In this work, gel-casting of foams method was used to produce ZrO2 porous ceramics. The obtained foams with total porosity of 89.5 vol% were composed of approximately spherical cells having the mean diameter of 537 ± 153 μm interconnected by circular cell windows having the mean diameter of 152 ± 82 μm. Next, the ZrO2 foams were coated with fluorapatite (FA) and hydroxyapatite (HA) layers by slurry infiltration. The intermediate fluorapatite (FA) layer was introduced to prevent the chemical reactions between ZrO2 and HA at high temperatures during sintering process. The ZrO2 samples containing only HA coatings, were also tested, for comparison. The obtained ceramic biomaterials were subjected to in vitro tests in the simulated body fluid (SBF) solution. The results show that the ZrO2 foams with FA/HA layers possessed better bioactivity than the foams with the HA/HA coating.
Słowa kluczowe
Wydawca
Czasopismo
Rocznik
Tom
Strony
885--891
Opis fizyczny
Bibliogr. 23 poz., fot., rys., tab.
Twórcy
autor
- Rzeszów University of Technology, Faculty of Chemistry, 6 Powstańców Warszawy Str., 35-959 Rzeszów, Poland
autor
- Rzeszów University of Technology, Faculty of Chemistry, 6 Powstańców Warszawy Str., 35-959 Rzeszów, Poland
autor
- Institute of Power Engineering, Ceramic Department Cerel, 1 Techniczna Str., 36-040 Boguchwała, Poland
autor
- Institute of Power Engineering, Ceramic Department Cerel, 1 Techniczna Str., 36-040 Boguchwała, Poland
Bibliografia
- [1] A. Rapacz-Kmita, A. Ślósarczyk, Z. Paszkiewicz, J. Eur. Ceram. Soc. 26 (8), 1481-1488 (2006), DOI: 10.1016/j.jeurceramsoc.2005.01.059.
- [2] Y. Nayak, R. Rana, S. Pratihar, S. Bhattacharyya, Int. J. Appl. Ceram. Technol. 5 (1), 29-36 (2008), DOI: 10.1111/j.1744-7402.2008.02180.x.
- [3] C. Piconi,G. Maccauro, Biomaterials 20, 1-25 (1999), DOI: 10.1016/s0142-9612(98)00010-6.
- [4] H.-W. Kim, Y.-M. Kong, Y.-H. Koh, H.-E. Kim, H.-M. Kim, J. S. Ko, J. Am. Ceram. Soc. 86 (12), 2019-2026 (2003), DOI: 10.1111/j.1151-2916.2003.tb03602.x.
- [5] H.-W. Kim, H.-E. Kim, V. Salih, J. C. Knowles, J. Biomed. Mater. Res. A 68 (3), 522-530 (2004), DOI: 10.1002/jbm.a.20094.
- [6] H.-W. Kim, S.-Y. Leea, C.-J. Baea, Y.-J. Noha, H.-E. Kim, H.-M. Kim, J. S. Ko J. Biomaterials 24 (19), 3277-3284 (2003), DOI: 10.1016/S0142-9612(03)00162-5.
- [7] A. Bianco, I. Cacciotti, M. Lombardi, L. Montanaro, E. Bemporad, M. Sebastiani, Ceram. Int. 36 (1), 313-322 (2010), DOI: 10.1016/j.ceramint.2009.09.007.
- [8] P. Sepulveda, F. S. Ortega, M. D. M. Innocentini, V. C. Pandolfelli, J. Am. Ceram. Soc. 83 (12), 3021-3024 (2000), DOI: 10.1111/j.1151-2916.2000.tb01677.x.
- [9] P. Sepulveda, J. G. P. Binner, J. Eur. Ceram. Soc. 19 (12), 2059-2066 (1999), DOI: 10.1016/S0955-2219(99)00024-2.
- [10] M. D. M. Innocentini, P. Sepulveda, V. R. Salvini, V. C. Pandolfelli, J. Am. Ceram. Soc. 81 (12), 3349-3352 (1998), DOI: 10.1111/j.1151-2916.1998.tb02782.x.
- [11] M. Potoczek, R. E. Śliwa, Arch. Metall. Mater. 56 (4), 1265-1269 (2011), DOI: 0.2478/v10172-011-0145-2.
- [12] M. Potoczek, A. Zima, Z. Paszkiewicz, A. Ślósarczyk, Ceram. Int. 35 (6), 2249-2254 (2009), DOI: 10.1016/j.ceramint.2008.12.006.
- [13] H. Ghomi, M. H. Fathi, H. Edris, Mater. Res. Bull. 47 (11), 3523-3532 (2012), DOI: 10.1016/j.materresbull.2012.06.066.
- [14] M. D. M. Innocentini, R. K. Faleiros, R. Pisani, Jr., I. Thijs, J. Luyten, S. Mullens, J. Porous Mater. 17 (5), 615-627 (2010), DOI: 10.1007/s10934-009-9331-2.
- [15] I. Santacruz, R. Moreno, J. B. Rodrigues Neto, Int. J Appl. Ceram. Technol. 5 (1), 74-83 (2008), DOI: 10.1111/j.1744-7402.2008.02189.x.
- [16] J. Ligoda-Chmiel, M. Potoczek, R. E. Śliwa, Arch. Metall. Mater. 60 (4), 2757-2762 (2015), DOI: 10.1515/amm-2015-0444.
- [17] J. Ligoda-Chmiel, R. E. Śliwa, M. Potoczek, Compos. Part B Eng. 112, 196-202 (2017), DOI: 10.1016/j.compositesb.2016.12.041.
- [18] M. Potoczek, A. Chmielarz, M. D. M. Innocentini, I. C. P. da Silva, P. Colombo, B. Winiarska, J. Am. Ceram. Soc. 101 (12), 5346-5357 (2018), DOI: 10.1111/jace.15802.
- [19] E. Adolfsson, J. Am. Ceram. Soc. 89 (6), 1897-1902 (2006), DOI: 10.1111/j.1551-2916.2006.01040.x.
- [20] T. Kokubo, H. Takadama, Biomaterials 27, 2907-2915 (2006), DOI: 10.1016/j.biomaterials.2006.01.017.
- [21] K. Vajravelu, K. V. Prasad, P. S. Datti, B. T. Raju, Ain Shams Eng. J. 5, 157-167 (2014), DOI: 10.1016/j.asej.2013.07.009.
- [22] H.-W. Kim, B.-H. Yoon, Y.-H. Koh, H.-E. Kim, J. Am. Ceram. Soc. 89 (8), 2466-2472 (2006), DOI: 10.1111/j.1551-2916.2006.01114.x.
- [23] N. S. Sambudi, S. Cho, K. Cho, RSC Adv. 6 (6), 43041-43048 (2016), DOI: 10.1039/C6RA03147A
Uwagi
EN
1. Financial support from Rzeszów University of Technology (DS.CM.19.001) is gratefully acknowledged.
PL
2. Opracowanie rekordu ze środków MNiSW, umowa Nr 461252 w ramach programu "Społeczna odpowiedzialność nauki" - moduł: Popularyzacja nauki i promocja sportu (2020).
Typ dokumentu
Bibliografia
Identyfikator YADDA
bwmeta1.element.baztech-da6cbf87-8ccb-4322-9792-87a23c74325e