Accumulation of Fatigue Microdefects - Entropy Interpretation

• Autorzy: Szafran K. , Delas N.

Identyfikatory

DOI

10.2478/fas-2018-0010

• Języki publikacji: EN

Abstrakty

EN

The authors of the paper presented some of the models describing the process of micro-cracks’ development. In this study, the process of a selected model of micro-cracking was analyzed. In the model it was assumed that the damage to the material has some “thermodynamic properties” or rather universal properties inherent in most complex systems. In order to calculate the long-term fatigue strength properties of a structure, it is important to have a good understanding of the distribution parameters of the number of defects of different sizes. A model was built using the entropy principle, which is effectively used to test complex systems that are difficult to formalize. As a result of many experimental studies it was found that the development of fatigue damage is closely related to the process of plastic deformation of the material at the contact point of local defects. The results of computer calculations and simulations led to the conclusions presented in the final part of this paper.

Słowa kluczowe

EN

distribution of microcracks; entropy interpretation of microcracks; fatigue curve formula

• Wydawca: Wydawnictwa Naukowe Sieci Badawczej Łukasiewicz - Instytutu Lotnictwa
• Czasopismo: Fatigue of Aircraft Structures
• Rocznik: 2018
• Tom: Iss. 10
• Strony: 104--116
• Opis fizyczny: Bibliogr. 13 poz., wykr., wzory

Twórcy

autor

Szafran K.

• Institute of Aviation, Warsaw, Poland

autor

Delas N.

• National Aviation University, Kyiv, Ukraine

Bibliografia

• [1] Хорошун Л. П. 1998. Основы микромеханики повреждаемости материала. 1. Кратковременная повреждаемость // Прикл. механика. 34, № 10. - С. 120-127.
• [2] Kasyanov V., Szafran K., 2015 „Some hybrid models of subjective analysis In the theory of active systems”. Transactions of the Institute of Aviation. ISSN 0509-6669 240 Nr 3. pp. 27-31.
• [3] Ботвина Л. P. 1985. Автомодельность накоплення повреждаемости [Текст] / Г. И. Баренблатт // Пробл. прочности. - №12. - С. 17-24.
• [4] Cane B. J., Greenwood G. W. 1975, The Nucleation and Growth of Cavities in Iron during Deformation at Elevated Temperatures. - Met. Sci., 9, N2, p. 55-60, https://doi.org/10.1179/030634575790444405
• [5] Cheng A. S., Laind C. 1981. Fatigue life behavior of copper single crystals. Part II^ Model for crack nucleation in persistent slip bands. - Fatigue Eng. Mater. Struckt., 4, N4, p. 343-353.
• [6] Page R., Weertman J. R. 1980, Investigation of fatigue-induced grain boundary cavitation by small angle neutron scatterring. - Scr. Metall., 14, N7, p. 773-777.
• [7] Делас Н. И. 2012. Предельно гиперболический закон распределения в самоорганизованных системах [Текст] / Н. И. Делас, В. А. Касьянов // Восточно-евроропейский журнал передовых технологий. - №4/4 - С. 13-18.
• [8] Делас Н. И. 2012. Энтрпийно-энергетическая модель развития усталостных дефектов [Текст] / Н. И. Делас, В. А. Касьянов // Восточно-евроропейский журнал передовых технологий. - №5/7 - С. 38-45.
• [9] Kasyanov V. A., Szafran K., Goncharenko A., Shipitiak T., 2013 „Entropy Paradigm in the theory of Hierarchical Active Systems. Elements of Conflict Theory”. Transactions of the Institute of Aviation. № 5-6 (232-233). - pp. 115-128.
• [10] Шанявский А. А. 2003. Безопасное усталостное разрушение элементов авиаконструкций. Синергетика в инженерных приложения - Уфа, - 803 с.
• [11] Банников М. В. 2011. Экспериментальное исследование особенностей процесса генерации тепла в вершине усталостной трещины [Текст] / А.И. Терехина, О.А. Плехов // Вестник ПГТУ. Механика. - Пермь: Изд-во Перм. Гос. Техн. Ун-та, - №2. - С. 14-27.
• [12] Плехов О. А., 2009. Теоретическое и экспериментальное исследование диссипации энергии в процессе локализации деформации в железе [Текст] / О. Б. Неймарк // ПМТФ. - Т. 50, вып. 1. - С. 153-164.
• [13] Wiśniowski W., 2014, “Structure fatigue crack in the effect of acoustic load-case study”. Journal of KONES, 21(4), pp 243-248, DOI: 10.5604/12314005.1130520

Uwagi

PL

Opracowanie rekordu w ramach umowy 509/P-DUN/2018 ze środków MNiSW przeznaczonych na działalność upowszechniającą naukę (2019).