Experimental study on fatigue damage of train K6 spring

• Autorzy: Huang H. , Ji S. , Huang G. , Qin X. , Shui G.

Warianty tytułu

PL

Badania eksperymentalne uszkodzeń zmęczeniowych w sprężynach wagonowych typu K6

• Języki publikacji: EN

Abstrakty

EN

Springs’ fatigue life and damage are key evaluation parameters for railway train bogies. Fatigue experiment on K6 bogie spring is carried out by digital display hydraulic pulse fatigue test device. Spring fatigue life is estimated by using nominal stress method. Based on the technology of ultrasound nondestructive test device, the relationship between accumulation of internal fatigue damage and cycle loading times is obtained. The results indicate that same batches of K6 springs have high reliability; spring material internal fatigue damage increases as cycle loading times.

PL

W artykule przedstawiono wyniki badań dotyczących zmęczenia sprężyn w podwoziach wagonowych. Analizie, przy pomocy hydraulicznego urządzenia testującego poddano sprężynę wagonową typu K6. Korzystając z badań ultradźwiękowych określono związek między tworzeniem się skupisk uszkodzeń wewnętrznych a cyklicznym obciążaniem.

Słowa kluczowe

EN

fatigue experiment; fatigue damage; ultrasonic nondestructive test; spring rigidity

PL

badanie zmęczenia; uszkodzenie zmęczeniowe; test ultradźwiękowy; twardość sprężyny

• Wydawca: Wydawnictwo SIGMA-NOT
• Czasopismo: Przegląd Elektrotechniczny
• Rocznik: 2013
• Tom: R. 89, nr 3b
• Strony: 131--133
• Opis fizyczny: Bibliogr. 6 poz., il., tab., wykr.

Twórcy

autor

Huang H.

• Institute of Engineering Mechanics, Beijing Jiaotong University, Beijing l00044 China

autor

Ji S.

• Institute of Engineering Mechanics, Beijing Jiaotong University, Beijing l00044 China

autor

Huang G.

• Institute of Engineering Mechanics, Beijing Jiaotong University, Beijing l00044 China

autor

Qin X.

• Qiqihar Railway Rolling Stock Co., Ltd. Qiqihar 161002 China

autor

Shui G.

• Institute of Engineering Mechanics, Beijing Jiaotong University, Beijing l00044 China

Bibliografia

• [1] R.K. Luo, W.J. Mortel, X.P. Wu. Fatigue failure investigation on anti-vibration springs, Engineering Failure Analysis, 16(2009), No.5, 1366-1378
• [2] D. Shiozawa, Y. Nakai, T. Murakami, H. Nosho. Observation of Fatigue Crack Propagation Behavior under Torsional Loading by Using Synchrotron Radiation Micro-CT Imaging. Procedia Engineering, 10 (2011), 1479-1484
• [3] B.R. Kumar, D.K. Bhattacharya, K.D. Swapan, S.G. Chowdhury. Premature fatigue failure of a spring due to Quelch cracks. Engineering Failure Analysis, 7(2000), No.5, 377-384
• [4] F. Takahashi, A. Tange, K. Ando. Effect of shot peening on fatigue limit of surface flawed samples. Fatigue and Fracture of Engineering Material and Structures, 31(2008), No.3, 242-250
• [5] B. Kaiser, B. Pyttel, C. Berger. VHCF-behavior of heli cal compression springs made of different materials. International Journal of Fatigue. 33(2011), No.1, 23-32
• [6] B. Koch, B. Skrotzki. Strain controlled fatigue testing of the metastable β-titanium alloy Ti-6.8Mo-4.5Fe-1.5Al (Timetal LCB). Materials Science & Engineering: A (Structural Materials: Properties, Microstructure and Processing). 528(2011), No.18, 5999-6005