Crease-resistant Finish of Linen/Viscose Blend Fabrics

• Autorzy: Kut D. , Güneşoğlu C. , Orhan M.

Warianty tytułu

PL

Wykończenie przeciwgniotliwe tkanin z mieszanki len/wiskoza

• Języki publikacji: EN

Abstrakty

EN

Linen/viscose blend fabrics are treated in different conditions with various concentrations of polycarboxylic acids (BTCA, CA, GA and MA) and N-methylol reagent (DMDHEU) with a relevant catalyst. The characterisation of such fibres is dependent on the degree of crosslinking, which is evaluated by the dry wrinkle recovery angle and tensile strength retention. In trials BTCA showed much better effects on the crease resistant finish of linen/viscose blend fabrics; when comparing the mixture of polycarboxylic acids, BTCA/GA treatment also gives moderate effects. High temperature curing is a handicap for linen/viscose blend fabric treatment when considering strength loss, whereas DMDHEU solutions give better results due to their lower acidity. In order to optimise the crease resistant finish of linen/viscose blend fabrics, it is acceptable to add a triethanolamine additive with the same ratio of the catalyst and cure at 160°C.

PL

Tkaniny wykańczane były za pomocą kwasów polikarboksylowych (BTCA, CA, GA i MA) o różnym stężeniu oraz N-hydroksymetylowego reagentu (DMDHEU) z dodatkiem odpowiedniego katalizatora. Charakterystyka obrabianych włókien zależy od stopnia usieciowania, ocenianego poprzez kąt odprężności i zmianę wytrzymałości na rozciąganie. Najlepsze wyniki uzyskano przy stosowaniu BTCA, a umiarkowane przy stosowaniu BTCA/GA. Optymalna temperatura obróbki wykańczającej wynosiła 160°C natomiast przy 180°C utrata wytrzymałości mechanicznej po obróbce był mniejsza. Korzystne wyniki uzyskuje się przy zastosowaniu katalizatora w postaci trietanoloaminy.

Słowa kluczowe

EN

crease resistance; finish; fabrics; linen; viscose

PL

odporność na zginanie; wykończenie; tkaniny; pościel; wiskoza

• Wydawca: Sieć Badawcza Łukasiewicz - Łódzki Instytut Technologiczny
• Czasopismo: Fibres & Textiles in Eastern Europe
• Rocznik: 2010
• Tom: Vol. 18, no. 6 (83)
• Strony: 91--93
• Opis fizyczny: Bibliogr. 19 poz., rys., tab.

Twórcy

autor

Kut D.

• Uludag University, Textile Engineering Department, Bursa, Turkey

autor

Güneşoğlu C.

• Gaziantep University, Textile Engineering Department, Gaziantep,Turkey

autor

Orhan M.

• Uludag University, Textile Engineering Department, Bursa, Turkey

Bibliografia

• 1. Wei W., Yang C.Q., Text.Chem.&Color., Vol.32, No.2, February 2000, pp.53-57.
• 2. Yang C.Q., Wei W. , McIlwaine D.B., Textile Res. J., Vol.70, No.3, March 2000, pp.230-236.
• 3. Laemmermann D., Melliand Textilber., No.3, 1992, pp. 274-279.
• 4. Welch C.M., Rew. Prog.Color, No.22, 1992, pp.32-41.
• 5. Welch C.M., Danna G.F., Textile Res. J., Vol.52, 1982, pp. 149-156.
• 6. Frick J.G., R.G. Jr. Harper, Textile Res. J., Vol.53, 1982, pp.141-148.
• 7. Welch C.M., Textile Res. J., Vol. 58, 1988, pp.480-486.
• 8. Xu W., Li Y., Textile Res. J. Vol.70, No. 11, November 2000, pp.957-961.
• 9. Schramm C., Rinderer B., Bobleter O., Textile Res. J., Vol.29, No.9, September 1997, pp.37-41.
• 10. Schramm C., Rinderer B., Text. Chem.&Color., Vol.32, No.9, September 2000, pp.37-40
• 12. Yang C.Q, Wang X., Kang I., Textile Res. J., Vol.67, No.11, November 1997, pp.334-342.
• 13. Chen J., Chen C., Textile Res. J., Vol.71, No.6, June 2001, pp.514-518.
• 14. Yang C.Q., Xu L., Li S., Jiang Y., Textile Res. J., Vol.68, No.5, May 1998, pp.457-464.
• 15. Yang C.Q., Wei W., Lickfeld G.C., Textile Res. J., Vol. 70, No.2, February 2000, pp.143-147.
• 16. Welch C.M., Peters J.G., Text. Chem&Color., Vol.29, No.3, March 1997, pp.22-27.
• 17. Yang C.Q., Wang X., Textile Res. J., Vol. 66, No.9, September 1996, pp.593-603.
• 18. Xu W., Shyr T., Textile Res. J., Vol.70, No.1, January 2000, pp.8-10.
• 19. Udomkichdecha W., et.al., Textile Res. J., Vol.73, No.5, May 2003, pp.401-406.
• 20. Welch C.M., Text.Chem.&Color., Vol.29, No.2, February 1997, pp.21-24.

Uwagi

W bibliografii brak pozycji 11.