Tem Observation Of Precipitate Structures In Al-Zn-Mg Alloys With Additions Of Cu/Ag

• Autorzy: Watanabe K. , Matsuda K. , Ikeno S. , Yoshida T. , Murakami S.

Identyfikatory

DOI

10.1515/amm-2015-0244

Warianty tytułu

PL

Obserwacje wydzieleń w stopach Al-Zn-Mg modyfikowanych Cu/Ag metodą mikroskopii TEM

• Języki publikacji: EN

Abstrakty

EN

Al-Zn-Mg alloy has been known as one of the aluminum alloys with the good age-hardening ability and the high strength among commercial aluminum alloys. The mechanical property of the limited ductility, however, is required to further improvement. In this work, three alloys, which were added Cu or Ag into the Al-Zn-Mg alloy, were prepared to compare the effect of the additional elements on the aging behavior. The content of Ag and Cu were 0.2at.% and the same as, respectively. Ag or Cu added alloy showed higher maximum hardness than base alloy. The particle shape and rod shape precipitates were observed in all alloys peak-aged at 423K. According to addition of Ag or Cu, the number density of the precipitates increased higher than that of base alloy.

PL

Al-Zn-Mg jest stopem, który można efektywnie poddawać procesowi utwardzania wydzieleniowego. Spośród różnorodnych stopów aluminium charakteryzuje się bardzo wysoką wytrzymałością mechaniczną, jednak jego ograniczona plastyczność jest cechą wymagającą poprawy. W toku prac przygotowano trzy stopy: stop bazowy Al-Zn-Mg oraz stopy zawierające dodatki Cu lub Ag, dla porównania wpływu tych dodatków na starzenie się materiału. Zawartość Ag i Cu wynosiła odpowiednio 0,2% at. Stopy z dodatkiem Ag lub Cu wykazywały większą twardość maksymalną w porównaniu ze stopem bazowym. We wszystkich stopach starzonych w temperaturze 423K obserwowano charakterystyczne wydzielenia, a ich koncentracja była odpowiednio większa dla stopów z dodatkiem Ag lub Cu.

Słowa kluczowe

EN

Al-Zn-Mg alloy; aging; precipitates; TEM; Cu and Ag addition

PL

stop Al-Zn-Mg; starzenie; wydzielenia; dodatek Cu i Ag

• Wydawca: Institute of Metallurgy and Materials Science of Polish Academy of Sciences ; Committee of Materials Engineering and Metallurgy of Polish Academy of Sciences
• Czasopismo: Archives of Metallurgy and Materials
• Rocznik: 2015
• Tom: Vol. 60, iss. 2A
• Strony: 977--979
• Opis fizyczny: Bibliogr. 7 poz., rys.

Twórcy

autor

Watanabe K.

• Graduate School of Science and Engineering for Education, University of Toyama, 3190 Gofuku, Toyama, 930-8555, Japan

autor

Matsuda K.

• Graduate School of Science and Engineering for Research, University of Toyama, Toyama, Gofuku, Toyama, 930-8555, Japan

autor

Ikeno S.

• Hokuriku Polytechnic College, 1289-1 Kawabari, Uozu, Toyama, 937-0856, Japan

autor

Yoshida T.

• Aisin Keikinzoku Co., Ltd. 12-3 Nagonoe, Imizu, Toyama, 934-8588, Japan

autor

Murakami S.

• Aisin Keikinzoku Co., Ltd. 12-3 Nagonoe, Imizu, Toyama, 934-8588, Japan

Bibliografia

• [1] E.A. Starke Jr, J.T. Staley, Aerospace Sci. 32, 131-172 (1996).
• [2] N. Ryum, Z. Metallkde 66, 338-345 (1975).
• [3] E. Salamci, Mater. Sci. Tech. 20, 859-863 (2004).
• [4] L.K. Berg, J. Gjonnes, V. Hansen, X.Z. Li, M. Knutson-Wedel, G. Waterloo, D. Schryvers, L.R. Wallenberg, Acta Mater. 49, 3443-3451 (2001).
• [5] J.K. Park, A.J. Ardel, Met. Trans. 14A, 1957 (1983).
• [6] J. Gjonnes, Chr. J. Simensen, Act Metal. 18, 881-890 (1970).
• [7] Yoshio Baba, J. Inst. Met. 4, 513-518 (1967).

Uwagi

PL

Opracowanie ze środków MNiSW w ramach umowy 812/P-DUN/2016 na działalność upowszechniającą naukę.