Effect of vacuum conditions on stability and crystallization of cobalt based amorphous alloy

• Autorzy: Yazici Ziya Ozgur

Identyfikatory

DOI

10.2478/msp-2020-0003

• Języki publikacji: EN

Abstrakty

EN

The aim of this work was to investigate the effects of moderate vacuum conditions (10 Pa, 1 × 10³ Pa and 2 × 10⁴ Pa) on glass forming ability, thermal stability and aging behavior of Co₄₂Cu₁Fe₂₀Ta_5:5B_26:5Si₅ amorphous samples in terms of size and distribution of crystalline precipitates. The thinnest parts (300 μm) of the wedge-shaped samples were amorphous for all vacuum conditions, and they had similar compositional, structural and thermal characteristics. However, they represented different microstructural features after heat treatments at 950 K and 1100 K. The same phases precipitated in all samples but the amount and the size of the precipitates increased as the pressure was raised to the normal atmospheric value. The differences in the glass forming ability and the microstructure due to aging are considered to originate from lower thermal characteristics, such as relaxation and reduced glass temperature as well as γ parameter, resulting from the poor vacuum pressure used in the production process. The differences in the microstructures and hardness values caused by heat treatments have been observed.

Słowa kluczowe

EN

metallic glass; glass forming ability; crystallization behavior; thermal stability; casting atmosphere

• Wydawca: De Gruyter
• Czasopismo: Materials Science Poland
• Rocznik: 2020
• Tom: Vol. 38, No. 1
• Strony: 181--188
• Opis fizyczny: Bibliogr. 19 poz., tab., rys.

Twórcy

autor

Yazici Ziya Ozgur

• Afyon Kocatepe University, Department of Materials Science and Engineering, Afyonkarahisar, 03200, Turkey

Bibliografia

• [1] WANG W.H., DONG C., SHEK H., Mater. Sci. Eng. Rep., 44 (2004), 45.
• [2] AXINTE E., Mater. Des., 35 (2012), 518.
• [3] WANG W.-M., ZHANG J.T., GEBERT A., ROTH S., SCHULTZ L., J. Non. Cryst. Solids, 357 (2011), 1657.
• [4] SETYAWAN A.D., KATO H., SAIDA J., INOUE A., J. Appl. Phys., 103 (2008), 044907.
• [5] LEE K.A., KIM Y.C., KIM J.H., LEE C.S., NAMKUNG J., KIM M.C., Mater. Sci. Eng. A, 449 – 451 (2007), 181.
• [6] RAMASAMY P., SZABO A., BORZEL S., ECKERT J., STOICA M., BARDOS A., Sci. Rep., 6 (2016), 35258.
• [7] CHANG C., ZHANG J., SHEN B., WANG W., INOUE A., J. Mater. Res., 29 (2014), 1217.
• [8] ZHANG J., LI Y., WAN F., ZHENG J., SONG J., TIAN M., CHANG C., SHEN B., J. Alloy. Compd., 702 (2017), 1.
• [9] YAZICI Z.O., HITIT A., YALCIN Y., OZGUL M., Met. Mater. Int., 22 (2016), 50.
• [10] INOUE A., SHINOHARA Y., YOKOYAMA Y., MASUMOTO T., Mater. Trans. JIM, 36 (1995), 1276.
• [11] SURYANARAYANA C., INOUE A., Glass-Forming Ability of Alloys, in: SURYANARAYANA C., INOUE A. (Eds.), Bulk Metallic Glasses, CRC Press, Boca Raton, FL, 2011, p. 49.
• [12] HITIT A., GECGIN M., ÖZTÜRK P., J. Mater. Sci. Technol., 31 (2015), 148.
• [13] SLIPENYUK A., ECKERT J., Scr. Mater., 50 (2004), 39.
• [14] ZHU J., MUKAI K., ISIJ Int., 38 (1998), 1039.
• [15] MILLS K.C., SU Y.C., Int. Mater. Rev., 51 (2006), 329.
• [16] SEN P., SRINIVASAN A., HEDGE M.S., RAO C.N.R., J. Mater. Sci., 18 (1983), 173.
• [17] SATO S., HONJO H., IKEDA S., OHNO H., ENDOH T., NIWA M., Appl. Phys. Lett., 106 (2015), 142407.
• [18] BYEON S.C., KIM C.K., HONG K.S., O’HANDLEY R.C., Mater. Sci. Eng. B, 60 (1999), 58.
• [19] SETYAWAN A.D., KATO H., SAIDA J., INOUE A., Mater. Trans., 48 (2007), 1266.

Uwagi

Opracowanie rekordu ze środków MNiSW, umowa Nr 461252 w ramach programu "Społeczna odpowiedzialność nauki" - moduł: Popularyzacja nauki i promocja sportu (2020).