweryfikować obecność fazy V3Ga. W trakcie badań SEM zaobserwowano zróżnicowany kontrast w osnowie oraz istnienie dwóch faz V-Ga i rdzenia T-Ga. Analiza EDS potwierdziła istnienie dwóch faz z układu V-Ga, w których stosunek V do Ga wynosi odpowiednio 3:1 i 6:5. Potwierdzono, ze te dwie fazy to V3Ga i V6Ga5.

Słowa kluczowe

EN

superconductor; Ti-Ga/V precursor composite material; V-Ga phase; TEM; microstructure

PL

drut nadprzewodzący; Ti-Ga/V materiał kompozytowy; faza V-Ga; TEM; mikrostruktura

• Wydawca: Institute of Metallurgy and Materials Science of Polish Academy of Sciences ; Committee of Materials Engineering and Metallurgy of Polish Academy of Sciences
• Czasopismo: Archives of Metallurgy and Materials
• Rocznik: 2013
• Tom: Vol. 58, iss. 2
• Strony: 325--326
• Opis fizyczny: Bibliogr. 5 poz., rys.

Twórcy

autor

Murakami S.

• Graduate School of Science and Engineering for Education, University of Toyama, Japan

autor

Matsuda K.

• Gaduate School of Science and Engineering for Research, University of Toyama, 3190 Gofuku, Toyama, Japan

autor

Kawabata T.

• National Institute for Fusion Science, Japan

autor

Hishinuma Y

• National Institute for Fusion Science, Japan

autor

Ikeno S.

• Hokuriku Polytechnic College, Japan

Bibliografia

• [1] T. Noda, T. Takeuchi, M. Fujita, J. Nucl. Mater. 329-333, 1590 (2004).
• [2] Y. Hishinuma, A. Kikuchi, Y. Iijima, T. Takeuchi, A. Nishimura, J. Japan Inst. Metals 71, 959 (2007).
• [3] Y. Hishinuma, A. Nishimura, A. Kikuchi, Y. Iijima, T. Takeuchi, TML Annual report 2006, 69 (2007).
• [4] Y. Hishinuma, A. Kikuchi, Y. Iijima, T. Takeuchi, A. Nishimura, J. Phys. Conf. Ser. 97, 012131 (2008).
• [5] Y. Hishinuma, A. Kikuchi, Y. Iijima, T. Takeuchi, M. Tomonaga, A. Nishimura, IEEE Trans. Appl. Supercond. 19, 2670 (2009).