Wpływ rodzaju tkaniny na jej odporność na ścieranie
Języki publikacji
Abstrakty
In this experimental study, the abrasion resistance properties of woven fabrics were investigated as a function of weave type. Seven woven fabrics with different weave derivatives were woven with 100% cotton and 20 Tex (Ne 30/1) combed ring spun yarn for this investigation. These fabrics were tested with a Martindale Abrasion Tester to determine the abrasion resistance property. The abrasion resistance of the fabrics was evaluated according to their mass loss ratio after 4 different cycles (5,000, 7,500, 10,000, 15,000) of the Martindale Abrasion testing device. According to data obtained from the test results of sample weave patterns, we observed that the weave pattern has a significant effect on the abrasion resistance property of woven fabrics (P < 0.01). Furthermore, it was also noted that the number of rubbing cycles has a significant effect on the abrasion resistance property of woven fabrics (P < 0.01). Tukey test results showed that weave types with a high number of floats and low number of interlacings decrease the abrasion resistance property (P < 0.05).
W pracy badano odporność na ścieranie tkanin, jako cechę zależną od rodzaju splotu. Analizowano siedem tkanin (100% bawełna, 20 tex) o różnym splocie. W celu określenia odporności na ścieranie tkaniny zbadano przy użyciu aparatu Martindale’a. Odporność na ścieranie tkanin oceniono na podstawie współczynnika ubytku masy po różnej ilości cykli tarcia (5.000, 7.500, 10.000, 15.000) na aparacie Martindale’a. Na podstawie uzyskanych wyników można zaobserwować, że typ splotu oraz ilość cykli tarcia mają znaczący wpływ na odporność na ścieranie tkaniny (P < 0,01). Wyniki testów pokazują, że typy splotów o długich odcinkach wątku nieprzeplatanych oraz małej liczbie przepleceń obniża odporność na ścieranie (P < 0,05).
Czasopismo
Rocznik
Strony
54--56
Opis fizyczny
Bibliogr. 7 poz., rys., tab.
Twórcy
autor
- Department of Textile Engineering, University of Gaziantep, 27310 Gaziantep, Turkey
autor
- Department of Textile Engineering, University of Gaziantep, 27310 Gaziantep, Turkey
Bibliografia
- 1. Collier, B. J., Epps, H. H., “Textile Testing and Analysis”, Prentice Hall, New Jersey, 1999.
- 2. Kalaoğlu, F., Önder, E., Özipek, B., “Influence Of Varying Structural Parameters On Abrasion Characteristics of 50/50 Wool/Polyester Blended Fabrics”, Textile Research Journal, November 2003, Vol. 73, No. 11, pp. 980-984.
- 3. ASTM D4966-98 Standard Test Method for Abrasion Resistance of Textile Fabrics (Martindale Abrasion Tester Method), Annual Book of ASTM Standards, vol. 7, Textiles, Philadelphia, 1985.
- 4. Saville B. P., “Physical Testing of Textiles”, Woodhead Publishing Limited, 2000.
- 5. Paek, S.L., “Pilling, Abrasion, and Tensile Properties of Fabrics from Open-End and Ring Spun Yarns”, Textile Research Journal, October 1989, Vol. 59, No. 10, pp. 577-583.
- 6. Özdemir, Ö., Çeven, E. K., “Influence of Chenille Yarn Manufacturing Parameters on Yarn and Upholstery Fabric Abrasion Resistance”, Textile Research Journal, June 2004, Vol. 74, No. 6, pp. 515-520.
- 7. Yang, C. Q., Zhou, W., Lickfield, G. C., Parachura, K., “Cellulase Treatment of Durable Press Finished Cotton Fabric: Effects on Fabric Strength, Abrasion Resistance and Handle”, Textile Research Journal, December 2003, Vol. 73, No. 12, pp. 1057-1062.
Typ dokumentu
Bibliografia
Identyfikator YADDA
bwmeta1.element.baztech-c5ca93de-7c8f-4993-a2e7-375b9110abca