Blended Polypropylene/Polyethylene Terephthalate Fibres: Crystallisation Behaviour of Polypropylene and Mechanical Properties

• Autorzy: Ujhelyiová A. , Bolhová E. , Marcinčin A. , Tiňo R.

Warianty tytułu

PL

Włókna mieszankowe z polipropylenu i poli(tereftalanu etylenu): proces krystalizacji polipropylenu i właściwości mechaniczne

• Języki publikacji: EN

Abstrakty

EN

Polyethylene terephthalate (PET) and the compatibilisers ethylenedistearamide (EDSA) and ethylenevinylacetate (EVAc) are used for the modification of PP fibres that are aimed at improving the dyeability by dyeing fibres in a bath. This causes changes in the melting and crystallisation process that affect the creation of the morphological structure in blended PP/PET fibres as well as the content of the crystalline phase of the PP matrix. The thermal properties of modified PP fibres were evaluated by the DSC method. Some thermal characteristics (Avrami exponent n, crystallisation kinetic constant K and free energy of crystal creation σe) of the blended PP/PET fibres at crystallisation were determined as well as their physical-mechanical properties. The various compatibilisers have a different influence on the crystallisation of PP in the PP/PET fibre blend. EDSA behaves as a nucleating agent and increases the crystallisation of PP. The compatibiliser EVAc decreases the crystallisation of PP in the PP/PET fibre blend. For the crystallisation of PP, heterogeneous nucleation with a tridimensional spherulitic growth of crystallites is characterised. The aforementioned additives emphasise this heterogeneous nucleation of crystallites in the crystallisation of PP in the blended PP/PET fibres. The tensile strength and elongation of the blended PP/PET fibres were changed by the influence of PET and compatibilisers.

PL

Poli(tereftalan etylenu) (PET) i środki homogenizujące EDSA i EVAc zostały użyte do modyfikacji włókien PP w celu polepszenia ich wybarwialności. Modyfikacje te spowodowały zmiany w procesach topnienia i krystalizacji, co wywarło wpływ na tworzenie się struktury morfologicznej w mieszankowych włóknach PP/PET, jak również na zawartość fazy krystalicznej w matrycy PP. Właściwości termiczne modyfikowanych włókien PP zostały ocenione metodą DSC. Wyznaczono dla włókien PP/PET wykładnik Avrami’ego n, stałą kinetyczną krystalizacji K oraz energia swobodna tworzenia kryształów σe. Różne środki homogenizujące mają różny wpływ na krystalizację PP. EDSA zachowuje się jak zarodek krystalizacji i zwiększa krystalizację PP, podczas, gdy EVAc obniża krystalizację PP w włóknach PP/PET. Dla krystalizacji PP charakterystyczna jest nukleacja heterogeniczna z trójwymiarowo-sferolitycznym wzrostem krystalitów, którą uwydatniają zastosowane dodatki. Wytrzymałość na rozciąganie i wydłużenie włókien PP/PET zostały zmienione pod wpływem PET , EDSA i EVAc.

Słowa kluczowe

EN

polypropylene; polyethylene terephthalate; crystallisation; mechanical properties; blend fibres

PL

polipropylen; politereftalan etylenu; krystalizacja; właściwości mechaniczne; włókna mieszankowe

• Wydawca: Sieć Badawcza Łukasiewicz - Łódzki Instytut Technologiczny
• Czasopismo: Fibres & Textiles in Eastern Europe
• Rocznik: 2007
• Tom: Vol. 15, no. 4 (63)
• Strony: 26--29
• Opis fizyczny: Bibliogr. 23 poz., tab.

Twórcy

autor

Ujhelyiová A.

• Slovak University of Technology in Bratislava, Faculty of Chemical and Food Technology, Institute of Polymer Materials, Department of Fibres and Textile Chemistry, Radlinského 9, 812 37 Bratislava, Slovak Republic

autor

Bolhová E.

• Slovak University of Technology in Bratislava, Faculty of Chemical and Food Technology, Institute of Polymer Materials, Department of Fibres and Textile Chemistry, Radlinského 9, 812 37 Bratislava, Slovak Republic

autor

Marcinčin A.

• Slovak University of Technology in Bratislava, Faculty of Chemical and Food Technology, Institute of Polymer Materials, Department of Fibres and Textile Chemistry, Radlinského 9, 812 37 Bratislava, Slovak Republic

autor

Tiňo R.

• Slovak University of Technology in Bratislava, Faculty of Chemical and Food Technology, Institute of Polymer Materials, Department of Fibres and Textile Chemistry, Radlinského 9, 812 37 Bratislava, Slovak Republic

Bibliografia

• 1. Bassett D. C., Hodge A. M., Proc. R. Soc. Lond. A, 377, 1981, p. 25.
• 2. Voigt-Martin I. G., Mandelkern L., In: N. P. Cheremisinoff, Editor. Handbook of polymer science and technology, vol. 3. New York: Marcel Dekker, 1989. p. 1.
• 3. Kopp S., Wittmann J. C., Lotz B., Polymer, 35(5), 1994, p. 908.
• 4. Overbergh N., Berghmans H., Reynaers H., J. Polym. Sci. Polym. Phys. Ed., 14, 1976, p. 1177.
• 5. Fillon B., Wittmann J.C., Lotz B., Thierry A., J. Polym. Sci., Part B, Polym. Phys. Ed., 31, 1993, p. 1383.
• 6. Marcincin A., Ujhelyiova A., Marcincinova T., Macromol. Symp., 176, 2001, pp. 65-72.
• 7. Marcincin A., Brejka O., Murarova A., Hodul P., Brejkova A., Vlákna a textil (Fibres and Textiles), 6(3), 1999, pp.119-124.
• 8.Marcincin A.. Progr. Polym. Sci., 37(5), 2002, pp. 853-913.
• 9. Ujhelyiova A., Marcincin A., Zemanova E., Ondrejmiska K., Marcincinova T., Vlákna a textil (Fibres and Textiles), 3(4), 1996, pp. 134-140.
• 10. Seves A., Testa B., Markandali B., Bergamasco L., Munaretto G., Beltrame P. L., Dyes and Pigments, 35(4), 1997, pp. 67-373.
• 11. Seves A., DE Marco T., Siciliano A.,. Dyes and Pigment, 28(4), 1995, pp. 19-29.
• 12. Ebrahimi G.N., Hassan-Nejed M., Iranian J. Pol. Sci., 13, 2000, p. 1.
• 13. Marcincin A., Brejka O., Ujhelyiova A., Körmendyova E., Staruch R., Vlákna a textil (Fibres and Textiles), 10(1), 2003, pp. 3-8.
• 14. Arroyo M., Zitzumbo R., Avalos F., Polymer, 41(16), 2000, pp. 6351-6359.
• 15. Marcincin A., Ujhelyiova A., Marcincinova T., Vlákna a textil (Fibres and Textiles), 1(2), 1994, pp. 81-88.
• 16. Marcincin A., Ujhelyiova A., Marcincin K., Marcincinova T., Vlákna a textil (Fibres and Textiles), 3(3), 1996, pp. 92-99.
• 17. Mandelkern L., Crystallisation of polymers. New York: McGraw-Hill, 1964.
• 18. Avrami M. J., Chem. Phys., 4, 1941, p. 315.
• 19. Martuscelli E., Pracella M., Crispino L., Polymer, 24(6), 1983, p. 693.
• 20. Sharples A., Introduction to polymer crystallisation. London: Arnold, 1966.
• 21. Körmendy E., Marcinčin A., Hricová M., Kovačič V., Fibres and Textiles in Eastern Europe, 13, No. 1(49), 2005, pp. 20-23.
• 22. Slusarczyk Cz., Graczyk T., Fabia J., Gawlowski A., Wlochowicz A., Fibres and Textiles in Eastern Europe, 13, No. 5(53), 2005, pp. 122-125.