Influence of Processing Conditions on Crystal Structure of Bi6Fe2Ti3O18 Ceramics

Treść / Zawartość
Identyfikatory
Warianty tytułu
Języki publikacji
EN
Abstrakty
EN
Aim of the present research was to apply a solid state reaction route to fabricate Aurivillius-type ceramics described with the formula Bi6Fe2Ti3O18 (BFTO) and reveal the influence of processing conditions on its crystal structure. Pressureless sintering in ambient air was employed and the sintering temperatures were 850 and 1080 °C. It was found that the fabricated BFTO ceramics were multiphase ones. They consisted of two Bim+1Fem-3Ti3O3m+3 phases, namely the phase with m=5 (i.e. the stoichiometric phase) and m=4 (i.e. the phase with a reduced number of layers in the slab). Detailed X-ray diffraction patterns analysis showed that both phases adopted the same orthorhombic structure described with Fmm2 (42) space group. The ratio of weight fractions of the constituent phases (m=5): (m=4) was ~30:70.
Słowa kluczowe
Twórcy
  • University of Silesia, Institute of Technology and Mechatronics, 12 Żytnia Str, 41-200 Sosnowiec, Poland
autor
  • University of Silesia, Institute of Technology and Mechatronics, 12 Żytnia Str, 41-200 Sosnowiec, Poland
autor
  • University of Silesia, Institute of Technology and Mechatronics, 12 Żytnia Str, 41-200 Sosnowiec, Poland
autor
  • University of Silesia, Institute of Technology and Mechatronics, 12 Żytnia Str, 41-200 Sosnowiec, Poland
  • Pedagogical University, Institute of Engineering, 2 Podchorążych Str., 30-084 Kraków, Poland
autor
  • Pedagogical University, Institute of Physics, 2 Podchorążych Str., 30-084 Kraków, Poland
Bibliografia
  • [1] M. Krzhizhanovskaya, S. Filatov, V. Gusarov, P. Paufler, R. Bubnova, M. Morozov, D. Meyer, Anorg. Allg. Chem. 631, 1603 - 1608 (2005).
  • [2] N. A. Lomanova, M. I. Morozov, V. L. Ugolkov, V. V.Gusarov, Inorg. Mater. 42, 189 - 195 (2006).
  • [3] E. Jartych, M. Mazurek, A. Lisińska-Czekaj, D. Czekaj, Journal of Magnetism and Magnetic Materials 322, 51-55 (2010).
  • [4] A. Lisińska-Czekaj, Wielofunkcyjne materiały ceramiczne na osnowie tytanianu bizmutu, Wydawnictwo Gnome, Uniwersytet Śląski, Katowice 2012.
  • [5] A. Lisińska-Czekaj, D. Czekaj, Ferroelektryki o warstwowej strukturze perowskitopodobnej BWPT. W: Z.Surowiak (Red.) Elektroceramika ferroelektryczna, Wydawnictwo Uniwersytetu Śląskiego, Katowice (2004).
  • [6] A. Lisińska-Czekaj, Materials Science Forum 730-732, 100-104 (2013).
  • [7] A. Lisińska-Czekaj, D. Czekaj, Materials Science Forum 730-732, 76-81 (2013).
  • [8] K. Srinivas, P. Sarah, S.V. Suryanarayana, Bulletin of Materials Science 26, (2), 247-253 (2003).
  • [9] D. Zientara, M. Bućko, J. Polnar, Advances in Science and Technology 67, 164-169 (2010).
  • [10] M. Bućko, J. Polnar, J. Przewoźnik, J. Żukrowski, Cz. Kapusta, Advances in Science and Technology 67 170-175 (2010).
  • [11] http://www.crystalimpact.com/match
  • [12] 1http://www.fiz-karlsruhe.de
  • [13] http://www.icdd.com
  • [14] M. I. Morozov, V. V. Gusarov, Inorganic Materials 38, (7), 723-729 (2002).
  • [15] M. I. Morozov, N. A. Lomanova, V. V. Gusarov, Russian J. Gen. Chem. 73 1676 - 1680 (2003).
  • [16] N. A. Lomanova, V. V. Gusarov, Russian Journal of Inorganic Chemistry 56, (4), 616-620 (2011).
  • [17] H.M.Rietveld, Austr. J. Phys. 41, (2) 113-116 (1988).
  • [18] A. Lisińska-Czekaj, D. Czekaj, Archives of Metallurgy and Materials 54, (4) 870-874 (2009).
  • [19] A. Lisińska-Czekaj, D. Czekaj, Z. Surowiak, J. Ilczuk, J. Plewa, A.V. Leyderman, E.S. Gagarina, A.T. Shuvaev, E.G. Fesenko, Journal of the European Ceramic Society 24, 947-951 (2004).
Typ dokumentu
Bibliografia
Identyfikator YADDA
bwmeta1.element.baztech-f038215d-09bf-43ff-ac52-81107c3af73d
JavaScript jest wyłączony w Twojej przeglądarce internetowej. Włącz go, a następnie odśwież stronę, aby móc w pełni z niej korzystać.