Równoosiowa i zorientowana mikrostruktura w żeliwie wysokochromowym
Języki publikacji
Abstrakty
It has been proved that an addition of boron carbide and shredded steel scrap introduced as an inoculants to the chromium white cast iron changes the microstructure of castings. The operation increases the number of crystallization nuclei of M7 C3 carbides. In this case the B4 C carbides act as substrates for the nucleation of M7 C3 (chromium carbides). Castings after B4 C inoculation have fine grain fracture surface. Primary precipitates of chromium carbide also appeared, lowering the mechanical properties of as-cast parts. Additionally, in order to increase the mechanical properties of chromium cast iron, unidirectional solidification was used. In this case, 0.3 wt. % cerium was used as inoculant.
W pracy wykazano, że wprowadzenie do żeliwa chromowego dodatków modyfikatora w postaci węglika B4 C oraz złomu stalowego w postaci rozdrobnionej powoduje zmianę struktury odlewu oraz właściwości wytrzymałościowych. Wprowadzenie B4 C zwiększa liczbę zarodków krystalizacji węglika chromu M7 C3. Struktura odlewu po zabiegu modyfikacji węglikiem boru charakteryzowała się drobnoziarnistym przełomem W pracy wyjaśniono problem pojawienia się pierwotnych wydzieleń węglika chromu w strukturze, które to węgliki wpływają na obniżenie właściwości wytrzymałościowych surowych odlewów. Dodatkowo w pracy zastosowano kierunkową krystalizację, w celu zwiększenia właściwości mechanicznych żeliwa chromowego. W tym przypadku jako modyfikatora użyto 0,3% mas. ceru.
Wydawca
Czasopismo
Rocznik
Tom
Strony
723--726
Opis fizyczny
Bibliogr. 19 poz., rys., tab.
Twórcy
autor
- AGH University of Science and Technology, Faculty of Foundry Engineering, Al. A. Mickiewicza 30, 30-059 Kraków, Poland
autor
- AGH University of Science and Technology, Faculty of Foundry Engineering, Al. A. Mickiewicza 30, 30-059 Kraków, Poland
autor
- AGH University of Science and Technology, Faculty of Foundry Engineering, Al. A. Mickiewicza 30, 30-059 Kraków, Poland
Bibliografia
- [1] Cz. Podrzucki, Cast Iron. ZG STOP Publication, Krakow 1991.
- [2] E. Guzik, Archives of Foundry Engineering Monograph 1M, Katowice (1-128) 2001.
- [3] J. R. David, Cast Irons. ASM Specialty Handbook, ASM Inter. Mater. Park, OH, 1996.
- [4] A. Studnicki, Archives of Foundry Engineering 10, 209-216 (2010).
- [5] D. Kopyciński, M. Kawalec, A. Szczęsny, R. Gilewski, S. Piasny, Archives of Metallurgy and Materials 58, 973-976 (2013).
- [6] D. Kopyciński, S. Piasny, Archives of Foundry Engineering 12, 57-60 (2012).
- [7] H. Chen, Z. Chang, J. Lu, H. Li n, Wear 166, 197-201 (1993).
- [8] M. Radulovic, M. Fiset, K. Peev, J. of Materials Science 29, 5085-5094 (1994).
- [9] P. Christodoulou, N. Calos, Materials Science and Engineering 301, 103-117 (2001).
- [10] C. Guo, P. M. Kelly, Materials Science and Engineering 352, 40-45 (2003).
- [11] A. Bedolla, R. Correa, J. G. Quezada, Materials Science and Engineering 398, 297-308 (2005).
- [12] G. Silman, E. Pamfilov, Metal Science and Heat Treatment 49, 405-410 (2007).
- [13] X. Zhi, J. Xing, H. Fu, B. Xiao, Materials Letters 62, 857-860 (2008).
- [14] W. Wołczyński, E. Guzik, W. Wajda, D. Jedrzejczyk, Archives of Metallurgy and Materials 57, 105-117 (2012).
- [15] M. Kawalec, Archives of Foundry Engineering 11, 111-116 (2011).
- [16] E. Guzik, D. Kopyciński, Metallurgical and Materials Transactions 37A, 3057-3068 (2006).
- [17] E. Guzik, D. Kopyciński, Archives of Metallurgy 41, 203-208 (1996).
- [18] J. Zhou, China Foundry 8/3, 337-349 (2011).
- [19] K. P. Bunin, J. N. Taran, Preparation of cast iron, Mietallurgizdat, Moscow 1972.
Typ dokumentu
Bibliografia
Identyfikator YADDA
bwmeta1.element.baztech-ec6f6723-6ccf-4a0d-b721-9a524c4396e1