Effect of chenille yarns produced with selected comfort fibres on the abrasion and bending properties of knitted fabrics

• Autorzy: Kavuşturan Y. , Çeven E. K. , Özdemir Ö.

Warianty tytułu

PL

Wpływ przędz szenilowych na odporność na ścieranie i zachowanie dzianin przy zginaniu

• Języki publikacji: EN

Abstrakty

EN

In this study, the effects of pile and core yarn material types on the abrasion and bending behavior of chenille knitted fabrics were studied. For this purpose different chenille yarns were produced from seven types of pile yarn material and two types of core yarn material at the same yarn counts. The different pile yarn fibre types used for the production of chenille yarns were comfort fibres like tencel, bamboo, modal, soybean, 50/50% soybean-tencel and conventional fibres like viscose and cotton; the different core yarn types were polyester and viscose. The abrasion resistance of knitted fabrics made from these yarns was measured with a Martindale Abrasion tester. According to the results of statistical analyses performed using the experimental values, physical properties like mass and thickness loss due to abrasion were affected by the pile and core yarn types. Course way, wale way and fabric bending rigidity properties were not affected by the core yarn fibre types. The course way bending rigidity property was affected by the pile yarn fibre types, while the wale way and fabric bending rigidity properties were affected by the pile yarn fibre types for undyed yarns.

PL

Badano wpływ przędz rdzeniowych i okrywowych na odporność na ścieranie i zachowanie przy zginaniu dzianin szenilowych. W tym celu wyprodukowano szereg dzianin szenilowych z siedmiu rodzajów przędz okrywowych oraz dwóch rodzajów przędz rdzeniowych o takich samych masach liniowych. Przędze okrywowe wykonane były z tak zwanych włókien komfortowych jak włókna celulozowe tencel i modalne, bambusowe, sojowe, mieszankowe 50/50% sojowe/tencel oraz konwencjonalnych takich jak wiskozowych i bawełnianych. Przędze rdzeniowe wykonano z włókien poliestrowych i wiskozowych. Odporność na ścieranie z dzianin wykonanych z tych przędz testowano za pomocą przyrządu typu Martindale . Na podstawie analizy statystycznej uzyskanych wyników eksperymentalnych stwierdzono, że fizyczne właściwości jak utrata masy i grubości dzianiny zależą od typu przędz okrywowych i rdzeniowych zastosowanych do produkcji dzianiny. Konfiguracja rządków i kolumienek oraz sztywność na zginanie dzianin nie zależały od rodzaju zastosowanych przędz rdzeniowych. Sztywność zginania w kierunku rządków była uzależniona od rodzaju zastosowanych przędz okrywowych podczas gdy sztywność kierunku kolumienek zależała od typu przędz okrywowych dla dzianin nie barwionych.

Słowa kluczowe

EN

chenille yarn; comfort fibres; bamboo; tencel; abrasion resistance; bending rigidity

PL

przędza szenilowa; włókna bambusowe; włókno Tencel; odporność na ścieranie; sztywność zginania

• Wydawca: Sieć Badawcza Łukasiewicz - Łódzki Instytut Technologiczny
• Czasopismo: Fibres & Textiles in Eastern Europe
• Rocznik: 2010
• Tom: Vol. 18, no. 1 (78)
• Strony: 48--53
• Opis fizyczny: Bibliogr. 21 poz., fig., tab.

Twórcy

autor

Kavuşturan Y.

• Uludag University, Faculty of Engineering and Architecture, Textile Engineering Department, Gorukle, 16059, Bursa, Turkey

autor

Çeven E. K.

• Uludag University, Faculty of Engineering and Architecture, Textile Engineering Department, Gorukle, 16059, Bursa, Turkey

autor

Özdemir Ö.

• Uludag University, Faculty of Engineering and Architecture, Textile Engineering Department, Gorukle, 16059, Bursa, Turkey

Bibliografia

• 1. Gong R.H., Wright R.M.; “Fancy Yarns, Their Manufacture and Application”, Woodhead Publishing Limited, Cambridge, U.K, 2002, 150 p.
• 2. Çeven E.K., Özdemir Ö.; A Study of the Basic Parameters Describing the Structure of Chenille Yarns, Fibres & Textiles in Eastern Europe, 2006, 14(2), pp. 24-28.
• 3. Tung P., Whitehead D.; 1997. Abrasion resistant chenille yarn and fabric and method for its manufacture, USPTO, www.uspto.gov.
• 4. Practical guide to handling complaints on textile products (revised) (complaints on damage and distortion p. 79, TES edition, by Japan Textile Advisers’ Association.
• 5. Kalaoğlu F., Demir E.; Chenille Yarn Properties and Performance of Chenille Upholstery Fabrics, Textile Asia, 2001, (3), pp. 37-40.
• 6. Özdemir Ö., Kalaoğlu F.; The Effect of Material and Machine Parameters on Chenille Yarn Properties, in “Proc. Tecnitex Autex Conference” 2001, pp. 184-189.
• 7. Nergis U.B., Candan C.; Properties of Plain Knitted Fabrics from Chenille Yarns, Textile Res. Journal, 2003, 73(12), pp. 1052-1056.
• 8. Özdemir Ö., Çeven E.K.; Influence of Chenille Yarn Manufacturing Parameters on Yarn and Upholstery Fabric Abrasion Resistance, Textile Res. J, 2004, 74(6), pp. 515-520.
• 9. Çeven E.K., Özdemir Ö.; Evaluation of Chenille Fabric Abrasion Performance with Several Abrasion Test Methods, Tekstil, Journal of Textile and Clothing Technology, 2005, 54(11), pp. 535-540.
• 10. Özdemir Ö., Çeven E.K.; Effect of Chenille Yarn Parameters on Yarn Shrinkage Behavior, Textile Res. Journal, 2005, 75(3), pp. 219-222.
• 11. Çeven E.K., Özdemir Ö.; Evaluation of Chenille Yarn Abrasion Behavior with Abrasion Tests and Image Analysis, Textile Res. Journal, 2006, 76(4), pp. 315-321.
• 12. Taylor J.M., Bradbury M.J., Moorhouse S.; Dyeing Tencel A100 with Poly-Functional Reactive Dyes, AATCC Review, 2001, 1(10), pp. 21.
• 13. Chavan R.B., Patra A.K.; Development and processing of lyocell, Indian Journal of Fibre & Textile Research, 2004, 29(1), December, pp. 483-492.
• 14. http://www.lenzing.com/fibers/en/textiles/303.jsp .
• 15. http://www.tencel.com/fibers/en/textiles/303.jsp .
• 16. http://ohioline.osu.edu/hyg-fact/5000/ 5572.html (Lyocell - One Fiber, Many Faces Joyce Ann Smith, Ph.D. Extension Specialist, Clothing).
• 17. http://www.bharattextile.com/products/ prod_02.php.
• 18. Yi-you Li.; Soybean Protein Fibre - A Healthy & Comfortable Fibre for the 21st Century, Fibres & Textiles in Eastern Europe, 2004, 12(2), pp. 8-9.
• 19. http://www.soysilk.com/.
• 20. EN ISO 12947: 1998. Determination of the Abrasion Resistance of Fabrics by the Martindale Method. Part 3.
• 21. Saville B.P.; “Physical Testing of Texiles”, Woodhead Publishing Ltd, U.K., 1999, pp. 195.