The Wear Mechanisms Description Of Multilayer Coatings, Performed By Transmission Electron Microscopy – An Overview Of The Own Research Work

• Autorzy: Major Ł.

Identyfikatory

DOI

10.1515/amm-2015-0379

Warianty tytułu

PL

Opis mechanizmu zużycia wielowarstwowych powłok w oparciu o transmisyjną mikroskopię elektronową – przegląd własnych badań doświadczalnych

• Języki publikacji: EN

Abstrakty

EN

The aim of the presented paper was to describe the wear mechanisms operating at the small length scale in multilayer coatings subjected to a mechanical testing. A hybrid PLD system (Pulsed Laser Deposition connected with magnetron sputtering) was used for the multi-layer coating deposition. Coatings were subjected to indentation, ball-on disc wear and scratch adhesion tests. Microstructure of the as-deposited coating and after mechanical tests was studied using the Scanning (SEM) and the Transmission (TEM) Electron Microscopes. The research work revealed that application of innovative multilayer coatings may allow to predict their life time and to steer their properties.

PL

Celem pracy było określenie mechanizmów zużycia wielowarstwowych powłok tribologicznych, poddanych testom mechanicznym na zużycie. Powłoki wytwarzane przy zastosowaniu hybrydowego układu PLD (technika laserowej ablacji połączona z rozpylaniem magnetronowym) poddane zostały mechanicznym testom na zużycie (indentacja oraz test kula-tarcza), a także testowi przylegania powłoki do podłoża (test zarysowania). Charakterystykę mikrostruktury powłok przed i po testach mechanicznych przeprowadzono za pomocą skaningowej (SEM) oraz transmisyjnej (TEM) mikroskopii elektronowej. Badania wykazały, że poprzez stosowanie innowacyjnych powłok wielowarstwowych można przewidzieć czas ich eksploatacji oraz dają możliwość sterowania właściwościami.

Słowa kluczowe

EN

multilayer coatings; TEM characterization; wear mechanisms

PL

powłoki wielowarstwowe; TEM; mechanizm zużycia

• Wydawca: Institute of Metallurgy and Materials Science of Polish Academy of Sciences ; Committee of Materials Engineering and Metallurgy of Polish Academy of Sciences
• Czasopismo: Archives of Metallurgy and Materials
• Rocznik: 2015
• Tom: Vol. 60, iss. 3
• Strony: 2319--2326
• Opis fizyczny: Bibliogr. 14 poz., rys.

Twórcy

autor

Major Ł.

• Polish Academy of Sciences, Institute of Metallurgy and Materials Sciences, ul. Reymonta 25, 30-059 Krakow, Poland

Bibliografia

• [1] P. Wiecinski, J. Smolik, H. Garbacz, K. J. Kurzydlowski, Thin Solid Films 519, 4069 (2011)
• [2] J. Romero, J. Esteve, A. Lousto, Surf. Coat. Technol. 188-189, 338 (2004)
• [3] L. Major, W. Tirry, G. Van Tendeloo, Surf. & Coat.Technol. 202, 6075 (2008)
• [4] J. M. Lackner, L. Major, M. Kot, Bull. Pol. Ac.: Tech. 59, 343 (2011)
• [5] P. Goodhew, Nano Today, 2006,1,40-43 ISSN:1748 0132, Elsevier
• [6] J. M. Lackner, Surf. Coat. Technol. 200, 1439 (2005)
• [7] J. M. Lackner, L. Major, M. Kot, Bull. Pol. Ac.: Tech. 59, 343 (2011)
• [8] L. Major, M. Janusz, M. Kot, J. M. Lackner, B. Major, RSC Adv., 5, 9405 (2015)
• [9] J. M. Lackner, W. Waldhauser, L. Major, M. Kot, Coatings 4, 121 (2014)
• [10] Q. Wang, F. Zhou, X. Ding, Z. Zhou, C. Wang, W. Zhang, L.K.-Y. Li and S.-T. Lee, Tribol. Int. 67, 104 (2013)
• [11] M. Kot, L. Major, K. Chronowska-Przywara, J. M. Lackner, W. Waldhauser, W. Rakowski, Mater. and Design 56, 981 (2014)
• [12] L. Major, Arch. of Civil and Mech. Eng. 14, 615 (2014)
• [13] L. Major, J. M. Lackner, B. Major, RSC Adv. 4, 21108 (2014)
• [14] L. Major, J. M. Lackner, M. Kot, M. Janusz, B. Major, Bull. Pol. Ac. Tech. 62, 565 (2014)

Uwagi

PL

Opracowanie ze środków MNiSW w ramach umowy 812/P-DUN/2016 na działalność upowszechniającą naukę.