Influence of a steel surface treatment on the wetting angle and free surface energy

• Autorzy: Lipa S. , Atraszkiewicz R. , Klimek L.

Identyfikatory

DOI

10.15199/28.2017.6.6

Warianty tytułu

PL

Wpływ obróbki powierzchni stali na kąt zwilżania i swobodną energię powierzchniową

• Języki publikacji: EN

Abstrakty

EN

This paper presents the influence of abrasive blasting of various grain sizes and types, electro-etching and heating in an argon-hydrogen atmosphere on the wettability and free surface energy of samples prepared steel strips. The choice of treatments was dictated by the surface preparation for hot-dip zinc-coating. It was shown that the surface abrasive that was blasted with silicon carbide by a 0.300-0.250 mm grain is of a hydrophobic nature. The surface electroetched at room temperature is at the edge of hydrophobicity and hydrophilicity. In contrast, the surfaces treated in the argon-hydrogen atmosphere may be considered to be hydrophilic. In summary, it can be concluded that the suitable choice of treatment has a favourable influence on the adhesive properties of the treated steel substrates, which should result in a solid and strong steel-zinc coating joint.

PL

Właściwe przygotowanie powierzchni dla procesu cynkowania ogniowego stanowi kluczowe zagadnienie poprawności i jakości wykonania tego procesu. Poza czystością powierzchni oraz stopniem jej rozwinięcia jest ważne określenie stopnia jej zwilżalności, co wpływa na jakość wytworzonych powłok cynkowych. W pracy przedstawiono wpływ obróbki strumieniowo-ściernej o różnej wielkości i rodzaju ziarna, elektro-trawienia i wygrzewania w atmosferze argon–wodór na zwilżalność i swobodną energię powierzchni próbek. Wybór sposobów obróbki był podyktowany przygotowaniem powierzchni pod cynkowanie ogniowe.

Słowa kluczowe

EN

free surface energy; abrasive blasting; electroetching; heating

PL

swobodna energia powierzchniowa; obróbka strumieniowo-ścierna; elektrotrawienie; wygrzewanie

• Wydawca: Wydawnictwo SIGMA-NOT
• Czasopismo: Inżynieria Materiałowa
• Rocznik: 2017
• Tom: Vol. 38, nr 6
• Strony: 285--289
• Opis fizyczny: Bibliogr. 10 poz., fig., tab.

Twórcy

autor

Lipa S.

• Institute of Materials Science and Engineering, Lodz University of Technology, Łódź

autor

Atraszkiewicz R.

• Institute of Materials Science and Engineering, Lodz University of Technology, Łódź

autor

Klimek L.

• Institute of Materials Science and Engineering, Lodz University of Technology, Łódź

Bibliografia

• [1] Sepper S., Peetsalu P., Saarna M., Mikli V., Kulu P.: Effect of hot dip galvanizing on the mechanical properties of high strength steels. Key Engineering Materials 604 (2014) 12÷15.
• [2] Pickering F. B.: Materials science and technology, constitution and properties of steels. Materials Science and Technology 7 (1991).
• [3] Arndt M., Duchoslav J., Steinberger R., Hesser G., Commenda C., Samek L., Arenholz E., Stifter D.: Nanoscale analysis of the influence of preoxidation on oxide formation and wetting behavior of hot-dip galvanized high strength steel. Corrosion Science 93 (2015) 148÷58.
• [4] Ming J. S., Li Y. P., Zhang Q. F.: Effects of structures of zinc/substrate interface on coating adhesion of hot-dip galvanized DP steels. Advanced Materials Research 887–888 (2014) 338÷444.
• [5] Manna M., Dutta M.: Improvement in galvanization and galvannealing characteristics of DP 590 steel by prior Cu or Cu–Sn flash coating. Surface and Coatings Technology 251 (2014) 29÷37.
• [6] Yang H., Zhang S., Li J., Liu X., Wang H.: Effect of strip entry temperature on the formation of interfacial layer during hot-dip galvanizing of presshardened steel. Surface and Coatings Technology 240 (2014) 269÷274.
• [7] Kania H., Liberski P., Podolski P., Gierek A.: Some aspects of improvements in hot-dip galvanizing technology. Inżynieria Materiałowa 2 (2004) 775÷782.
• [8] Płocińska M., Płociński T., Szawłowski J.: The Morphology of zinc coating obtained on armco iron with various plastic deformations. Inżynieria Materialowa 6 (2008) 784÷787.
• [9] Mardera A. R.: The Metallurgy of zinc-coated steel. Progress in Materials Science 45 (2000) 191÷271.
• [10] Gołębiowski M., Sobczyk-Guzenda A., Szymański W., Klimek L.: Influence of parameters of stream abrasive treatment of titanium surfaces on contact angle and surface free energy. Inżynieria Materiałowa 4 (2010) 978 ÷ 980.

Uwagi

Opracowanie ze środków MNiSW w ramach umowy 812/P-DUN/2016 na działalność upowszechniającą naukę (zadania 2017).