Influence of alkaline solvents on the physical and mechanical properties of selected wood species

• Autorzy: Zduniak D. , Drożdżek M.

Warianty tytułu

PL

Zbadanie wpływu cieczy o zasadowym charakterze na właściwości fizyko-mechaniczne drewna wybranych gatunków

• Języki publikacji: EN

Abstrakty

EN

Three species of wood (larch, beech and red oak) were boiled in alkaline liquids. Wood species were divided into three groups for 30 samples each (the same average density and standard deviations). Samples were boiling in two types of liquids – seawater and black liquor. Time of boiling was always 20 hours. The density before and after treatment were measured also was investigated compressive strength parallel to grain after treatment. Native wood for each species was used as reference samples. Result show that wood samples density after treatment in seawater is a little smaller and after black liquid is bigger. Compressive strength parallel to fiber decrease after treatment in used alkaline liquids. The reason of this was probability smaller cracks inside wood and changes in chemical compositions of wood samples. Long time being in alkaline liquid with combination in drying process has negative influence of parameters of wood materials.

PL

Trzy gatunki drewna: modrzewia, buka oraz dębu czerwonego zostały poddane gotowaniu w cieczach o zasadowym charakterze. Gotowanie trwało 20 godzin i było prowadzone w wodzie morskiej oraz ługu czarnym. Grupy próbek do badań zostały dobrane zgodnie z gęstością (przy wilgotności W = 0%) tak, aby średnia gęstość i odchylenie standardowe w każdym zestawie były podobne. Na próbkach przed gotowaniem oraz po oznaczona została gęstość. Po procesie gotowania zbadano także wytrzymałość na ściskanie wzdłuż włókien. Próbki natywne zostały użyte, jako materiał odniesienia. Wszystkie poddano ściskaniu wzdłuż włókien na 4 tonowej maszynie Amslera. Na podstawie przeprowadzonych badań można wnioskować, że środowisko, w jakim przebywało drewno wpływa negatywnie na jego właściwości. Podniosła się gęstość, ale zmniejszyła się wytrzymałość na ściskanie wzdłuż włókien. Najmniejsze zmiany zaszły w przypadku drewna modrzewiowego. Prawdopodobnie jest to związane z żywicą która występuje naturalnie w tym gatunku.

Słowa kluczowe

EN

Black liquor; seawater; wood; compressive strength; density

PL

obróbka drewna; buk; dąb; gotowanie

• Wydawca: Wydawnictwo Szkoły Głównej Gospodarstwa Wiejskiego w Warszawie
• Czasopismo: Annals of Warsaw University of Life Sciences - SGGW. Forestry and Wood Technology
• Rocznik: 2018
• Tom: No. 103
• Strony: 77--83
• Opis fizyczny: Bibliogr. 12 poz., rys., tab.

Twórcy

autor

Zduniak D.

• Department of Wood Science and Wood Protection, Faculty of Wood Technology, Warsaw University of Life Science – SGGW

autor

Drożdżek M.

• Department of Wood Science and Wood Protection, Faculty of Wood Technology, Warsaw University of Life Science – SGGW

Bibliografia

• 1. BYTNER O., 2016: Analysis of chemical components of the black liquor from poplar's wood after kraft pulping, Warszawa.
• 2. EVANS P. D., 2008: Weathering and photoprotection of wood. In: Schultz TP, Militz H, Freeman MH, et al (eds) Development of commercial wood preservatives. American Chemical Society, Washington D.C., pp 69-120.
• 3. GREEN D. W., WMANDY J. E., KRETSCHMANN D.E., Mechanical Properties of Wood.
• 4. JOHNSON B. R., IBACH R. E., BAKER A. J., 1992: Effect of salt water evaporation on tracheid separation from wood surfaces. Forest Prod J 42:57-59.
• 5. JONES P. D., SHMULSKY R., KITCHENS S., BARNES M., 2011: What is salt killed wood Publication 2662. Extension Service of Mississippi State University.
• 6. KJRKER G.T., GLAESER J., LEBOW S. T., 2011: Physical deterioration of preservative treated poles and pilings exposed to salt water. U.S. Department of Agriculture, Forest Service, Forest Products Laboratory, Madison.
• 7. KRZYSIK F., 1974: Nauka o drewnie. WydawnictwoPWRiL Warszawa.
• 8. MORRELL J. J., HELSING G. G., GRAHAM R. D., 1984: Marine wood maintenance manual: a guide for proper use of Douglas-fir in marine exposures. Oregon State University, Forest Research Lab, Corvallis.
• 9. PARAMESWARAN N., 1981: Micromorphology of spruce timber after long-term service in a potash store house. HolzRoh-Werkst 39:149-156.
• 10. PONNETH D., VASU A., EASWARAN J., 2014: Destructive and non-destructive evaluation of seven hardwoods and analysis of data correlation. Holzforschung, 68(8), pp. 951-956. Retrieved 31 Jul. 2018, from doi:10.1515/hf-2013-0193.
• 11. Standards: PN-58/D-04102 standard, physical and mechanical properties of wood.
• 12. WILLIAMS R. S., 2005: Weathering of wood. In: Rowell RM (ed) Hand-book of wood chemistry and wood composites. CRC, Boca Raton.

Uwagi

Opracowanie rekordu ze środków MEiN, umowa nr SONP/SP/546092/2022 w ramach programu "Społeczna odpowiedzialność nauki" - moduł: Popularyzacja nauki i promocja sportu (2022-2023).