Performance Stability of Ballistic Para-Aramid Woven Fabrics Modified by Plasma-Assisted Chemical Vapour Deposition (PACVD)

• Autorzy: Struszczyk M. H. , Puszkarz A. K. , Miklas M. , Wilbik-Hałgas B. , Cichecka M. , Urbaniak–Domagała W. , Krucińska I.

Identyfikatory

DOI

10.5604/12303666.1201137

Warianty tytułu

PL

Stabilność cech użytkowych balistycznych tkanin modyfikowanych przy zastosowaniu techniki plazmy niskotemperaturowej (PACVD)

• Języki publikacji: EN

Abstrakty

EN

Plasma-assisted chemical vapour deposition (PACVD) is often used for the modification of the surface properties of a wide range of materials. The resulting effect of PACVD modification considerably changes the behaviour of the material. The process of surface modification by PACVD of a textile is significantly complex due to the topography resulting in the fabric structure. Taking ecology and economy into account, PACVD modification is more efficient as compared with traditional finishing processes. However, the stability of the PACVD effect gets lost during usage of the textile under standard conditions. The aim of the research was to verify in an enhanced accelerated ageing test the stability of PACVD modification of para-aramid woven fabrics applied for designing of soft ballistic inserts in body protectors. The simulated ageing yielded a significant change in the mechanical properties of non-modified textiles, whereas PACVD-modified samples showed prolonged stability of the properties obtained.

PL

Technika plazmy niskotemperaturowej (PACVD) jest często stosowana do modyfikacji właściwości powierzchni szerokiej gamy materiałów. Uzyskany efekt modyfikacji PACVD zmienia znacznie zachowanie się materiału. Proces modyfikacji PACVD wyrobów włókienniczych jest bardziej złożony ze względu na topografię wynikająca z ich struktury. Biorąc pod uwagę aspekty ekologii i ekonomii, modyfikacja PACVD jest bardziej efektywna, w porównaniu do tradycyjnych procesów wykończeniowych. Jednakże uzyskany efekt jest tracony w czasie użytkowania wyrobów włókienniczych w warunkach standardowych. Celem prowadzonych badań była weryfikacja w czasie przyspieszonego starzenia stabilności modyfikacji PACVD tkaniny ar amidowej stosowanej do projektowania miękkich wkładów balistycznych. W wyniku symulacji starzenia niezmodyfikowane tekstylia traciły swoje właściwości użytkowe szybciej niż w przypadku próbek modyfikowanych PACVD.

Słowa kluczowe

EN

para-aramid ballistic woven fabrics; PACVD; accelerated ageing

PL

tkanina aramidowa; PACVD; przyspieszone starzenie

• Wydawca: Sieć Badawcza Łukasiewicz - Łódzki Instytut Technologiczny
• Czasopismo: Fibres & Textiles in Eastern Europe
• Rocznik: 2016
• Tom: Vol. 24, no. 4 (118)
• Strony: 92--97
• Opis fizyczny: Bibliogr. 6 poz., rys., tab.

Twórcy

autor

Struszczyk M. H.

• Institute of Security Technology MORATEX, Łódź, Poland

autor

Puszkarz A. K.

• Department of Material and Commodity Sciencs and Textile Metrology, Faculty of Material Technologies and Textile Design, Lodz University of Technology, Łódź, Poland

autor

Miklas M.

• Institute of Security Technology MORATEX, Łódź, Poland

autor

Wilbik-Hałgas B.

• Institute of Security Technology MORATEX, Łódź, Poland

autor

Cichecka M.

• Institute of Security Technology MORATEX, Łódź, Poland

autor

Urbaniak–Domagała W.

• Department of Material and Commodity Sciencs and Textile Metrology, Faculty of Material Technologies and Textile Design, Lodz University of Technology, Łódź, Poland

autor

Krucińska I.

• Department of Material and Commodity Sciencs and Textile Metrology, Faculty of Material Technologies and Textile Design, Lodz University of Technology, Łódź, Poland

Bibliografia

• 1. Morent R, De Geyter N, Verschuren J, De Clerck K, Kiekens P and Leys C. Non-Thermal Plasma Treatment of Textiles. Surface & Coatings Technology 2008; 202, 14: 3427-3449.
• 2. Struszczyk MH, Puszkarz AK, Wilbik-Hałgas B, Cichecka M, Litwa P, Urbaniak-Domagała W and Krucinska I. The surface modification of ballistic textiles using plasma-assisted chemical vapor deposition (PACVD). Textile Research Journal (Impact Factor: 1.33). 2014; 11, 84(19). DOI: 10.1177/0040517514528559
• 3. Fejdyś M, Łandwijt M and Struszczyk MH. Effect of Accelerated Ageing Conditions on the Degradation Process of Dyneema® Polyethylene Composites. Fibres and Textiles in Eastern Europe 2011; 19, 1 (84): 60-65.
• 4. Struszczyk MH, Gutowska A, Palys B, et al. Accelerated Ageing of the Implantable, Ultra-Light, Knitted Medical Devices Modified by Low-Temperature Plasma Treatment - Part 1. Effects on the Physical Behaviour. Fibres and Textiles in Eastern Europe 2012; 20, 6B(96): 121-127.
• 5. Kucharska M, Struszczyk MH, Cichecka M, et al., Prototypes of Primary Wound Dressing of Fibrous and Quasi-Fibrous Structure in Terms of Safety of Their Usage. Fibres and Textiles in Eastern Europe 2012, 20, 6B(96), 142-148.
• 6. Struszczyk MH, Puszkarz AK, Miklas M, Wilbik-Hałgas B, Cichecka M, Urbaniak-Domagała W and Krucinska I. The Effect of the Accelerated Ageing on the Ballistic Textiles Modified by Plasma-Assisted Chemical Vapour Deposition (PACVD). Fibres and Textiles in Eastern Europe 2016; 24, 1(115): 83-88. DOI: 10.5604/12303666.1167429

Uwagi

Opracowanie ze środków MNiSW w ramach umowy 812/P-DUN/2016 na działalność upowszechniającą naukę.