Effect of metakaolin developed from local natural material soorh on workability, compressive strength, ultrasonic pulse velocity and drying shrinkage of concrete

• Autorzy: Saand A. , Keerio M. A. , Bangwar D. K.
• Języki publikacji: EN

Abstrakty

EN

The utilization of pozzolanic materials like metakaolin (MK) in cement mortar and concrete is growing in construction industry all around the world to reduce the CO2 release into the atmosphere and reduce energy consumption. This study instigates the performance of concrete containing locally developed metakaolin in terms of workability, unit weight, compressive strength, ultrasonic pulse velocity and drying shrinkage of concrete. The Portland cement (PC) is replaced by inclusion of developed local metakaolin (calcined Soorh at 800°C for 2 hours duration) with dosages range; 5% to 25% with increment of 5% (by weight of cement). The investigation revealed that concrete made with 15% replacement of ordinary Portland cement (OPC) with locally developed metakaolin (MK) has significant influance on workability, compressive strength, ultrasonic pulse velocity measurements and drying shrinkage of concrete as compared to OPC concrete.

PL

Wykorzystanie materiałów pucolanowych takich jak metakaolin (MK) w zaprawie cementowej i w betonie jest coraz częstsze w przemyśle budowlanym na całym świecie w celu ograniczenia emisji dwutlenku węgla do atmosfery oraz redukcji zużycia energii. W artykule opisano właściwości betonu zawierającego lokalnie dostępny metakaolin w kontekście urabialności, ciężaru właściwego, wytrzymałości na ściskanie, szybkości rozchodzenia się fali ultradźwiękowej i skurczu od wysychania betonu. Cement portlandzki (PC) został zastąpiony mieszanką lokalnie dostępnego metakaolinu (Soorh odwodniony w temperaturze 800°C w czasie 2 godzin) ze zróżnicowanym dozowaniem; 5% do 25% ze stopniowaniem co 5% (w stosunku do ciężaru cementu). W badaniach udowodniono, że zastąpienie 15% tradycyjnego cementu Portlandzkiego (OPC) lokalnie dostępnym metakaolinem (MK) znacząco wpływa na urabialność mieszanki, wytrzymałość na ściskanie, szybkość rozchodzenia się fali ultradźwiękowej i na wielkość skurczu od wysychania, w odniesieniu do betonu wykonanego z cementu portlandzkiego (OPC).

Słowa kluczowe

EN

compressive strength; local metakaolin; mechanical properties; soorh; UPV

PL

wytrzymałość na ściskanie; metakaolin; właściwości mechaniczne; soorh; UPV

• Wydawca: Silesian University of Technology
• Czasopismo: Architecture Civil Engineering Environment
• Rocznik: 2017
• Tom: Vol. 10, no. 2
• Strony: 115--122
• Opis fizyczny: Bibliogr. 10 poz.

Twórcy

autor

Saand A.

• Department of Civil Engineering, Quaid-e-Awam University of Engineering, Science & Technology, Nawabshah, Pakistan

autor

Keerio M. A.

• Quaid-e-Awam University College of Engineering, Science & Technology, Larkana, Pakistan

autor

Bangwar D. K.

• Quaid-e-Awam University College of Engineering, Science & Technology, Larkana, Pakistan

Bibliografia

• [1] Sabir, B., S. Wild, and J. Bai(2001). Metakaolin and calcined clays as pozzolans for concrete: a review. Cement and Concrete Composites, 23(6), 441–454.
• [2] Portland cement association (PCA) report.; Global cement consumption on the rise. Published on 3 June 2015.
• [3] Rashad, A.M. and S.R. Zeedan (2011). The effect of activator concentration on the residual strength of alkali-activated fly ash pastes subjected to thermal load. Construction and Building Materials, 25(7), 3098–3107.
• [4] Scrivener, K.L. and R.J. Kirkpatrick (2008). Innovation in use and research on cementitious mate- rial. Cement and concrete research, 38(2), 128–136.
• [5] Park, S.-S. and H.-Y. Kang (2008). Characterization of fly ash-pastes synthesized at different activator conditions. Korean Journal of Chemical Engineering, 25(1), 78–83.
• [6] Samet, B., T. Mnif, and M. Chaabouni (2007). Use of a kaolinitic clay as a pozzolanic material for cements: formulation of blended cement. Cement and Concrete Composites, 29(10), 741–749.
• [7] Habert, G., et al. (2008). Effects of the secondary minerals of the natural pozzolans on their pozzolanic activity. Cement and Concrete Research, 38(7), 963–975.
• [8] Habert, G., et al. (2009). Clay content of argillites: Influence on cement based mortars. Applied Clay Science, 43(3), 322–330.
• [9] Janotka, I., et al. (2010). Metakaolin sand–blended- cement pastes: Rheology, hydration process and mechanical properties. Construction and Building Materials, 24(5), 791–802.
• [10] Morsy, M.S. and S.S. Shebl (2007). Effect of silica fume and metakaoline pozzolana on the performance of blended cement pastes against fire. Ceramics Silikaty, 51(1), 40.