New possibilities of shaping the surface properties in austempered ductile iron castings

• Autorzy: Myszka D.
• Języki publikacji: EN

Abstrakty

EN

The paper presents recent developments concerning the formation of surface layer in austempered ductile iron castings. It was found that the traditional methods used to change the properties of the surface layer, i.e. the effect of protective atmosphere during austenitising or shot peening, are not fully satisfactory to meet the demands of commercial applications. Therefore, new ways to shape the surface layer and the surface properties of austempered ductile iron castings are searched for, to mention only detonation spraying, carbonitriding, CVD methods, etc.

Słowa kluczowe

EN

austempered ductile iron; surface treatments; surface properties; casting; heat treatment

PL

żeliwo sferoidalne austenityczne; obróbka powierzchni; właściwości powierzchniowe; odlew; obróbka cieplna

• Wydawca: Komisja Odlewnictwa Polskiej Akademii Nauk Oddział w Katowicach
• Czasopismo: Archives of Foundry Engineering
• Rocznik: 2013
• Tom: Vol. 13, iss. 1
• Strony: 103--106
• Opis fizyczny: Bibliogr. 14 poz., rys., tab., wykr.

Twórcy

autor

Myszka D.

• Institute of Manufacturing Technologies, Warsaw University of Technology, Narbutta 85, 02-524 Warsaw, Poland

Bibliografia

• [1] D. Myszka, M. Kaczorowski, J. Tybulczuk: Żeliwo sferoidalne ausferrytyczne – bezpośrednio hartowane izotermicznie. Wydawnictwo Instytutu Odlewnictwa, Kraków 2003.
• [2] A. Kowalski, J Tybulczuk, Properties of ductile iron alloyed 1,5%Ni and 0,8%Cu as-cast and austempered, Prace Instytutu Odlewnictwa, Int.Sc. Conf. ADI – Foundry’s offer for designers and users of casting, Kraków 2000, II, 45-56.
• [3] www.ductile.org.
• [4] D. Myszka, I. Pokorska, G. Mońka, Umocnienie warstwy wierzchniej odlewów z żeliwa sferoidalnego ausferrytycznego poddanych kulowaniu, Inżynieria Materiałowa, 4/2011, 616-619.
• [5] Cheng-Hsun Hsu, Jung-Kai Lu, Rung-Jie Tsai, Effects of low-temperature coating process on mechanical behaviours of ADI, Materials Science and Engineering A, 2005, A 398, 282-290.
• [6] Cheng-Hsun Hsu, Jung-Kai Lu, Rung-Jie Tsai, Characteristics of duplex surface coatings on austempered ductile iron substrates, Surface and Coatings Technology, 2006, 200, 5725-5732.
• [7] Cheng-Hsun Hsu, Ming-Li Chen, Kuei-Laing Lai, Corrosion resistance of TiN/TiAlN-coated ADI by cathodic arc deposition, Materials Science and Engineering A, 2006, A 421, 182-190.
• [8] D. Myszka, K. Stoberska, T. Babul, Detonation sprayed coatings Al2O3–TiO2 and Wc/Co on ADI investment castings, Archives of metallurgy and materials, 2009, vol.54, 217-223.
• [9] D. Myszka, M. Kłębczyk, L. Kwiatkowski, A. Zych, The surface layer of austempered ductile iron investment casting properties, Archives of Foundry Engineering, vol.9, no 1, 2009, 157-162.
• [10] D. Myszka, Thermo-chemical treatment of austempered ductile iron castings”, Materials Engineering (Medzagotyra) 2006, vol.12, no1, 11-15.
• [11] D. Myszka, T. Babul, Wytwarzanie żeliwa sferoidalnego ausferrytycznego w piecach próżniowych z chłodzeniem gazowym, Archiwum Technologii Maszyn i Automatyzacji, 2010, vol.28.
• [12] A. Kowalski, Morfologia ausferrytu i właściwości żeliwa ADI z dodatkami Mn, Cu i Mo po niepełnym austenityzowaniu i dwustopniowym hartowaniu izotermicznym, projekt badawczy NCN, no N N507 273336.
• [13] D. Myszka, T. Borowski, Wymrażania żeliwa sferoidalnego ausferrytycznego, Inżynieria Materiałowa, 2006, no3, 221-224.
• [14] A. Wieczorek, D. Myszka, Możliwości zastosowania żeliwa sferoidalnego ausferrytycznego na elementy maszyn górniczych, Międzynarodowa Konferencja TEMAG, Wisła, 2011.