Optimisation of the deoxidation degree and modification on the cast steel properties improvement at low temperature

• Autorzy: Sierant Z.

Warianty tytułu

PL

Optymalizacja stopnia odtleniania i modyfikacji na poprawę własności w niskich temperaturach

• Języki publikacji: EN

Abstrakty

EN

Industrial conditions of obtaining thick-walled and shaped castings intended for operations at temperatures: minus 40÷60°C are presented in the paper. The selection of a cast steel grade is based on known studies [1,10,14], however due to castings wall thickness (70-240mm), the way of preparing liquid metal (deep deoxidation and modification, argon stirring in a ladle) and conditions of filling mould cavities (gating system assuring quiet filling, directional solidification and avoiding a formation of inessential heat centres), were developed to assure the required impact strength. Maintaining these parameters as well as the selection of heat treatments for the produced massive castings allowed to achieve the impact strength over 50 J/cm₂ at minus 40°. This value was obtained for walls of various thickness.

PL

Przedstawiono przemysłowe warunki otrzymywania grubościennych i kształtowych odlewów, przeznaczonych do pracy w temperaturze minus 40÷60°. Dobór gatunku staliwa oparto o znane prace [1,10,14], jednak ze względu na grubość ścianek odlewów (70-240 mm), opracowano sposób przygotowania ciekłego metalu (głębokie odtlenianie i modyfikacja, argonowanie w kadzi) oraz warunki zapełnienia wnęki formy (układ wlewowy zapewniający spokojne wypełnianie, kierunkowe krzepnięcie i unikanie tworzenia zbędnych węzłów cieplnych), dla zapewnienia wymaganej udarności. Zachowanie tych parametrów jak również dobór obróbki cieplnej dla produkowanych masywnych odlewów, pozwoliły na uzyskanie udarności w minus 40° wynoszącej powyżej 50 J/cm₂. Wartość tą otrzymano dla ścianek o różnej grubości.

Słowa kluczowe

EN

steel castings; minus temperatures; wall thickness

PL

odlewy stalowe; niskie temperatury; grubość ścianki

• Wydawca: Institute of Metallurgy and Materials Science of Polish Academy of Sciences ; Committee of Materials Engineering and Metallurgy of Polish Academy of Sciences
• Czasopismo: Archives of Metallurgy and Materials
• Rocznik: 2013
• Tom: Vol. 58, iss. 3
• Strony: 763--767
• Opis fizyczny: Bibliogr. 17 poz., rys., tab.

Twórcy

autor

Sierant Z.

• Metalodlew S. A., ul. Ujastek 1, 31-752 Kraków, Poland

Bibliografia

• [1] M. M. Salama, Low-Temperature Properties of Structural Steels, Materials Handbook, ASm International 1, 662-672.
• [2] J. Głownia, R. Bujas, L. Młynarczyk, Wpływ obróbki cieplnej i odtleniania staliwa Mn-Ni na jego udarność, Przegląd Odlewnictwa, 1, 1-6 (1995).
• [3] Metale - Próba udarności sposobem Charpy’ego - Część 1: Metoda badania, PN-EN ISO 148-1-.
• [4] T. Wachelko, i inni, 51st World Foundry Congress, Lisbon, ref. nr 18.
• [5] B. Kalandyk, Wpływ węglików VC na udarność niskostopowego staliwa Mn-Ni, Przegląd Odlewnictwa 12, 566-570 (2007).
• [6] R. C. Voigtatal., Influence of Composition and Processing Variables on Mechanical Properties of As-cast C-Mn Cast Steels, AFS Trans. 98-26, 427-432.
• [7] Wittekopf - Giessereitechnik, 8, 267-270 (1988).
• [8] G. J. Roe, B. L. Bramfit, ASTM, Metals Handbook, 10 th 2 d, vol. 1.
• [9] J. Głownia, B. Kalandyk, Metallurgy and foundry engineering 30, 1 (2004).
• [10] P. Mandal at al., Development of cast high strength microalloyed steels, Inter J. of Cast Metals Research 17, 2, 89-93 (2004).
• [11] Ju.W. Grebujew, i in., Snizenije sebstoimosti stalnych otliwok za sczet legirowania wanadiem, Lit. Proizw., 5, 13-14 (2006).
• [12] H. Stuart, The properties and processing of Microalloyed HSLA Steels, JOM 43, 1, 35-40 (1991).
• [13] T. Gladman, The physical metallurgy of microalloyed steels, 1997.
• [14] Jackson, Michie, Low temperature impact properties of cast steel, 1956.
• [15] B. Kalandyk, Z. Sierant, S. Sobula, Optymalizacja mikrostruktury, granicy plastyczności i udarności staliwa weglowego dodatkiem wanadu, Przegląd Odlewnictwa, 3, 108-113 (2009).
• [16] K. Hübner, XII Konferencja Odlewnictwa Staliwa, 19-25, Kraków, 2000.
• [17] M. Kowalówka, Praca Doktorska, AGH, Kraków, 1984.