Research on the Assessment of Selected Austenitic Stainless Steels Hot Crack Susceptibility

• Autorzy: Tuz L. , Pańcikiewicz K. , Tasak E. , Adamiec J. , Góral T.

Warianty tytułu

PL

Badania skłonności do pęknięć gorących wybranych stali austenitycznych

• Języki publikacji: EN

Abstrakty

EN

The article presents the results concerning hot crack susceptibility of selected steels having an austenitic structure. The tests were based on the analysis of the chemical composition of these steels and utilising special stations for the Transvarestraint tests and the Blanchet method. During the tests it was possible to observe cracks in the liquid-solid area. The results obtained indicate the existence of an area free from solidification cracks for a certain strain value at a pre-set welding rate. It was also possible to observe the absence of a distinct boundary between such areas, which was reflected in the crack length.

PL

W artykule przedstawiono wyniki oceny skłonności do pęknięć gorących wybranych stali o strukturze austenitycznej. Badania przeprowadzono w oparciu o analizę składu chemicznego tych stali oraz wykorzystując specjalne stanowiska dla próby Transvarestraint i metody Blancheta. Obserwowano występowanie pęknięć w obszarze ciekło stałym. Uzyskane wyniki wskazują na istnienie obszaru, gdzie przy pewnej wartości odkształcenia przy zadanej prędkości spawania, nie ma pęknięć krystalizacyjnych oraz obszaru ich występowania. Stwierdzono, że nie istnieje wyraźna granica pomiędzy tymi obszarami, co znajduje odzwierciedlenie w długości pęknięcia.

Słowa kluczowe

EN

hot cracking; austenitic steel; transvarestraint test; Blanchet method

PL

pękanie gorące; stal austenityczna; próba Transvarestraint; metoda Blancheta

• Wydawca: Sieć Badawcza Łukasiewicz - Górnośląski Instytut Technologiczny
• Czasopismo: Biuletyn Instytutu Spawalnictwa w Gliwicach
• Rocznik: 2014
• Tom: Vol. 58, No. 6
• Strony: 17--22
• Opis fizyczny: Bibliogr. 6 poz., rys., tabl.

Twórcy

autor

Tuz L.

• AGH University of Science and Technology in Cracow; Faculty of Metals Engineering and Industrial Computer Science;

autor

Pańcikiewicz K.

• AGH University of Science and Technology in Cracow; Faculty of Metals Engineering and Industrial Computer Science;

autor

Tasak E.

• AGH University of Science and Technology in Cracow; Faculty of Metals Engineering and Industrial Computer Science;

autor

Adamiec J.

• Silesia University of Technology, Faculty of Material Engineering and Metallurgy, Katowice, Poland;

autor

Góral T.

• AGH University of Science and Technology in Cracow; Faculty of Mechanical Engineering and Robotics

Bibliografia

• 1. Song K.H., Nakata K.: Effect of precipitation on post-heat-treated Inconel 625 alloy after friction stir welding. Materials and Design, 31 (2010), pp. 2942-2947.
• 2. Yenia C., Koc-akb M.: Fracture analysis of laser beam welded superalloys Inconel 718 and 625 using the fitnet procedure. International Journal of Pressure Vessels and Piping, 85 (2008), pp. 532-539.
• 3. Yilbas B.S., Akhtar S.S., Karatas C.: Laser surface treatment of Inconel 718 alloy: Thermal stress analysis. Optics and Lasers in Engineering, 48 (2010), pp. 740-749.
• 4. Pakieła Z.: Microstructure and mechanical properties of Inconel 625 superalloy. Obróbka Plastyczna Metali, vol. XXI, 3 (2010), pp. 143-154.
• 5. Huang C.A., Wang T.H., Han W.C, Lee C.H.: A study of the galvanic corrosion behavior of Inconel 718 after electron beam welding. Materials Chemistry and Physics, 104 (2007), pp. 293-300.
• 6. Tasak E., Ziewiec A.: Spawalność materiałów konstrukcyjnych Tom 1 Spawalność stali. Wydawnictwo JAK, Kraków 2009.

Uwagi

PL

Wersja polska artykułu w wydaniu papierowym s. 31--35.