Effect of Heat Treatment Conditions on the Morphology of α Phase and Mechanical Properties In Ti-10V-2Fe-3Al Titanium Alloy

• Autorzy: Bogucki R. , Mosór K. , Nykiel M.

Identyfikatory

DOI

10.2478/amm-2014-0217

Warianty tytułu

PL

Wpływ warunków obróbki cieplnej na morfologię fazy α i własności mechaniczne w stopie tytanu Ti-10V-2Fe-3Al

• Języki publikacji: EN

Abstrakty

EN

The influence of heat treatment on the microstructure and mechanical properties was studied in the Ti-10V-2Fe-3Al titanium alloy for two heat treatment schemes (α + β) and β + (β + α), which resulted in different morphologies of the α phase. Scheme I resulted in the α-phase of globular morphology, whose volume fraction did not change much during annealing. Scheme II led to obtaining a needle-like α-phase, whose amount increased together with heating time. The phenomenon of stress-induced martensitic transformation was observed in the material with needle-like morphology annealed for 15 and 30 min. Longer times of annealing effected in the decay of that transformation, provided the volume fraction of α-phase exceeded 50%.

PL

W pracy przedstawiono wyniki badan wpływu obróbki cieplnej na mikrostrukture i własciwosci mechaniczne stopu tytanu Ti-10V-2Fe-3Al, które analizowano w dwóch schematach obróbki cieplnej (α + β) oraz β + (β + α). Uzyskane mikrostruktury charakteryzowały sie rózna morfologia fazy α. W schemacie I obserwowano globularna faze α, której udział objetosciowy nie ulegał znacznym zmianom w funkcji czasu wygrzewania. W schemacie II faza α miała kształt iglasty i jej udział objetosciowy wzrastał z czasem wygrzewania. W próbkach o iglastej morfologii fazy α dla czasów wygrzewania 15 min. i 30 min. zaobserwowano wystepowanie zjawiska przemiany martenzytycznej indukowanej naprezeniem. Zastosowanie dłuzszych czasów wygrzewania ujawniło zanik dodatkowej.

Słowa kluczowe

EN

phase transformations; microstructure; mechanical properties; β-phase; α-phase

PL

przemiany fazowe; mikrostruktura; właściwości mechaniczne; faza α; faza β

• Wydawca: Institute of Metallurgy and Materials Science of Polish Academy of Sciences ; Committee of Materials Engineering and Metallurgy of Polish Academy of Sciences
• Czasopismo: Archives of Metallurgy and Materials
• Rocznik: 2014
• Tom: Vol. 59, iss. 4
• Strony: 1269--1273
• Opis fizyczny: Bibliogr. 15 poz., rys., tab.

Twórcy

autor

Bogucki R.

• Institute of Materials Science, Cracow University of Technology, Al. Jana Pawła II 37, 31-864 Kraków, Poland

autor

Mosór K.

• Institute of Materials Science, Cracow University of Technology, Al. Jana Pawła II 37, 31-864 Kraków, Poland

autor

Nykiel M.

• Institute of Materials Science, Cracow University of Technology, Al. Jana Pawła II 37, 31-864 Kraków, Poland

Bibliografia

• [1] G. T. Terlinde, T. W. Duerig, J. C. Williams, Metall. Mater. Trans. A 14 , 2101-2115 (1983).
• [2] T. W. Duerig, J. Albrecht, D. Richer, P. Fischer, Acta Metall. 30, 2161-2172 (1982).
• [3] R. Dąbrowski, The kinetics of phase transformations during continuous cooling of Ti6Al4V alloy from the diphase α+ β range , Arch. Metal. Mater. 56, 217-221 (2011).
• [4] R. Dąbrowski, The kinetics of phase transformations during continuous cooling of Ti6Al4V alloy from the single-phase β range , Arch. Metal. Mater. 56, 703-707 (2011
• [5] R. R Boyer, R. D. Brigs, Journal of Materials Engineering and Performance 14(6), 681-685 (2005).
• [6] C. LI, X. Wu, J. H. Chen, S. van der Zwaag, Materials Science and Engineering A 528 , 5854-5860 (2011).
• [7] M. Jackson, R. Dashwood, L. Christodoulou, H. Flower, Metallurgical and Materials Transactions A, 36A, 1317-1327 (2015).,
• [8] L. Zhou, G. Liu, X. L. Ma, K. Lu, Acta Mater. 56, 78-87 (2008).
• [9] P. J. Apps, J. R. Bowen, P. B. Prangnell, Acta Mater. 51, 2811-2822 (2003).
• [10] I. Gutierrez-Urrutia, M. A. Munoz-Morris, D. G. Morris, Mater. Sci. Eng. A 394 399-410 (2005).
• [11] A. Paradkar, V. Kumar, S. V. Kamat, A. K. Gogia, B. P. Kashyap, Materials Science and Engineering A 486, 273-282 (2008).,
• [12] A. Bhattacharjee, V. K. Varma, S. V. Kamat, A. K. Gogia, S. Bhargava, Metallurgical and Materials Transaction 37A, 1423-1433 (2006).
• [13] W. Chen, Q. Sun, L. Xiao, J. Sun, Materials Science and Engineering A 527, 7225-7234 (2010).
• [14] A. Bhattacharjee, S. Bhargava, V. K. Varma, S. V. Kamat, A.K. Gogia, Scripta Materialia 53 195-200 (2005).
• [15] A. Paradkar, S. V. Kamat, A. K. Gogia, B. P. Kashyap, Materials Science and Engineering A 491 390-396 (2008).