Evaluation of high-temperature corrosion on 13CrMo4-5 steel operated in the power industry

• Autorzy: Gwoździk M.
• Języki publikacji: EN

Abstrakty

EN

The paper presents results of studies of steel and the oxide layer formed during a long-term operation (t=130,000h) on 13CrMo4-5 steel at an elevated temperature (T=455°C). The oxide layer was studied on a surface and a cross-section at the inner site of the pipe (in the flowing medium – steam side). The paper contains results of studies such as: light microscopy, scanning electron microscopy, X-ray phase analysis.

Słowa kluczowe

EN

oxide layer; 13CrMo4-5 steel; SEM; XRD; LM

• Wydawca: Wydawnictwo Uniwersytetu Warmińsko-Mazurskiego w Olsztynie
• Czasopismo: Technical Sciences / University of Warmia and Mazury in Olsztyn
• Rocznik: 2018
• Tom: nr 21(4)
• Strony: 335--343
• Opis fizyczny: Bibliogr. 14 poz., rys., wykr.

Twórcy

autor

Gwoździk M.

• Instytut Inżynierii Materiałowej, Politechnika Częstochowska, al. Armii Krajowej 19, 42-201 Częstochowa

Bibliografia

• BRUNÉ W., TRZESZCZYŃSKI J., HALIŃSKI J. 2011. Remote diagnostics of main steam pipelines of power units. 13th Informative & Training Symposium. Maintenance of thermo-mechanical power equipment. Management of the Productive Assets of a Group of Power Plants, 91-95 (in Polish)
• DOBOSIEWICZ J., BRUNNÉ K. 2007. Ultrasonic measurement of oxides layer thickness on superheater coil inner surface. Energetyka, 6, 460-464 (in Polish)
• GAWRON P. 2014. Czystość wody kotłowej a uszkodzenia rur w rejonach przewężeń, na łukach oraz na odcinkach pochyłych. Dozór Techniczny, 3, 54-58 (in Polish)
• GWOŹDZIK M. 2011. Analiza zdefektowania warstw tlenkowych na stali X10CrMoVNb9- 1 długotrwale eksploatowanej w temperaturze 535oC. Inżynieria Materiałowa, 182 (4), 432-434 (in Polish)
• GWOŹDZIK M., Nitkiewicz Z. 2011. Charakterystyka odporności na zarysowanie warstwy tlenkowej powstałej na stali P91. Inżynieria Materiałowa, 182 (4), 435-438 (in Polish)
• GWOŹDZIK M. 2014. Mechanizm degradacji warstw tlenkowych na stalach długotrwale eksploatowanych w energetyce. Monograph No. 291, Copyright by Wydawnictwo Politechniki Częstochowskiej (in Polish)
• GWOŹDZIK M. 2016a. Analysis of Crystallite Size Changes in an Oxide Layer Formed on Steel Used in the Power Industry. Acta Physica Polonica A, 130 (4), 935-938.
• GWOŹDZIK M. 2016b. Structure Studies of Porous Oxide Layers Formed on 13CrMo4-5 Steels Long-Term Operated in the Power Industry. Technical Sciences, 19 (3), 257-266.
• KLEPACKI F., WYWROT D. 2010. Life of resuperheater coils exposed to the effects of low-emission combustion. 12th Informative & Training Symposium. Maintenance of thermo-mechanical power equipment. Upgrading power equipment to extend its operating period beyond 300.000 hours, 29-35 (in Polish)
• LAVERDE D., GOMEZ-ACEBO T., CASTRO F. 2004. Continuous and cyclic oxidation of T91 ferritic steel under steam. Corrosion Science, 46, 613-631.
• LELUSZ M. 2012. Ocena zawartości aktywnego SiO2 w popiołach lotnych wytwarzanych w obiektach energetycznych północno-wschodniej Polski. Civil and Environmental Engineering, 3, 179-184 (in Polish)
• PRISS J., ROJACZ H., KLEVTSOV I., DEDOV A., WINKELMANN H., BADISCH E. 2014. High temperature corrosion of boiler steels in hydrochloric atmosphere under oil shale ashes. Corrosion Science, 82, 36-44.
• ŚLIWA A. GAWRON P. 2009. Miedź w osadach w urządzeniach energetycznych – problem eksploatacyjny i remontowy. Dozór Techniczny, 2, 40-43 (in Polish)
• TRZESZCZYŃSKI J. 2010. Technical condition assessment of and life prediction for the critical components of thermo-mechanical power equipment intended to remain in service beyond 300 000 hours. 12th Informative & Training Symposium. Maintenance of thermomechanical power equipment. Upgrading power equipment to extend its operating period beyond 300.000 hours, 13-21 (in Polish)