The Influence of Load History on Durability of P92 Steel Used for the Construction of Energy Pipelines

• Autorzy: Cieśla M. , Junak G.

Identyfikatory

DOI

10.1515/amm-2015-0316

Warianty tytułu

PL

Wpływ historii obciążenia na trwałość stali P92 stosowanej do budowy rurociągów energetycznych

• Języki publikacji: EN

Abstrakty

EN

The research material used in the study was the martensitic creep-resistant steel P92 used for the manufacture of pipes being part of power generation units subject to heavy load. The research problem focused on two issues. The first one was to analyze how the plastic deformation cumulated in the material in low-cycle fatigue conditions affects the characteristics of the material in creep conditions in a temperature of 600ºC. The other one was concerned with analysis of a reverse situation, i.e. how the initial plastic deformation of the material in creep conditions changes the mechanical characteristics of the steel under low-cycle fatigue conditions in a temperature of 600ºC.

PL

W pracy materiałem badawczym była żarowytrzymała stal martenzytyczna P92 wykorzystywana do wytwarzania rur wchodzących w skład wysokoobciążonych bloków energetycznych. Problem badawczy koncentrował się na dwóch zagadnieniach. W pierwszym analizowano jak odkształcenie plastyczne kumulowane w materiale w warunkach procesu zmęczenia niskocyklowego wpływa na charakterystyki materiału w warunkach pełzania w temperaturze 600ºC. W drugim analizowano sytuację odwrotną, tzn. jak wstępna deformacja plastyczna materiału w warunkach pełzania zmienia charakterystyki mechaniczne stali w warunkach zmęczenia niskocyklowego w temperaturze 600ºC.

Słowa kluczowe

EN

P92 steel; load history; creep; low-cycle fatigue

PL

stal P92; wysokoobciążone bloki energetyczne; pełzanie; zmęczenie niskocyklowe

• Wydawca: Institute of Metallurgy and Materials Science of Polish Academy of Sciences ; Committee of Materials Engineering and Metallurgy of Polish Academy of Sciences
• Czasopismo: Archives of Metallurgy and Materials
• Rocznik: 2015
• Tom: Vol. 60, iss. 3A
• Strony: 1853--1857
• Opis fizyczny: Bibliogr. 9 poz., rys., tab., wykr.

Twórcy

autor

Cieśla M.

• Silesian University of Technology, Faculty of Materials Engineering And Metallurgy, Department of Metals Technology, 8 Krasińskiego Str., 40-019 Katowice, Poland

autor

Junak G.

• Silesian University of Technology, Faculty of Materials Engineering And Metallurgy, Department of Metals Technology, 8 Krasińskiego Str., 40-019 Katowice, Poland

Bibliografia

• [1] G. Junak, M. Cieśla, Low-cycle fatigue of P91 and P92 steels used in the power engineering industry, “International Conference “Achievements in Mechanical and Materials Engineering”, Archives of Materials Science and Engineering 48, 19-24 (2011).
• [2] A. Marek, J. Okrajni, Local stress-strain behavior of a high-temperature steam valve under transient mechanical and thermal loading. J. Mater. Eng. Perform. 23, 1, 31-38 (2014).
• [3] J. Zieliński, J. Dobrzański, T. Jóźwik, Assessment of loss in life time of the primary steam pipeline material after long-term service under creep conditions, Journal of Achievements in Materials and Manufacturing Engineering 54, (1), 67-74 (2012).
• [4] A. Hernas, J. Dobrzański, Durability and damage of boiler and steam turbine components, Publishing House of the Silesian University of Technology, (2003).
• [5] K. Mutwil, M. Cieśla, Study on Cracking Process of Power Boiler Element, Production Editor, IOP Conference Series: Materials Science and Engineering 35 012017, 1-11 (2012).
• [6] J. Okrajni, Zmęczenie cieplno-mechaniczne i trwałość instalacji energetycznych. Wydawnictwo Politechniki Śląskiej. Gliwice (2011).
• [7] H. Sehitoglu, Thermal and Thermo-mechanical Fatigue of Structural Alloys, Fatigue and Fracture, ASTM Handbook 19, 527-556 (2008).
• [8] A. Marek, J. Okrajni, “Local Stress-Strain Behavior of a High-Temperature Steam Valve Under Transient Mechanical and Thermal Loading”, Journal of Materials Engineering and Performance, ISSN 1059-9495 23, 1, 1-8 (2013).
• [9] Z. Kowalewski, Zjawisko pełzania metali – eksperyment I modelowanie, Polska Akademia Nauk, Instytut Podstawowych Problemów Techniki, Warszawa (2005).